采用共沉淀和固相烧结工艺制备LiNi0.5Mn1.5O4和LiCr0.1Ni0.45Mn1.45O4正极材料,对其比表面积、振实密度、倍率性能、高低温循环性能等性能指标进行测试,并利用SEM、XRD对所制材料进行形貌观察及物相分析。结果表明:添加微量Cr元素可稳...采用共沉淀和固相烧结工艺制备LiNi0.5Mn1.5O4和LiCr0.1Ni0.45Mn1.45O4正极材料,对其比表面积、振实密度、倍率性能、高低温循环性能等性能指标进行测试,并利用SEM、XRD对所制材料进行形貌观察及物相分析。结果表明:添加微量Cr元素可稳定材料结构,降低比表面积,改善LiNi0.5Mn1.5O4材料电化学性能;LiCr0.1Ni0.45Mn1.45O4正极材料振实密度可达到2.32 g/cm3,比表面积可达到0.51 m2/g,25℃下1.5C充放电,最高容量达到127.2 m A·h/g,300次循环后容量保持率为94.9%;50℃下1.5C充放电,初始容量达到128.5 m A·h/g,200次循环后容量保持率为88.7%。经XRD分析,循环完成后材料尖晶石的结构没有变化。展开更多
1 Results The pyrolyzed product of peanut shells was utilized as a carbon source to synthesize a LiFePO4/C composite.The advantages of using agricultural wastes such as peanut shells are low costs,easy processing,and ...1 Results The pyrolyzed product of peanut shells was utilized as a carbon source to synthesize a LiFePO4/C composite.The advantages of using agricultural wastes such as peanut shells are low costs,easy processing,and environmentally benigness.Peanut shell was first treated with a porogenic agent to produce a precursor with high porosity and surface area (>2 000 m2·g-1).A small amount of precursor was mixed with LiFePO4 fine powders and heated.The optimum calcination process for synthesizing LiFePO4/C co...展开更多
文摘采用共沉淀和固相烧结工艺制备LiNi0.5Mn1.5O4和LiCr0.1Ni0.45Mn1.45O4正极材料,对其比表面积、振实密度、倍率性能、高低温循环性能等性能指标进行测试,并利用SEM、XRD对所制材料进行形貌观察及物相分析。结果表明:添加微量Cr元素可稳定材料结构,降低比表面积,改善LiNi0.5Mn1.5O4材料电化学性能;LiCr0.1Ni0.45Mn1.45O4正极材料振实密度可达到2.32 g/cm3,比表面积可达到0.51 m2/g,25℃下1.5C充放电,最高容量达到127.2 m A·h/g,300次循环后容量保持率为94.9%;50℃下1.5C充放电,初始容量达到128.5 m A·h/g,200次循环后容量保持率为88.7%。经XRD分析,循环完成后材料尖晶石的结构没有变化。
文摘1 Results The pyrolyzed product of peanut shells was utilized as a carbon source to synthesize a LiFePO4/C composite.The advantages of using agricultural wastes such as peanut shells are low costs,easy processing,and environmentally benigness.Peanut shell was first treated with a porogenic agent to produce a precursor with high porosity and surface area (>2 000 m2·g-1).A small amount of precursor was mixed with LiFePO4 fine powders and heated.The optimum calcination process for synthesizing LiFePO4/C co...