Anisotropic MnBi/NdFeB （MnBi contents of 0 wt%, 20 wt%, 40 wt%, 60 wt%, 80 wt%, and 100 wt%） hybrid bonded magnets were prepared by molding compression using MnBi powders and commercial hydro-genation disproportiona...Anisotropic MnBi/NdFeB （MnBi contents of 0 wt%, 20 wt%, 40 wt%, 60 wt%, 80 wt%, and 100 wt%） hybrid bonded magnets were prepared by molding compression using MnBi powders and commercial hydro-genation disproportionation desorption and recombination （HDDR） NdFeB powders. Magnetic measurements at room temperature show that with MnBi content increasing, the magnetic properties of the MnBi/NdFeB hybrid bonded magnets all decrease gradually, while the density of the hybrid magnets improves almost linearly. In a temperature range of 293-398 K, the coercivity temperature coefficient of the hybrid magnets improves gradually from -0.59 %.K^-1 for the pure NdFeB bonded magnet to -0.32 %.K^-1 for the hybrid bonded magnet with 80 wt% MnBi, and the pure MnBi bonded magnet exhibits a positive coercivity temperature coefficient of 0.61%-K^-1.展开更多
为获得磁性能适中的磁体,采用流动温压成型技术制备了各向同性粘结Nd Fe B/锶铁氧体复合磁体.利用振动样品磁强计(VSM)研究了不同粘结剂对粘结Nd Fe B/锶铁氧体复合磁体磁性能的影响.研究表明:环氧值适中的酚醛环氧树脂制备的磁体具有...为获得磁性能适中的磁体,采用流动温压成型技术制备了各向同性粘结Nd Fe B/锶铁氧体复合磁体.利用振动样品磁强计(VSM)研究了不同粘结剂对粘结Nd Fe B/锶铁氧体复合磁体磁性能的影响.研究表明:环氧值适中的酚醛环氧树脂制备的磁体具有较好的磁性能;当采用环氧值为0.480 mol/100 g酚醛环氧树脂BPANE8200H做粘结剂时,粘结Nd Fe B/锶铁氧体复合磁体获得了最佳的磁性能:Br=0.55 T,Hcj=620.6 k A/m,(BH)max=45.6 k J/m3.在保证磁体磁性能的前提下兼顾力学性能,粘结磁体流动温压成型温度参数的设置必须考虑粘结剂的软化点温度.展开更多
Magnetic properties and intergranular action in bonded hybrid magnets,based on NdFeB and strontium ferrite powders were investigated.The long-range magnetostatic interaction and short-range exchange coupling interacti...Magnetic properties and intergranular action in bonded hybrid magnets,based on NdFeB and strontium ferrite powders were investigated.The long-range magnetostatic interaction and short-range exchange coupling interaction existed simultaneously in bonded hybrid magnets,and neither of them could be neglected.Some magnetic property parameters of hybrid magnets could be approximately obtained by adding the hysteresis loops of two magnets pro rata.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51271005)the Beijing Municipal Natural Science Foundation(No.2122006)+2 种基金the Scientific Research Foundation for the Returned Overseas Chinese Scholars,State Education Ministry(No.32009001201301)the Project from Samsung Advanced Institute of Technology(No.46009001201402)the Fundamental Research Foundation of Beijing University of Technology(No.009000514313002)
文摘Anisotropic MnBi/NdFeB （MnBi contents of 0 wt%, 20 wt%, 40 wt%, 60 wt%, 80 wt%, and 100 wt%） hybrid bonded magnets were prepared by molding compression using MnBi powders and commercial hydro-genation disproportionation desorption and recombination （HDDR） NdFeB powders. Magnetic measurements at room temperature show that with MnBi content increasing, the magnetic properties of the MnBi/NdFeB hybrid bonded magnets all decrease gradually, while the density of the hybrid magnets improves almost linearly. In a temperature range of 293-398 K, the coercivity temperature coefficient of the hybrid magnets improves gradually from -0.59 %.K^-1 for the pure NdFeB bonded magnet to -0.32 %.K^-1 for the hybrid bonded magnet with 80 wt% MnBi, and the pure MnBi bonded magnet exhibits a positive coercivity temperature coefficient of 0.61%-K^-1.
文摘为获得磁性能适中的磁体,采用流动温压成型技术制备了各向同性粘结Nd Fe B/锶铁氧体复合磁体.利用振动样品磁强计(VSM)研究了不同粘结剂对粘结Nd Fe B/锶铁氧体复合磁体磁性能的影响.研究表明:环氧值适中的酚醛环氧树脂制备的磁体具有较好的磁性能;当采用环氧值为0.480 mol/100 g酚醛环氧树脂BPANE8200H做粘结剂时,粘结Nd Fe B/锶铁氧体复合磁体获得了最佳的磁性能:Br=0.55 T,Hcj=620.6 k A/m,(BH)max=45.6 k J/m3.在保证磁体磁性能的前提下兼顾力学性能,粘结磁体流动温压成型温度参数的设置必须考虑粘结剂的软化点温度.
基金Project supported by the Nanocompound Rare Earth Permanent Magnetic Material Research(BG2004033)National KeyProject for Basic Research(2005CB623605)
文摘Magnetic properties and intergranular action in bonded hybrid magnets,based on NdFeB and strontium ferrite powders were investigated.The long-range magnetostatic interaction and short-range exchange coupling interaction existed simultaneously in bonded hybrid magnets,and neither of them could be neglected.Some magnetic property parameters of hybrid magnets could be approximately obtained by adding the hysteresis loops of two magnets pro rata.