Cross-linked polyethylene (PEX) pipes used in hot water supply are required for high mechanical strength and high creep resistance at high temperature. Especially PEX-a pipes which are made by peroxide cross-linking h...Cross-linked polyethylene (PEX) pipes used in hot water supply are required for high mechanical strength and high creep resistance at high temperature. Especially PEX-a pipes which are made by peroxide cross-linking have better performance, such as creep resistance and thermal shock resistance than the pipes made by the other cross-linking method. Because the PEX-a pipes indicate the higher cross-link degree as compared with the other PEX pipes. In this study, the PEX-a pipes which were mixed with several stabilizers were tested to evaluate the effects on cross-link degree and the oxygen induction time. And also they are evaluated with the chlorine aqueous solution by the performance of the long-term hydrostatic pressure test and the long-term hydro dynamic pressure test. As a result, it was found that the combination of antioxidants for PEX-a pipes plays an important role to prolong the oxygen induction time without inhibiting the cross-linking. From the results of the 1H pulsed NMR measurement over the melting point of polyethylene, it was found that each peroxide PEX pipe with different antioxidant combinations indicated the different proportion and crosslink density of cross-linked region, in addition, that these pipes had the effective structure of cross-linking for the hydrostatic and hydrodynamic pressure test with the chlorine aqueous solution. Therefore, it was considered to be useful results for studies of the stricture of cross-linking of polyethylene.展开更多
Large-scale and low-cost preparation of carbon-based potassium anode with long life and high capacity is one of the footstones for the development of potassium ion batteries(PIBs).Herein,a low-cost carbon-based materi...Large-scale and low-cost preparation of carbon-based potassium anode with long life and high capacity is one of the footstones for the development of potassium ion batteries(PIBs).Herein,a low-cost carbon-based material,cross-linked hollow graphitic carbon(HGC),is large scale synthesized to apply for PIBs anode.Its hollow structure can afford sufficient space to overcome the damage caused by the volume expansion of graphitic carbon(GC).While the cross-linked structure forms a compact interconnection network that allows electrons to rapid transfer between different GC frameworks.Electrochemical measurements demonstrated that the HGC anode exhibited low charge/discharge plateau(about 0.25 V and 0.1 V)and excellent specific capacity as high as 298 m A h g^(-1)at the current density of 50 m A g^(-1).And more important,after 200 cycles the capacity of HGC anode still shows 269 m A h g^(-1)(the decay rate of per cycle is only 0.048%).Meanwhile,the use of commercial traditional electrolyte(KPF_(6))and cheap raw materials that provide new hope for trying and realizing the large-scale production of PIBs based on carbon anode materials.展开更多
The development of high-sulfur-loading Li-S batteries is a key prerequisite for their commercial applications.This requires to surmount the huge polarization,severe polysulfide shuttling and drastic volume change caus...The development of high-sulfur-loading Li-S batteries is a key prerequisite for their commercial applications.This requires to surmount the huge polarization,severe polysulfide shuttling and drastic volume change caused by electrode thickening.High-strength polar binders are ideal for constructing robust and long-life high-loading sulfur cathodes but show very weak interfacial interaction with non-polar sulfur materials.To address this issue,this work devises a highly integrated sulfur@polydopamine/highstrength binder composite cathodes,targeting long-lasting and high-sulfur-loading Li-S batteries.The super-adhesion polydopamine(PD)can form a uniform nano-coating over the graphene/sulfur(G-S)surface and provide strong affinity to the cross-linked polyacrylamide(c-PAM)binder,thus tightly integrating sulfur with the binder network and greatly boosting the overall mechanical strength/conductivity of the electrode.Moreover,the PD coating and c-PAM binder rich in polar groups can form two effective blockades against the effusion of soluble polysulfides.As such,the 4.5 mg cm−2 sulfur-loaded G-S@PD-c-PAM cathode achieves a capacity of 480 mAh g−1 after 300 cycles at 1 C,while maintaining a capacity of 396 mAh g−1 after 50 cycles at 0.2 C when the sulfur loading rises to 9.1 mg cm−2.This work provides a system-wide concept for constructing high-loading sulfur cathodes through integrated structural design.展开更多
