The present work involves the development of siliconized epoxy resin to overcome the drawback of epoxy resin like poor impact strength, high rigidity and moisture absorbing nature because of which they are not applied...The present work involves the development of siliconized epoxy resin to overcome the drawback of epoxy resin like poor impact strength, high rigidity and moisture absorbing nature because of which they are not applied as corrosion resistant coating. By embedding silicone into the back bone of polymeric resin the above drawback can be reduced to substantial level. For achieving this, siliconised epoxy resins were prepared by reacting amine terminated silicone resin with novolac epoxy resin and meta-phenylenediamine was used as curing agent. The applied films of coating were baked at 150oC. Cured films were evaluated for their thermal, mechanical, chemical and corrosion resistance properties to ascertain the commercial utility of these eco-friendly resin for use in anti corrosive formulations. The siliconized epoxy resins system was found to exhibit good thermal and anticorrosive properties.展开更多
In order to improve the corrosion resistance of AZ91D magnesium alloy,a coating was formed by a potentiostatic technique from a solutions containing Ce(NO_(3))_(3),Na_(2)MoO_(4)and citric acid(H_(3)Cit).The degree of ...In order to improve the corrosion resistance of AZ91D magnesium alloy,a coating was formed by a potentiostatic technique from a solutions containing Ce(NO_(3))_(3),Na_(2)MoO_(4)and citric acid(H_(3)Cit).The degree of corrosion protection achieved was evaluated in simulated physiological solution by monitoring the open circuit potential,polarization techniques and electrochemical impedance spectroscopy(EIS).Surface analysis techniques(SEM,EDS,X-ray diffraction and X-ray photoelectron spectroscopy(XPS))were used for coating characterization.The film is mainly composed by cerium and molybdenum oxides and magnesium oxides and hydroxides.The obtained results show that the corrosion resistance of the coated electrodes has been increased significantly.This improvement in the anticorrosive performance is in part due to the corrosion inhibition properties of H_(3)Cit.展开更多
文摘The present work involves the development of siliconized epoxy resin to overcome the drawback of epoxy resin like poor impact strength, high rigidity and moisture absorbing nature because of which they are not applied as corrosion resistant coating. By embedding silicone into the back bone of polymeric resin the above drawback can be reduced to substantial level. For achieving this, siliconised epoxy resins were prepared by reacting amine terminated silicone resin with novolac epoxy resin and meta-phenylenediamine was used as curing agent. The applied films of coating were baked at 150oC. Cured films were evaluated for their thermal, mechanical, chemical and corrosion resistance properties to ascertain the commercial utility of these eco-friendly resin for use in anti corrosive formulations. The siliconized epoxy resins system was found to exhibit good thermal and anticorrosive properties.
基金CONICET(PIP-112-201101-00055)ANPCYT(PICT-2015-0726)Universidad Nacional del Sur(PGI 24/M127),Bahía Blanca,Argentina。
文摘In order to improve the corrosion resistance of AZ91D magnesium alloy,a coating was formed by a potentiostatic technique from a solutions containing Ce(NO_(3))_(3),Na_(2)MoO_(4)and citric acid(H_(3)Cit).The degree of corrosion protection achieved was evaluated in simulated physiological solution by monitoring the open circuit potential,polarization techniques and electrochemical impedance spectroscopy(EIS).Surface analysis techniques(SEM,EDS,X-ray diffraction and X-ray photoelectron spectroscopy(XPS))were used for coating characterization.The film is mainly composed by cerium and molybdenum oxides and magnesium oxides and hydroxides.The obtained results show that the corrosion resistance of the coated electrodes has been increased significantly.This improvement in the anticorrosive performance is in part due to the corrosion inhibition properties of H_(3)Cit.