Composite solid propellant is prepared using tri-modal Ammonium perchlorate(AP)containing coarse,fine and ultrafine fractions of AP with average particle size(APS)340,40 and 5 mm respectively,in various compositions a...Composite solid propellant is prepared using tri-modal Ammonium perchlorate(AP)containing coarse,fine and ultrafine fractions of AP with average particle size(APS)340,40 and 5 mm respectively,in various compositions and their rheological,mechanical and burn rate characteristics are evaluated.The optimum combination of AP coarse to fine to ultrafine weight fraction was obtained by testing of series of propellant samples by varying the AP fractions at fixed solid loading.The concentration of aluminium was maintained constant throughout the experiments for ballistics requirement.The propellant formulation prepared using AP with coarse to fine to ultrafine ratio of 67:24:9 has lowest viscosity for the propellant paste and highest tensile strength due to dense packing as supported by the literature.A minimum modulus value was also observed at 9 wt.%of ultrafine AP concentration indicates the maximum solids packing density at this ratio of AP fractions.The burn rate is evaluated at different pressures to obtain pressure exponent.Incorporation of ultrafine fraction of AP in propellant increased burn rate without adversely affecting the pressure exponent.Higher solid loading propellants are prepared by increased AP concentration from 67 to 71 wt.%using AP with coarse to fine to ultrafine ratio of67:24:9.Higher solid content up to 89 wt.%was achieved and hence increased solid motor performance.The unloading viscosity showed a trend with increased AP content and the propellant couldn't able to cast beyond 71 wt.%of AP.Mechanical properties were also studied and from the experiments noticed that%elongation decreased with increased AP content from 67 to 71 wt.%,whereas tensile strength and modulus increased.Burn rate increased with increased AP content and observed that pressure exponent also increased and it is high for the propellant containing with 71 wt.%of AP due to increased oxidiser to fuel ratio.Catalysed composite solid propellant is prepared by using burn rate modifiers Copper chromite and Iron oxide.Addition of Co展开更多
The ballistic properties of a low solid loading composite solid propellant family （Butalites） was studied experimentally by using propellant formulations based on hydroxy-terminated polybutadiene pre-polymer （HTPB...The ballistic properties of a low solid loading composite solid propellant family （Butalites） was studied experimentally by using propellant formulations based on hydroxy-terminated polybutadiene pre-polymer （HTPB） as fuel binder main backbone, mono and bi-modal system ammonium perchlorate oxidizer （AP）, copper chromite （CC） as burning rate accelerator and aluminum powder （A1） as metallic fuel. Higher pressures and AP contents as well as smaller AP particle size were found to increase burning rate. The same behavior verified with AI and CC addition. A significant increase of burning rate was recorded when CC added to the aluminized formulations compared with the non-aluminized of the same oxidizer solid loading and particle size.展开更多
文摘Composite solid propellant is prepared using tri-modal Ammonium perchlorate(AP)containing coarse,fine and ultrafine fractions of AP with average particle size(APS)340,40 and 5 mm respectively,in various compositions and their rheological,mechanical and burn rate characteristics are evaluated.The optimum combination of AP coarse to fine to ultrafine weight fraction was obtained by testing of series of propellant samples by varying the AP fractions at fixed solid loading.The concentration of aluminium was maintained constant throughout the experiments for ballistics requirement.The propellant formulation prepared using AP with coarse to fine to ultrafine ratio of 67:24:9 has lowest viscosity for the propellant paste and highest tensile strength due to dense packing as supported by the literature.A minimum modulus value was also observed at 9 wt.%of ultrafine AP concentration indicates the maximum solids packing density at this ratio of AP fractions.The burn rate is evaluated at different pressures to obtain pressure exponent.Incorporation of ultrafine fraction of AP in propellant increased burn rate without adversely affecting the pressure exponent.Higher solid loading propellants are prepared by increased AP concentration from 67 to 71 wt.%using AP with coarse to fine to ultrafine ratio of67:24:9.Higher solid content up to 89 wt.%was achieved and hence increased solid motor performance.The unloading viscosity showed a trend with increased AP content and the propellant couldn't able to cast beyond 71 wt.%of AP.Mechanical properties were also studied and from the experiments noticed that%elongation decreased with increased AP content from 67 to 71 wt.%,whereas tensile strength and modulus increased.Burn rate increased with increased AP content and observed that pressure exponent also increased and it is high for the propellant containing with 71 wt.%of AP due to increased oxidiser to fuel ratio.Catalysed composite solid propellant is prepared by using burn rate modifiers Copper chromite and Iron oxide.Addition of Co
文摘The ballistic properties of a low solid loading composite solid propellant family （Butalites） was studied experimentally by using propellant formulations based on hydroxy-terminated polybutadiene pre-polymer （HTPB） as fuel binder main backbone, mono and bi-modal system ammonium perchlorate oxidizer （AP）, copper chromite （CC） as burning rate accelerator and aluminum powder （A1） as metallic fuel. Higher pressures and AP contents as well as smaller AP particle size were found to increase burning rate. The same behavior verified with AI and CC addition. A significant increase of burning rate was recorded when CC added to the aluminized formulations compared with the non-aluminized of the same oxidizer solid loading and particle size.