文摘Cross-linked polyethylene (PEX) pipes used in hot water supply are required for high mechanical strength and high creep resistance at high temperature. Especially PEX-a pipes which are made by peroxide cross-linking have better performance, such as creep resistance and thermal shock resistance than the pipes made by the other cross-linking method. Because the PEX-a pipes indicate the higher cross-link degree as compared with the other PEX pipes. In this study, the PEX-a pipes which were mixed with several stabilizers were tested to evaluate the effects on cross-link degree and the oxygen induction time. And also they are evaluated with the chlorine aqueous solution by the performance of the long-term hydrostatic pressure test and the long-term hydro dynamic pressure test. As a result, it was found that the combination of antioxidants for PEX-a pipes plays an important role to prolong the oxygen induction time without inhibiting the cross-linking. From the results of the 1H pulsed NMR measurement over the melting point of polyethylene, it was found that each peroxide PEX pipe with different antioxidant combinations indicated the different proportion and crosslink density of cross-linked region, in addition, that these pipes had the effective structure of cross-linking for the hydrostatic and hydrodynamic pressure test with the chlorine aqueous solution. Therefore, it was considered to be useful results for studies of the stricture of cross-linking of polyethylene.
基金financially supported by National Natural Science Foundation of China(Nos.51922038 and 51672078)Hunan Outstanding Youth Talents(No.2019JJ20005)
文摘Large-scale and low-cost preparation of carbon-based potassium anode with long life and high capacity is one of the footstones for the development of potassium ion batteries(PIBs).Herein,a low-cost carbon-based material,cross-linked hollow graphitic carbon(HGC),is large scale synthesized to apply for PIBs anode.Its hollow structure can afford sufficient space to overcome the damage caused by the volume expansion of graphitic carbon(GC).While the cross-linked structure forms a compact interconnection network that allows electrons to rapid transfer between different GC frameworks.Electrochemical measurements demonstrated that the HGC anode exhibited low charge/discharge plateau(about 0.25 V and 0.1 V)and excellent specific capacity as high as 298 m A h g^(-1)at the current density of 50 m A g^(-1).And more important,after 200 cycles the capacity of HGC anode still shows 269 m A h g^(-1)(the decay rate of per cycle is only 0.048%).Meanwhile,the use of commercial traditional electrolyte(KPF_(6))and cheap raw materials that provide new hope for trying and realizing the large-scale production of PIBs based on carbon anode materials.
基金supported by the National Natural Science Foundation of China(21875155,51675275,21703185 and 21473119)Q.B.Z.acknowledges the Leading Project Foundation of Science Department of Fujian Province(2018H0034)Shenzhen Science and Technology Planning Project(JCYJ20170818153427106).
文摘The development of high-sulfur-loading Li-S batteries is a key prerequisite for their commercial applications.This requires to surmount the huge polarization,severe polysulfide shuttling and drastic volume change caused by electrode thickening.High-strength polar binders are ideal for constructing robust and long-life high-loading sulfur cathodes but show very weak interfacial interaction with non-polar sulfur materials.To address this issue,this work devises a highly integrated sulfur@polydopamine/highstrength binder composite cathodes,targeting long-lasting and high-sulfur-loading Li-S batteries.The super-adhesion polydopamine(PD)can form a uniform nano-coating over the graphene/sulfur(G-S)surface and provide strong affinity to the cross-linked polyacrylamide(c-PAM)binder,thus tightly integrating sulfur with the binder network and greatly boosting the overall mechanical strength/conductivity of the electrode.Moreover,the PD coating and c-PAM binder rich in polar groups can form two effective blockades against the effusion of soluble polysulfides.As such,the 4.5 mg cm−2 sulfur-loaded G-S@PD-c-PAM cathode achieves a capacity of 480 mAh g−1 after 300 cycles at 1 C,while maintaining a capacity of 396 mAh g−1 after 50 cycles at 0.2 C when the sulfur loading rises to 9.1 mg cm−2.This work provides a system-wide concept for constructing high-loading sulfur cathodes through integrated structural design.