In this study,for the first time,direct copper production from copper sulfide was carried out via direct electrochemical reduction method using inexpensive and stable molten borax electrolyte.The effects of current de...In this study,for the first time,direct copper production from copper sulfide was carried out via direct electrochemical reduction method using inexpensive and stable molten borax electrolyte.The effects of current density(100–800 mA/cm^2)and electrolysis time(15–90 min)on both the cathodic current efficiency and copper yield were systematically investigated in consideration of possible electrochemical/chemical reactions at 1200℃.The copper production yield reached 98.09%after 90 min of electrolysis at a current density of 600 mA/cm^2.Direct metal production was shown to be possible with 6 kWh/kg energy consumption at a 600 mA/cm2 current density,at which the highest current efficiency(41%)was obtained.The suggested method can also be applied to metal/alloy production from single-and mixed-metal sulfides coming from primary production and precipitated sulfides,which are produced in the mining and metallurgical industries during treatment of process solutions or wastewaters.展开更多
Sulfation roasting was studied to extract copper from the copper sulfide concentrate. Sodium sulfite was added as sulfation agent to the copper sulfide concentrate during roasting in this study. Sulfur removal rate at...Sulfation roasting was studied to extract copper from the copper sulfide concentrate. Sodium sulfite was added as sulfation agent to the copper sulfide concentrate during roasting in this study. Sulfur removal rate at different roasting temperatures was investigated, and the effects of roasting temperature, roasting time, and the amount of sodium sulfite on copper extraction were studied. Copper extraction higher than 96% was achieved at optimum roasting conditions.展开更多
The extraction of copper from acidic medium using Liquid Emulsion Membrane LEM as contactors was studied. b diketone LIX 54 as an extractant ,sesqueoleate which is nonionic surfactant with HLB value 3.7 and 0.1 M H2SO...The extraction of copper from acidic medium using Liquid Emulsion Membrane LEM as contactors was studied. b diketone LIX 54 as an extractant ,sesqueoleate which is nonionic surfactant with HLB value 3.7 and 0.1 M H2SO4 as stripping solution were used. The influence of initial concentration of copper in the aqueous feed phase, pH of external and internal aqueous phase, stirring speed, and concentration of extractant on the extraction rate was examined. The results obtained showed that practically all the copper content was removed from the acidic feed solution. The recovery of copper attained 96–100% and concentration ratios of about 40-fold could be achieved.展开更多
Recently a research team at Ohio University,USA,conducted a unique full-scale feld load test to simulate the aeration pipe installations at a copper extraction mine operated in Chile.The overliner material taken from ...Recently a research team at Ohio University,USA,conducted a unique full-scale feld load test to simulate the aeration pipe installations at a copper extraction mine operated in Chile.The overliner material taken from the mine was used in recreating the in situ conditions.Electric heaters were utilized to raise the temperature inside each pipe to simulate the essential element of the copper extraction process.The maximum vertical deflection reached by the test pipes was close to 20%,when the simulated heap pile height was 80 m.The plastic pipes and the overliner material were also tested in the laboratory.Based on the results,the maximum heap pile fll depth was recommended for the aeration system.The results indicated that the vertical deflection was the primary performance index for the aeration pipes installed in heap piles at mines.Lastly,the pipe made of polypropylene resin was super.展开更多
文摘In this study,for the first time,direct copper production from copper sulfide was carried out via direct electrochemical reduction method using inexpensive and stable molten borax electrolyte.The effects of current density(100–800 mA/cm^2)and electrolysis time(15–90 min)on both the cathodic current efficiency and copper yield were systematically investigated in consideration of possible electrochemical/chemical reactions at 1200℃.The copper production yield reached 98.09%after 90 min of electrolysis at a current density of 600 mA/cm^2.Direct metal production was shown to be possible with 6 kWh/kg energy consumption at a 600 mA/cm2 current density,at which the highest current efficiency(41%)was obtained.The suggested method can also be applied to metal/alloy production from single-and mixed-metal sulfides coming from primary production and precipitated sulfides,which are produced in the mining and metallurgical industries during treatment of process solutions or wastewaters.
文摘Sulfation roasting was studied to extract copper from the copper sulfide concentrate. Sodium sulfite was added as sulfation agent to the copper sulfide concentrate during roasting in this study. Sulfur removal rate at different roasting temperatures was investigated, and the effects of roasting temperature, roasting time, and the amount of sodium sulfite on copper extraction were studied. Copper extraction higher than 96% was achieved at optimum roasting conditions.
文摘The extraction of copper from acidic medium using Liquid Emulsion Membrane LEM as contactors was studied. b diketone LIX 54 as an extractant ,sesqueoleate which is nonionic surfactant with HLB value 3.7 and 0.1 M H2SO4 as stripping solution were used. The influence of initial concentration of copper in the aqueous feed phase, pH of external and internal aqueous phase, stirring speed, and concentration of extractant on the extraction rate was examined. The results obtained showed that practically all the copper content was removed from the acidic feed solution. The recovery of copper attained 96–100% and concentration ratios of about 40-fold could be achieved.
文摘Recently a research team at Ohio University,USA,conducted a unique full-scale feld load test to simulate the aeration pipe installations at a copper extraction mine operated in Chile.The overliner material taken from the mine was used in recreating the in situ conditions.Electric heaters were utilized to raise the temperature inside each pipe to simulate the essential element of the copper extraction process.The maximum vertical deflection reached by the test pipes was close to 20%,when the simulated heap pile height was 80 m.The plastic pipes and the overliner material were also tested in the laboratory.Based on the results,the maximum heap pile fll depth was recommended for the aeration system.The results indicated that the vertical deflection was the primary performance index for the aeration pipes installed in heap piles at mines.Lastly,the pipe made of polypropylene resin was super.