Using the inexpensive inorganic salts as the starting materials,pure yttria nanopowders were prepared by sol-gel method. The primary particles are spherical and about 60 nm in diameter with a narrow size distribution....Using the inexpensive inorganic salts as the starting materials,pure yttria nanopowders were prepared by sol-gel method. The primary particles are spherical and about 60 nm in diameter with a narrow size distribution. Moderate sulfate ions used as additive were the key to the formation of precursor and the preparation of spherical Y_2O_3 nanopowders. Transformation of the precursor was investigated during the calcining. The influence of calcination temperature on size and purity of production was analyzed. The results show that higher temperature is beneficial to the preparation of pure and complete crystallization of yttria powders under the condition of not making particles excessively grow.展开更多
We proposed a good calcinations condition of the ZnO disk to control the crystallography and nanoparticles in ZnO disk. The crystallography of precursor powder and disk powder were analyzed by the X-ray diffraction (X...We proposed a good calcinations condition of the ZnO disk to control the crystallography and nanoparticles in ZnO disk. The crystallography of precursor powder and disk powder were analyzed by the X-ray diffraction (XRD). The mean nanoparticles of ZnO disk was determinate by XRD results and observed by scanning electron microscope. The temperature ranges of 400℃ to 650℃ in air for 30 minutes were used calcinations ZnO disk. These temperature can be controlled the single phase, lattice parameters, unit cell volume, crystalline size, d-value, texture coefficient and bond lengths of Zn–Zn, Zn–O and O–O which correspond significantly the hexagonal crystal structure. The nanoparticles were small changed mean of 76.59 nm at the calcinations temperature range.展开更多
文摘Using the inexpensive inorganic salts as the starting materials,pure yttria nanopowders were prepared by sol-gel method. The primary particles are spherical and about 60 nm in diameter with a narrow size distribution. Moderate sulfate ions used as additive were the key to the formation of precursor and the preparation of spherical Y_2O_3 nanopowders. Transformation of the precursor was investigated during the calcining. The influence of calcination temperature on size and purity of production was analyzed. The results show that higher temperature is beneficial to the preparation of pure and complete crystallization of yttria powders under the condition of not making particles excessively grow.
文摘We proposed a good calcinations condition of the ZnO disk to control the crystallography and nanoparticles in ZnO disk. The crystallography of precursor powder and disk powder were analyzed by the X-ray diffraction (XRD). The mean nanoparticles of ZnO disk was determinate by XRD results and observed by scanning electron microscope. The temperature ranges of 400℃ to 650℃ in air for 30 minutes were used calcinations ZnO disk. These temperature can be controlled the single phase, lattice parameters, unit cell volume, crystalline size, d-value, texture coefficient and bond lengths of Zn–Zn, Zn–O and O–O which correspond significantly the hexagonal crystal structure. The nanoparticles were small changed mean of 76.59 nm at the calcinations temperature range.