Abstract A friction stir processing-based method was used to repair cracks in the 2024 aluminum alloy plates. The temperature field and plastic material flow pattern were analyzed on the basis of experimental and fini...Abstract A friction stir processing-based method was used to repair cracks in the 2024 aluminum alloy plates. The temperature field and plastic material flow pattern were analyzed on the basis of experimental and finite element simulation results. Microstructure and tensile properties of the repaired specimens were studied. The results showed that the entire crack repairing was a solid-phase process and plastic materials tended to flow toward the shoulder center and then resulted in the repairing of cracks. Meanwhile, the coarse grain structures were refined in repaired zone （RZ）, while the grains in thermal-mechanically affected zone and heat-affected zone were elongated and driven to grow up. Meanwhile, large phases are crushed into small particles and dispersed inside the RZ. Finally, the strength of the repaired specimens can be restored dramatically and their ductility can be partially restored. After heat treatment, the tensile properties of the repaired specimens can be further enhanced.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51405309)the Natural Science Foundation of Liaoning Province(Grant No. 2015020183)
文摘Abstract A friction stir processing-based method was used to repair cracks in the 2024 aluminum alloy plates. The temperature field and plastic material flow pattern were analyzed on the basis of experimental and finite element simulation results. Microstructure and tensile properties of the repaired specimens were studied. The results showed that the entire crack repairing was a solid-phase process and plastic materials tended to flow toward the shoulder center and then resulted in the repairing of cracks. Meanwhile, the coarse grain structures were refined in repaired zone （RZ）, while the grains in thermal-mechanically affected zone and heat-affected zone were elongated and driven to grow up. Meanwhile, large phases are crushed into small particles and dispersed inside the RZ. Finally, the strength of the repaired specimens can be restored dramatically and their ductility can be partially restored. After heat treatment, the tensile properties of the repaired specimens can be further enhanced.