To prepare potassium titanate catalyst, a novel citrate acid complex-combustion method using CH3COOK and Ti（OC4H9）4 as raw materials was developed. The crystalline phase and surface morphology of K2Ti205 were invest...To prepare potassium titanate catalyst, a novel citrate acid complex-combustion method using CH3COOK and Ti（OC4H9）4 as raw materials was developed. The crystalline phase and surface morphology of K2Ti205 were investigated by X-ray diffraction （XRD）, field emission scanning electron microscope （FE-SEM） and transmission electron microscope （TEM）. The impact of some factors, such as the type of contact between K2Ti205 and soot, the content of water vapor and SO2 in exhaust, and the repeated use on catalytic activity of K2Ti205 were studied by temperature programmed reaction （TPR）. A comparison between the new method and the reported ones on catalytic activity of potassium titanate was investigated. The results showed that K2Ti205 had high catalytic activity and good stability.展开更多
我们采用柠檬酸配合法制备了Ce基复合氧化物催化剂,分别在热重分析仪(TG)和管式反应器中测试了其氧化碳烟及同时脱除NOx的催化活性;并利用XRD、BET、H2-TPR、XPS表征手段考察其结构.其中,Co0.1/C e La0.05复合氧化物同时催化去除碳烟和...我们采用柠檬酸配合法制备了Ce基复合氧化物催化剂,分别在热重分析仪(TG)和管式反应器中测试了其氧化碳烟及同时脱除NOx的催化活性;并利用XRD、BET、H2-TPR、XPS表征手段考察其结构.其中,Co0.1/C e La0.05复合氧化物同时催化去除碳烟和NOx的性能最佳,碳烟脱除率为50%的反应温度为301℃,N2产率为41.4%.实验结果表明,Co主要以氧化物形式均匀分散在Ce-La固溶体表面,Co3+与Co2+价态共存,离子间的变价有利于提高催化剂的氧化还原性能,有效降低了碳烟的起燃温度.La的引入增大了催化剂的比表面积,抑制了Ce O2晶粒长大,进而提高了N2产率.部分La和Co形成了微量的La Co O3,形成了更多氧空位,有利于提高催化氧化碳烟的活性.展开更多
基金the financial supports provided for this research by the Education Department of Liaoning Province of China(No.2009T061)the Ministry of Education of China(No.[2010]1561)
文摘To prepare potassium titanate catalyst, a novel citrate acid complex-combustion method using CH3COOK and Ti（OC4H9）4 as raw materials was developed. The crystalline phase and surface morphology of K2Ti205 were investigated by X-ray diffraction （XRD）, field emission scanning electron microscope （FE-SEM） and transmission electron microscope （TEM）. The impact of some factors, such as the type of contact between K2Ti205 and soot, the content of water vapor and SO2 in exhaust, and the repeated use on catalytic activity of K2Ti205 were studied by temperature programmed reaction （TPR）. A comparison between the new method and the reported ones on catalytic activity of potassium titanate was investigated. The results showed that K2Ti205 had high catalytic activity and good stability.
文摘我们采用柠檬酸配合法制备了Ce基复合氧化物催化剂,分别在热重分析仪(TG)和管式反应器中测试了其氧化碳烟及同时脱除NOx的催化活性;并利用XRD、BET、H2-TPR、XPS表征手段考察其结构.其中,Co0.1/C e La0.05复合氧化物同时催化去除碳烟和NOx的性能最佳,碳烟脱除率为50%的反应温度为301℃,N2产率为41.4%.实验结果表明,Co主要以氧化物形式均匀分散在Ce-La固溶体表面,Co3+与Co2+价态共存,离子间的变价有利于提高催化剂的氧化还原性能,有效降低了碳烟的起燃温度.La的引入增大了催化剂的比表面积,抑制了Ce O2晶粒长大,进而提高了N2产率.部分La和Co形成了微量的La Co O3,形成了更多氧空位,有利于提高催化氧化碳烟的活性.