The electrochemical corrosion behaviors of the welded joints of 2205 duplex stainless steel with the laser continuous heat treatment were investigated. The secondary austenite formation is the outcome of thermodynamic...The electrochemical corrosion behaviors of the welded joints of 2205 duplex stainless steel with the laser continuous heat treatment were investigated. The secondary austenite formation is the outcome of thermodynamic equilibrium breach of the alloy during heat treatment and the result of the continuous heat treatment which has the most important effect on the weld material. The partitioning behaviors of chromium and molybdenum as well as the volume fraction of ferrite and austenite have a remarkable influence on the composition of the individual phase. Mechanical examination of the laser trated weld demonstrates that the tensile strength and yield strength increase with increasing the amount of the secondary austenite. It is shown that the ultimate tensile strength of the 6 kW laser-treated weld is higher about 20 MPa than no heat treatment weld and the ductility can be further improved without compromising strength. The results indicate that the welding alters the corrosion behavior because of different post heat treatment power and the broad active peak is not identified which is attributed to the dissolution of the secondary austenitic in the ferrite phase. It is indicated that pitting resistance equivalent （PRE） values of base metal and 6 kW weld are higher than that of other welds; base metal is 33.7, 6 kW weld 33.3, no treatment 32.4, 4 kW weld 32.8, 8 kW weld 32.5. The extent of corrosion resistance improvement after reheating treatment is mainly caused by the removal of nitrogen from ferritic regions, which occurred as a consequence of secondary austenite growth.展开更多
The effects of conform continuous extrusion and subsequent heat treatment on the mechanical and wear-resistance properties of high-alloying Al–13Si–7.5Cu–1Mg alloy were investigated.The microstructures of alloys be...The effects of conform continuous extrusion and subsequent heat treatment on the mechanical and wear-resistance properties of high-alloying Al–13Si–7.5Cu–1Mg alloy were investigated.The microstructures of alloys before and after conform processing and aging were compared by transmission electron microscopy and scanning electron microscopy,respectively.The results reveal that the primary phases were broken and refined by intense shear deformation during conform processing.After the conform-prepared Al–13Si–7.5Cu–1Mg alloy was subjected to solid-solution treatment at 494℃for 1.5 h and aging at 180℃for 4 h,its hardness improved from HBS 115.8 to HBS 152.5 and its ultimate tensile strength increased from 112.6 to 486.8 MPa.Its wear resistance was also enhanced.The factors leading to the enhanced strength,hardness,and wear resistance of the alloy were discussed in detail.展开更多
Microstructural characterization in fusion zone of the laser continuous heat treatment welded joint was in vestigated. The results showed that the martensite-like microstructure is the face centered cubic （FCC） crys...Microstructural characterization in fusion zone of the laser continuous heat treatment welded joint was in vestigated. The results showed that the martensite-like microstructure is the face centered cubic （FCC） crystal structure so that it can be identified as the secondary austenite. The dislocation is observed inside and outside the seconda ry austenite, whereas inclusion is not found in the vicinity of the secondary austenite. In the fusion zone, there is a kind of carbide precipitate which is identified as M23 C6 by the means of transmission electron microscope （TEM）. The carbide precipitate is a representative mode of transformation, which can be generated by the eutectoid reaction. Furthermore, the formation mechanisms of the secondary austenite and chromium carbide are analyzed.展开更多
基金Funded by the Major State Basic Research Development Program of China (973 Program) (No.2011CB706604)the R&D Project from Department of Railway(No. 2010G023)
文摘The electrochemical corrosion behaviors of the welded joints of 2205 duplex stainless steel with the laser continuous heat treatment were investigated. The secondary austenite formation is the outcome of thermodynamic equilibrium breach of the alloy during heat treatment and the result of the continuous heat treatment which has the most important effect on the weld material. The partitioning behaviors of chromium and molybdenum as well as the volume fraction of ferrite and austenite have a remarkable influence on the composition of the individual phase. Mechanical examination of the laser trated weld demonstrates that the tensile strength and yield strength increase with increasing the amount of the secondary austenite. It is shown that the ultimate tensile strength of the 6 kW laser-treated weld is higher about 20 MPa than no heat treatment weld and the ductility can be further improved without compromising strength. The results indicate that the welding alters the corrosion behavior because of different post heat treatment power and the broad active peak is not identified which is attributed to the dissolution of the secondary austenitic in the ferrite phase. It is indicated that pitting resistance equivalent （PRE） values of base metal and 6 kW weld are higher than that of other welds; base metal is 33.7, 6 kW weld 33.3, no treatment 32.4, 4 kW weld 32.8, 8 kW weld 32.5. The extent of corrosion resistance improvement after reheating treatment is mainly caused by the removal of nitrogen from ferritic regions, which occurred as a consequence of secondary austenite growth.
基金financially supported by the National Natural Science Foundation of China (No.51274245)
文摘The effects of conform continuous extrusion and subsequent heat treatment on the mechanical and wear-resistance properties of high-alloying Al–13Si–7.5Cu–1Mg alloy were investigated.The microstructures of alloys before and after conform processing and aging were compared by transmission electron microscopy and scanning electron microscopy,respectively.The results reveal that the primary phases were broken and refined by intense shear deformation during conform processing.After the conform-prepared Al–13Si–7.5Cu–1Mg alloy was subjected to solid-solution treatment at 494℃for 1.5 h and aging at 180℃for 4 h,its hardness improved from HBS 115.8 to HBS 152.5 and its ultimate tensile strength increased from 112.6 to 486.8 MPa.Its wear resistance was also enhanced.The factors leading to the enhanced strength,hardness,and wear resistance of the alloy were discussed in detail.
基金Item Sponsored by National Natural Science Foundation of China(51201154,51174251)Natural Science Foundation of Shanxi Province of China(2013011014-1)School Foundation of North University of China(2013051)
文摘Microstructural characterization in fusion zone of the laser continuous heat treatment welded joint was in vestigated. The results showed that the martensite-like microstructure is the face centered cubic （FCC） crystal structure so that it can be identified as the secondary austenite. The dislocation is observed inside and outside the seconda ry austenite, whereas inclusion is not found in the vicinity of the secondary austenite. In the fusion zone, there is a kind of carbide precipitate which is identified as M23 C6 by the means of transmission electron microscope （TEM）. The carbide precipitate is a representative mode of transformation, which can be generated by the eutectoid reaction. Furthermore, the formation mechanisms of the secondary austenite and chromium carbide are analyzed.