A process using soda roasting-alkaline leaching-acid leaching to remove selenium, tellurium and copper sequentially from the copper anode slime with high content of Ni was tested. The mechanism of this process was out...A process using soda roasting-alkaline leaching-acid leaching to remove selenium, tellurium and copper sequentially from the copper anode slime with high content of Ni was tested. The mechanism of this process was outlined based on thermodynamic analysis and the change in the XRD patterns of different intermediate products. During soda roasting, copper which occurs as Cu4SeTe in the slime was oxidized to CuO and Cu3TeO6, while selenium and tellurium were oxidized to Ag2SeO4 and Cu3TeO6, respectively. Ag2SeO4 in the calcine is easily leached in the subsequent alkaline leaching, but CuTeO3 resulted from the decomposition of CCu3TeO6 remains inactive in this process through which selenium is leached out in preference to tellurium. The CuTeO3 and Cu O in the alkaline leaching residue can be leached in the following sulfuric acid leaching process. More than 97% of selenium was leached with little tellurium leached under the optimal condition. Then, more than 96% of copper and almost all the tellurium were leached out in the following acid leaching process.展开更多
The leaching kinetics of selenium from copper anode slimes was studied in a nitric acid?sulfuric acid mixture.The effects of main parameters on selenium leaching showed that the leaching rate of selenium was practical...The leaching kinetics of selenium from copper anode slimes was studied in a nitric acid?sulfuric acid mixture.The effects of main parameters on selenium leaching showed that the leaching rate of selenium was practically independent of stirring speed,while dependent on temperature and the concentrations of HNO3and H2SO4.The leaching of selenium includes two stages.The activation energy in the first stage is103.5kJ/mol,and the chemical reaction is the rate controlling step.It was almost independent of H2SO4concentration and dependent on HNO3concentration since the empirical reaction order with respect to HNO3concentration is0.5613.In the second stage,the activation energy is30.6kJ/mol,and the process is controlled by a mixture of diffusion and chemical reaction.The leaching of selenium was almost independent of HNO3concentration.展开更多
In this paper, recovery of silver from anode slime of Sarcheshmeh copper complex in lran and subsequent synthesis of silver nanoparticles from leaching solution is investigated. Sarcheshmeh anode slime is mainly consi...In this paper, recovery of silver from anode slime of Sarcheshmeh copper complex in lran and subsequent synthesis of silver nanoparticles from leaching solution is investigated. Sarcheshmeh anode slime is mainly consisted ofCu, Ag, Pb and Se. Amount of Ag in the considered anode slime was 5.4% （by weight）. The goal was to recover as much as possible Ag from anode slime at atmospheric pressure to synthesize Ag nanoparticles. Therefore, acid leaching was used for this purpose. The anode slime was leached with sulfuric and nitric acid from room to 90 ~C at different acid concentrations and the run which yielded the most recovery of Ag was selected for Ag nanoparticles synthesis. At this condition, Cu, Pb and Se are lea- ched as well as Ag. To separate Ag from leach solution HCI was added and silver was precipitated as AgCl which were then dissolved by ammonia solution. The Ag nanoparticles are synthesized from this solution by chemical reduction method by aid of sodium borohydride in the presence of PVP and PEG as stabilizers. The synthesized Ag nanoparticles showed a peak of 394 nm in UV-vis spectrum and TEM images showed a rather uniform Ag nanoparticles of 12 nm.展开更多
基金Project(2012BAE06B05)supported by the National Science and Technology Support Plan of China
文摘A process using soda roasting-alkaline leaching-acid leaching to remove selenium, tellurium and copper sequentially from the copper anode slime with high content of Ni was tested. The mechanism of this process was outlined based on thermodynamic analysis and the change in the XRD patterns of different intermediate products. During soda roasting, copper which occurs as Cu4SeTe in the slime was oxidized to CuO and Cu3TeO6, while selenium and tellurium were oxidized to Ag2SeO4 and Cu3TeO6, respectively. Ag2SeO4 in the calcine is easily leached in the subsequent alkaline leaching, but CuTeO3 resulted from the decomposition of CCu3TeO6 remains inactive in this process through which selenium is leached out in preference to tellurium. The CuTeO3 and Cu O in the alkaline leaching residue can be leached in the following sulfuric acid leaching process. More than 97% of selenium was leached with little tellurium leached under the optimal condition. Then, more than 96% of copper and almost all the tellurium were leached out in the following acid leaching process.
基金Projects(51374066,U1608254) supported by the National Natural Science Foundation of ChinaProject(2014BAC03B07) supported by the National Key Technology R&D Program of ChinaProjects(2012223002,2014020037) supported by Industrial Research Projects in Liaoning Province,China
文摘The leaching kinetics of selenium from copper anode slimes was studied in a nitric acid?sulfuric acid mixture.The effects of main parameters on selenium leaching showed that the leaching rate of selenium was practically independent of stirring speed,while dependent on temperature and the concentrations of HNO3and H2SO4.The leaching of selenium includes two stages.The activation energy in the first stage is103.5kJ/mol,and the chemical reaction is the rate controlling step.It was almost independent of H2SO4concentration and dependent on HNO3concentration since the empirical reaction order with respect to HNO3concentration is0.5613.In the second stage,the activation energy is30.6kJ/mol,and the process is controlled by a mixture of diffusion and chemical reaction.The leaching of selenium was almost independent of HNO3concentration.
基金the International Center for Science, High Technology & Environmental Sciences for financial support of this work (No. 1.213)
文摘In this paper, recovery of silver from anode slime of Sarcheshmeh copper complex in lran and subsequent synthesis of silver nanoparticles from leaching solution is investigated. Sarcheshmeh anode slime is mainly consisted ofCu, Ag, Pb and Se. Amount of Ag in the considered anode slime was 5.4% （by weight）. The goal was to recover as much as possible Ag from anode slime at atmospheric pressure to synthesize Ag nanoparticles. Therefore, acid leaching was used for this purpose. The anode slime was leached with sulfuric and nitric acid from room to 90 ~C at different acid concentrations and the run which yielded the most recovery of Ag was selected for Ag nanoparticles synthesis. At this condition, Cu, Pb and Se are lea- ched as well as Ag. To separate Ag from leach solution HCI was added and silver was precipitated as AgCl which were then dissolved by ammonia solution. The Ag nanoparticles are synthesized from this solution by chemical reduction method by aid of sodium borohydride in the presence of PVP and PEG as stabilizers. The synthesized Ag nanoparticles showed a peak of 394 nm in UV-vis spectrum and TEM images showed a rather uniform Ag nanoparticles of 12 nm.
