A series of MgO-based adsorbents were prepared through solution–combustion synthesis and ball-milling process.The prepared MgO-based powders were characterized using X-ray diffraction,scanning electron microscopy,N_2...A series of MgO-based adsorbents were prepared through solution–combustion synthesis and ball-milling process.The prepared MgO-based powders were characterized using X-ray diffraction,scanning electron microscopy,N_2 physisorption measurements,and employed as potential adsorbents for CO_2 adsorption.The influence of structural and textural properties of these adsorbents over the CO_2 adsorption behaviour was also investigated.The results showed that MgO-based products prepared by solution–combustion and ball-milling processes,were highly porous,fluffy,nanocrystalline structures in nature,which are unique physico-chemical properties that significantly contribute to enhance their CO_2 adsorption.It was found that the MgO synthesized by solution combustion process,using a molar ratio of urea to magnesium nitrate（2：1）,and treated by ball-milling during 2.5 hr（MgO-BM2.5h）,exhibited the maximum CO_2 adsorption capacity of 1.611 mmol/g at 25℃ and 1 atm,mainly via chemisorption.The CO_2 adsorption behaviour on the MgO-based adsorbents was correlated to their improved specific surface area,total pore volume,pore size distribution and crystallinity.The reusability of synthesized MgO-BM2.5h was confirmed by five consecutive CO_2adsorption–desorption times,without any significant loss of performance,that supports the potential of MgO-based adsorbent.The results confirmed that the special features of MgO prepared by solution–combustion and treated by ball-milling during 2.5 hr are favorable to be used as effective MgO-based adsorbent in post-combustion CO_2 capture technologies.展开更多
The doctor-blade method is investigated for the preparation of Cu2ZnSnS4 films for low-cost solar cell application. Cu2ZnSnS4 precursor powder, the main raw material for the doctor-blade paste, is synthesized by a sim...The doctor-blade method is investigated for the preparation of Cu2ZnSnS4 films for low-cost solar cell application. Cu2ZnSnS4 precursor powder, the main raw material for the doctor-blade paste, is synthesized by a simple ball-milling process. The doctor-bladed Cu2ZnSnS4 films are annealed in N2 ambient under various conditions and characterized by X-ray diffraction, ultraviolent/vis spectrophotometry, scanning electron microscopy, and current-voltage （J-V） meansurement. Our experimental results indicate that （i） the X-ray diffraction peaks of the Cu2ZnSnS4 precursor powder each show a red shift of about 0.4°; （ii） the high-temperature annealing process can effectively improve the crystallinity of the doctor-bladed Cu2ZnSnS4, whereas an overlong annealing introduces defects; （iii） the band gap value of the doctor-bladed Cu2ZnSnS4 is around 1.41 eV; （iv） the short-circuit current density, the open-circuit voltage, the fill factor, and the efficiency of the best Cu2ZnSnS4 solar cell obtained with the superstrate structure of fluorine-doped tin oxide glass/TiO2/In2S3/Cu2ZnSnS4/Mo are 7.82 mA/cm2, 240 mV, 0.29, and 0.55%, respectively.展开更多
基金the National Institute of Nuclear Research(ININ),México,for financial support through project CB-406 stagesⅠ-Ⅲ
文摘A series of MgO-based adsorbents were prepared through solution–combustion synthesis and ball-milling process.The prepared MgO-based powders were characterized using X-ray diffraction,scanning electron microscopy,N_2 physisorption measurements,and employed as potential adsorbents for CO_2 adsorption.The influence of structural and textural properties of these adsorbents over the CO_2 adsorption behaviour was also investigated.The results showed that MgO-based products prepared by solution–combustion and ball-milling processes,were highly porous,fluffy,nanocrystalline structures in nature,which are unique physico-chemical properties that significantly contribute to enhance their CO_2 adsorption.It was found that the MgO synthesized by solution combustion process,using a molar ratio of urea to magnesium nitrate（2：1）,and treated by ball-milling during 2.5 hr（MgO-BM2.5h）,exhibited the maximum CO_2 adsorption capacity of 1.611 mmol/g at 25℃ and 1 atm,mainly via chemisorption.The CO_2 adsorption behaviour on the MgO-based adsorbents was correlated to their improved specific surface area,total pore volume,pore size distribution and crystallinity.The reusability of synthesized MgO-BM2.5h was confirmed by five consecutive CO_2adsorption–desorption times,without any significant loss of performance,that supports the potential of MgO-based adsorbent.The results confirmed that the special features of MgO prepared by solution–combustion and treated by ball-milling during 2.5 hr are favorable to be used as effective MgO-based adsorbent in post-combustion CO_2 capture technologies.
文摘The doctor-blade method is investigated for the preparation of Cu2ZnSnS4 films for low-cost solar cell application. Cu2ZnSnS4 precursor powder, the main raw material for the doctor-blade paste, is synthesized by a simple ball-milling process. The doctor-bladed Cu2ZnSnS4 films are annealed in N2 ambient under various conditions and characterized by X-ray diffraction, ultraviolent/vis spectrophotometry, scanning electron microscopy, and current-voltage （J-V） meansurement. Our experimental results indicate that （i） the X-ray diffraction peaks of the Cu2ZnSnS4 precursor powder each show a red shift of about 0.4°; （ii） the high-temperature annealing process can effectively improve the crystallinity of the doctor-bladed Cu2ZnSnS4, whereas an overlong annealing introduces defects; （iii） the band gap value of the doctor-bladed Cu2ZnSnS4 is around 1.41 eV; （iv） the short-circuit current density, the open-circuit voltage, the fill factor, and the efficiency of the best Cu2ZnSnS4 solar cell obtained with the superstrate structure of fluorine-doped tin oxide glass/TiO2/In2S3/Cu2ZnSnS4/Mo are 7.82 mA/cm2, 240 mV, 0.29, and 0.55%, respectively.