Simple three-point bending test at ambient tempera- ture characterized the mechanical behavior of burned Al2O3 -C refractories before and after thermal shock in association with the processing parameters （graphite co...Simple three-point bending test at ambient tempera- ture characterized the mechanical behavior of burned Al2O3 -C refractories before and after thermal shock in association with the processing parameters （graphite content and coking temperature, etc. ）. The results showed that non-linear plastic-elastic behavior under load lower than cold modulus of rupture （CMOR） was registered in all specimens and real linear elastic behavior could be identified after the first load, The total deformation could be divided into two parts, plastic and elastic areas. The graphite content and joint bonding system of carbon and ceramic phases were responsible for mechanical behavior of Al2O3 - C refractories.展开更多
The Al2O3 -SiC-C bricks for iron ladles were pre-pared asing bauxite, fused corundum,pyrophyllite, SiC powder and flake graphite as main starting materials, and phenolic resin as binder. The effect of pyroph,yllite pa...The Al2O3 -SiC-C bricks for iron ladles were pre-pared asing bauxite, fused corundum,pyrophyllite, SiC powder and flake graphite as main starting materials, and phenolic resin as binder. The effect of pyroph,yllite particle size on permanent change in dimensions, cold crushing strength, oxidation resistance, and corrosion resistance of Al2O3 - SiC - C bricks was investigated. The results show that with the decrease of the pyrophyllite particle size, the permanent change in dimensions of Al2O3 - SiC - C bricks decreases, cold crushing strength increases, the oxidation resistance at 1400 ℃ increases, and the corrosion resistance at 1500℃ decreases.展开更多
文摘Simple three-point bending test at ambient tempera- ture characterized the mechanical behavior of burned Al2O3 -C refractories before and after thermal shock in association with the processing parameters （graphite content and coking temperature, etc. ）. The results showed that non-linear plastic-elastic behavior under load lower than cold modulus of rupture （CMOR） was registered in all specimens and real linear elastic behavior could be identified after the first load, The total deformation could be divided into two parts, plastic and elastic areas. The graphite content and joint bonding system of carbon and ceramic phases were responsible for mechanical behavior of Al2O3 - C refractories.
文摘The Al2O3 -SiC-C bricks for iron ladles were pre-pared asing bauxite, fused corundum,pyrophyllite, SiC powder and flake graphite as main starting materials, and phenolic resin as binder. The effect of pyroph,yllite particle size on permanent change in dimensions, cold crushing strength, oxidation resistance, and corrosion resistance of Al2O3 - SiC - C bricks was investigated. The results show that with the decrease of the pyrophyllite particle size, the permanent change in dimensions of Al2O3 - SiC - C bricks decreases, cold crushing strength increases, the oxidation resistance at 1400 ℃ increases, and the corrosion resistance at 1500℃ decreases.