Ni/Al_2O_3-SiO_2 catalysts were synthesized via one-step method employing SiO_2 as an additive for the selective hydrogenation of butyne-1,4-diol(B_3D) to butane-1,4-diol(B1D). The prepared catalysts were evaluated by...Ni/Al_2O_3-SiO_2 catalysts were synthesized via one-step method employing SiO_2 as an additive for the selective hydrogenation of butyne-1,4-diol(B_3D) to butane-1,4-diol(B1D). The prepared catalysts were evaluated by a series of characterization techniques including BET, XRD, SEM, EDX-mapping, TEM, H_2-TPR, XPS, NH_3-TPD and Py-FTIR. Compared to Ni/Al_2O_3 catalyst, the SiO_2-doped samples exhibited better B_3D conversion. SiO_2 could help to form a strong interaction between NiO with the support, which inhibited Ni agglomeration at high temperature, improved the Ni dispersion, and enhanced the hydrogenation activity. B_1D selectivity was mainly influenced by the quantity of Lewis acid sites in addition to the Ni dispersion. The catalyst with a silica loading of 6.4% demonstrated an excellent selectivity of 75.18%(by 13% higher than the contrastive Ni/Al_2O_3 catalyst), which was attributed to the larger amount of Lewis acid sites and the moderate interaction between NiO with the support, which could facilitate the nickel dispersion on a preferable surface area of 176.3 m^2/g of support.展开更多
基金Financial support from the National Natural Science Foundation of China (21163019) is gratefully acknowledged
文摘Ni/Al_2O_3-SiO_2 catalysts were synthesized via one-step method employing SiO_2 as an additive for the selective hydrogenation of butyne-1,4-diol(B_3D) to butane-1,4-diol(B1D). The prepared catalysts were evaluated by a series of characterization techniques including BET, XRD, SEM, EDX-mapping, TEM, H_2-TPR, XPS, NH_3-TPD and Py-FTIR. Compared to Ni/Al_2O_3 catalyst, the SiO_2-doped samples exhibited better B_3D conversion. SiO_2 could help to form a strong interaction between NiO with the support, which inhibited Ni agglomeration at high temperature, improved the Ni dispersion, and enhanced the hydrogenation activity. B_1D selectivity was mainly influenced by the quantity of Lewis acid sites in addition to the Ni dispersion. The catalyst with a silica loading of 6.4% demonstrated an excellent selectivity of 75.18%(by 13% higher than the contrastive Ni/Al_2O_3 catalyst), which was attributed to the larger amount of Lewis acid sites and the moderate interaction between NiO with the support, which could facilitate the nickel dispersion on a preferable surface area of 176.3 m^2/g of support.