Using Fe3O4 nano-particles as seeds, a new type of Fe3O4/Au composite particles with core/shell structure and diameter of about 170 nm was prepared by reduction of Au3+ with hydroxylamine in an aqueous solution. Parti...Using Fe3O4 nano-particles as seeds, a new type of Fe3O4/Au composite particles with core/shell structure and diameter of about 170 nm was prepared by reduction of Au3+ with hydroxylamine in an aqueous solution. Particle size analyzer and transmission electron micro-scope were used to analyze the size distribution and microstructure of the particles in different conditions. The result showed that the magnetically responsive property and suspension stability of Fe3O4 seeds as well as reduction conditions of Au3+ to Au0 are the main factors which are crucial for obtaining a colloid of the Fe3O4/Au composite particles with uniform particle dispersion, excellent stability, homogeneity in particle sizes, and effective response to an external magnet in aqueous suspension solutions. UV-Vis analysis revealed that there is a characteristic peak of Fe3O4/Au fluid. For particles with d(0.5)=168 nm, the lmax is 625 nm.展开更多
n-Alkane isomerization is a critical reaction that can affect parameters in oil refining, such as the gasoline octane number and diesel oil solidifying point. In this study, a catalyst support, mordenite (MOR)/silicoa...n-Alkane isomerization is a critical reaction that can affect parameters in oil refining, such as the gasoline octane number and diesel oil solidifying point. In this study, a catalyst support, mordenite (MOR)/silicoaluminophosphate (SAPO)-11 composite zeolite with core/shell structure, was synthesized by hydrothermal method with MOR acting as the seed for crystallization. The crystal structure, elemental composition, surface area, pore volume, and acidity of the catalyst was thoroughly characterized. In addition, the catalytic performance of the as-obtained Pt/MOR/SAPO-11 in the hydroisomerization of n-dodecane was tested. The results indicated that the properties and catalytic performance of the composite molecular sieve were quite different from those of the pure zeolites and physical mixture of MOR and SAPO-11 (MOR+SAPO-11). Compared with the physical mixture, MOR and SAPO-11 were more tightly bound in MOR/SAPO-11 because of chemical bonding. Moreover, the acidity and pore structure were favorable to the catalytic hydroisomerization of n-dodecane. Pt/MOR/SAPO-11 exhibited higher isomerization activity than the Pt-loaded pristine MOR and MOR+SAPO-11. Thus, the core-shell composite molecular sieve has promising industrial applications as the catalyst support.展开更多
基金This work was supported by the National Natural Science Foundation of China(Grant No.20273035)the National High Technology Research and Development Program of China(863 Program)(Grant Nos.2002AA2Z2031 and 2001AA224032)the Science and Technology Program of Xi'an(Grant No.GG200148).
文摘Using Fe3O4 nano-particles as seeds, a new type of Fe3O4/Au composite particles with core/shell structure and diameter of about 170 nm was prepared by reduction of Au3+ with hydroxylamine in an aqueous solution. Particle size analyzer and transmission electron micro-scope were used to analyze the size distribution and microstructure of the particles in different conditions. The result showed that the magnetically responsive property and suspension stability of Fe3O4 seeds as well as reduction conditions of Au3+ to Au0 are the main factors which are crucial for obtaining a colloid of the Fe3O4/Au composite particles with uniform particle dispersion, excellent stability, homogeneity in particle sizes, and effective response to an external magnet in aqueous suspension solutions. UV-Vis analysis revealed that there is a characteristic peak of Fe3O4/Au fluid. For particles with d(0.5)=168 nm, the lmax is 625 nm.
基金the National Natural Science Fund of China (2016-Z0030)the Natural Science Foundation of Liaoning Province (L2017LQN008, L2016020)the Fushun Science & Technology Program (2011ZX05039-003)
文摘n-Alkane isomerization is a critical reaction that can affect parameters in oil refining, such as the gasoline octane number and diesel oil solidifying point. In this study, a catalyst support, mordenite (MOR)/silicoaluminophosphate (SAPO)-11 composite zeolite with core/shell structure, was synthesized by hydrothermal method with MOR acting as the seed for crystallization. The crystal structure, elemental composition, surface area, pore volume, and acidity of the catalyst was thoroughly characterized. In addition, the catalytic performance of the as-obtained Pt/MOR/SAPO-11 in the hydroisomerization of n-dodecane was tested. The results indicated that the properties and catalytic performance of the composite molecular sieve were quite different from those of the pure zeolites and physical mixture of MOR and SAPO-11 (MOR+SAPO-11). Compared with the physical mixture, MOR and SAPO-11 were more tightly bound in MOR/SAPO-11 because of chemical bonding. Moreover, the acidity and pore structure were favorable to the catalytic hydroisomerization of n-dodecane. Pt/MOR/SAPO-11 exhibited higher isomerization activity than the Pt-loaded pristine MOR and MOR+SAPO-11. Thus, the core-shell composite molecular sieve has promising industrial applications as the catalyst support.