Comparative investigations were carried out of the effect of heat treatment regimes Jor steel GC-4(40CrMnSiMoVA)on its crack propagating rates,from corrosion fatigue, (da/dN)_(CF),or stress corrosion cracking,(da/dt)_...Comparative investigations were carried out of the effect of heat treatment regimes Jor steel GC-4(40CrMnSiMoVA)on its crack propagating rates,from corrosion fatigue, (da/dN)_(CF),or stress corrosion cracking,(da/dt)_(SCC),in media with various constituents and pH values.Both(da/dN)_(CF) and(da/dt)_(SCC) accelerate with the increase of yield stress of the steel,yet the former is far less than the later.In comparison with media,the (da/dt)_(SCC) in distilled water is slightly greater than that in 3.5% NaCl solution,and the (da/dN)_(CF) in distilled water is far less than that in 3.5% NaCl solution.With the pH value increasing in 3.5% NaCl solution,the(da/dN)_(CF) lowers down and the(da/dt)_(SCC) speeds up.An explanation was also proposed with concept of the cyclic hardening and softening at crack tip,as well as the crack closure and occluded cell effect.展开更多
Based on probabilistic fracture mechanics approach, a new concept of material initial fatigue quality （MIFQ） is developed. Then, the relation between S-N curve and crack propagation curve is studied. From the study,...Based on probabilistic fracture mechanics approach, a new concept of material initial fatigue quality （MIFQ） is developed. Then, the relation between S-N curve and crack propagation curve is studied. From the study, a new durability analysis method is presented. In this method, S-N curve is used to determine crack growth rate under constant amplitude loading and evaluate the effects of different factors on durability and then the structural durability is analyzed. The tests and analyses indicate that this method has lower dependence on testing, and higher accuracy, reliability and generality and is convenient for application.展开更多
文摘Comparative investigations were carried out of the effect of heat treatment regimes Jor steel GC-4(40CrMnSiMoVA)on its crack propagating rates,from corrosion fatigue, (da/dN)_(CF),or stress corrosion cracking,(da/dt)_(SCC),in media with various constituents and pH values.Both(da/dN)_(CF) and(da/dt)_(SCC) accelerate with the increase of yield stress of the steel,yet the former is far less than the later.In comparison with media,the (da/dt)_(SCC) in distilled water is slightly greater than that in 3.5% NaCl solution,and the (da/dN)_(CF) in distilled water is far less than that in 3.5% NaCl solution.With the pH value increasing in 3.5% NaCl solution,the(da/dN)_(CF) lowers down and the(da/dt)_(SCC) speeds up.An explanation was also proposed with concept of the cyclic hardening and softening at crack tip,as well as the crack closure and occluded cell effect.
基金National Natural Science Foundation of China (60472118) High-tech Research Project of Jiangsu Province (BG2004008)
文摘Based on probabilistic fracture mechanics approach, a new concept of material initial fatigue quality （MIFQ） is developed. Then, the relation between S-N curve and crack propagation curve is studied. From the study, a new durability analysis method is presented. In this method, S-N curve is used to determine crack growth rate under constant amplitude loading and evaluate the effects of different factors on durability and then the structural durability is analyzed. The tests and analyses indicate that this method has lower dependence on testing, and higher accuracy, reliability and generality and is convenient for application.