Considering aviation and space sectors, aluminium alloys are commonly used due to its excellent mechanical and physical properties. Though satellite hard-ware is confined to controlled environment, it requires anticor...Considering aviation and space sectors, aluminium alloys are commonly used due to its excellent mechanical and physical properties. Though satellite hard-ware is confined to controlled environment, it requires anticorrosive treatment over metal substrate followed by a systematic coating scheme. The trivalent chromium coating was deposited over three aluminium alloys namely AA6063, AA7075 and AA6082. The variation in corrosion resistance property of trivalent chromium over each aluminium alloy has been studied in detail. The Neutral Salt Spray (NSS) test result shows that trivalent chromium coating over AA7075 alloy is affected by pitting corrosion compared to other two alloys. In addition to that, NSS test also proves that thickness of the layer does not have any influence corrosion resistance property of trivalent chromium coating. Furthermore, ions in trivalent chromium coating was identified using Secondary Neutral Mass Spectroscopy (SNMS) and degradation of coating in a corrosive liquid studied using Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES) instrument to understand mechanism of corrosion. The results indicated that both coating and substrate is involved in corrosion process. The number of elements dissolved in to salt solution reveals the weak ionic bonding of coating towards substrates. In comparison, AA7075 alloy has weaker bonding than AA6082 and AA6063 series. The alloying elements such as zinc and copper are removed from substrate by corrosive solution.展开更多
A no pollution organic acid based conversion coating solution MIS. No.1 has been examined as to its suitability as possible replacement for chromate containing formulations on magnesium alloys. Investigations have c...A no pollution organic acid based conversion coating solution MIS. No.1 has been examined as to its suitability as possible replacement for chromate containing formulations on magnesium alloys. Investigations have concentrated on the formation of passive film from simple MIS. No.1 solution using immersion. The morphology of passivated surfaces was examined using scanning electron microscopy (SEM). The corrosion resistance of the passivated surfaces and the painted surface was assessed using electrochemical techniques as well as humidity and salt fog tests. It was concluded that the surface treatment magnesium alloy by MIS.No.1 solution is more effective than that by chromate coating treatment, and the MIS.No.1 coating is also suitable for painting's pretreatment.展开更多
文摘Considering aviation and space sectors, aluminium alloys are commonly used due to its excellent mechanical and physical properties. Though satellite hard-ware is confined to controlled environment, it requires anticorrosive treatment over metal substrate followed by a systematic coating scheme. The trivalent chromium coating was deposited over three aluminium alloys namely AA6063, AA7075 and AA6082. The variation in corrosion resistance property of trivalent chromium over each aluminium alloy has been studied in detail. The Neutral Salt Spray (NSS) test result shows that trivalent chromium coating over AA7075 alloy is affected by pitting corrosion compared to other two alloys. In addition to that, NSS test also proves that thickness of the layer does not have any influence corrosion resistance property of trivalent chromium coating. Furthermore, ions in trivalent chromium coating was identified using Secondary Neutral Mass Spectroscopy (SNMS) and degradation of coating in a corrosive liquid studied using Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES) instrument to understand mechanism of corrosion. The results indicated that both coating and substrate is involved in corrosion process. The number of elements dissolved in to salt solution reveals the weak ionic bonding of coating towards substrates. In comparison, AA7075 alloy has weaker bonding than AA6082 and AA6063 series. The alloying elements such as zinc and copper are removed from substrate by corrosive solution.
文摘A no pollution organic acid based conversion coating solution MIS. No.1 has been examined as to its suitability as possible replacement for chromate containing formulations on magnesium alloys. Investigations have concentrated on the formation of passive film from simple MIS. No.1 solution using immersion. The morphology of passivated surfaces was examined using scanning electron microscopy (SEM). The corrosion resistance of the passivated surfaces and the painted surface was assessed using electrochemical techniques as well as humidity and salt fog tests. It was concluded that the surface treatment magnesium alloy by MIS.No.1 solution is more effective than that by chromate coating treatment, and the MIS.No.1 coating is also suitable for painting's pretreatment.