The flat clinching process is attracting a growing attention in the joining field of lightweight materials because it avoids the geometric protrusion that appears in the conventional clinching process. In this paper, ...The flat clinching process is attracting a growing attention in the joining field of lightweight materials because it avoids the geometric protrusion that appears in the conventional clinching process. In this paper, the effects of sheet thickness and material on the mechanical properties of the clinched joint were studied. Al1060 and Al2024 sheets with 2 mm thickness were employed to develop the clinched joint by using different material configurations, and Al1060 sheets with 2.5- and 1.5-mm thicknesses were used to produce the clinched joint by using different thickness configurations. The clinched joints using various sheet configurations were sectioned, and dimensional analysis was conducted. Cross-tensile and shearing tests were carried out to analyze the mechanical properties of the clinched joint, including tensile strength, shearing strength, and absorbed energy. In addition, the failure modes of the clinched joints were discussed. Results indicated that the clinched joint with a stiff top sheet had increased static strength regardless of the test type. The clinched joint with a thick top sheet demonstrated lower static strength than the joint with a thick bottom sheet in the cross-tensile test. However, this result was reversed in the shearing tests. The flat clinching process has a great potential in joining dissimilar and various thickness materials.展开更多
To extend the service life of the clinched joint,a reconditioning process conducted with an additional tubular rivet was proposed in this work.Different reconditioning forces were employed to produce dissimilar recond...To extend the service life of the clinched joint,a reconditioning process conducted with an additional tubular rivet was proposed in this work.Different reconditioning forces were employed to produce dissimilar reconditioned joints by experimental method.The experimental results indicated that the neck fracture was the common failure mode of both original clinched and reconditioned joints.Compared with the original clinched joint,the shearing strength of the reconditioned joint produced by a reconditioning force of 40 kN increased from 1810.5 to 1986.47 N,and the energy absorption increased from 2.34 to 3.46 J.The range of effective reconditioning force was from 35 to 40 kN and 40 kN was the best choice for reconditioning the AA5052 failed joints.The mechanical properties of the reconditioned joints are obviously better than those of the original clinched joints,which fully demonstrates that the reconditioning method proposed in this work has a broad prospect of industrial application.展开更多
基金This research work was supported by the National Natural Science Foundation of China(Grant No.51805416)the Young Elite Scientists Sponsorship Program by CAST,the Natural Science Foundation of Hunan Province,China(Grant No.2020JJ5716)+2 种基金the Natural Science Basic Research Plan in Shaanxi Province of China(Grant No.2019JQ-372)the Research Fund of State Key Laboratory of High Performance Complex Manufacturing(Grant No.ZZYJKT2019-01)the Huxiang High-Level Talent Gathering Project of Hunan Province,China(Grant No.2019RS1002).
文摘The flat clinching process is attracting a growing attention in the joining field of lightweight materials because it avoids the geometric protrusion that appears in the conventional clinching process. In this paper, the effects of sheet thickness and material on the mechanical properties of the clinched joint were studied. Al1060 and Al2024 sheets with 2 mm thickness were employed to develop the clinched joint by using different material configurations, and Al1060 sheets with 2.5- and 1.5-mm thicknesses were used to produce the clinched joint by using different thickness configurations. The clinched joints using various sheet configurations were sectioned, and dimensional analysis was conducted. Cross-tensile and shearing tests were carried out to analyze the mechanical properties of the clinched joint, including tensile strength, shearing strength, and absorbed energy. In addition, the failure modes of the clinched joints were discussed. Results indicated that the clinched joint with a stiff top sheet had increased static strength regardless of the test type. The clinched joint with a thick top sheet demonstrated lower static strength than the joint with a thick bottom sheet in the cross-tensile test. However, this result was reversed in the shearing tests. The flat clinching process has a great potential in joining dissimilar and various thickness materials.
基金financial supports from the National Natural Science Foundation of China (No. 51805416)the Young Elite Scientists Sponsorship Program by CAST, China (No. YESS20200279)+3 种基金the Natural Science Foundation of Hunan Province, China (No. 2020JJ5716)the Project of State Key Laboratory of High Performance Complex Manufacturing, Central South University, China (No. ZZYJKT2019-01)the Hunan Provincial Natural Science Foundation for Excellent Young Scholars, China (No. 2021JJ20059)the Huxiang High-Level Talent Gathering Project of Hunan Province, China (No. 2019RS1002)。
文摘To extend the service life of the clinched joint,a reconditioning process conducted with an additional tubular rivet was proposed in this work.Different reconditioning forces were employed to produce dissimilar reconditioned joints by experimental method.The experimental results indicated that the neck fracture was the common failure mode of both original clinched and reconditioned joints.Compared with the original clinched joint,the shearing strength of the reconditioned joint produced by a reconditioning force of 40 kN increased from 1810.5 to 1986.47 N,and the energy absorption increased from 2.34 to 3.46 J.The range of effective reconditioning force was from 35 to 40 kN and 40 kN was the best choice for reconditioning the AA5052 failed joints.The mechanical properties of the reconditioned joints are obviously better than those of the original clinched joints,which fully demonstrates that the reconditioning method proposed in this work has a broad prospect of industrial application.
基金the National Natural Science Foundation of China(Nos.51675414,51805416)the Joint Fund for Aerospace Advanced Manufacturing Technology Research Key Program,China(No.U1937203).
基金Project(52275398)supported by the National Natural Science Foundation of ChinaProject(2023CXQD068)supported by the Innovation-Driven Research Programme of Central South University,China+3 种基金Project(2021JJ20059)supported by the Hunan Provincial Natural Science Foundation for Excellent Young Scholars,ChinaProject(ZZYJKT2022-01)supported by the State Key Laboratory of High Performance Complex Manufacturing,Central South University,ChinaProject(2021RC3024)supported by the Huxiang Young Talents Program of Hunan Province,ChinaProject(2021RC5001)supported by the Huxiang High-level Talent Gathering Project of Hunan Province,China。