Steel T8 treated by plasma surface decarburizing was alloyed by the Xu Tec process with Co,W and Mo. An alloyed layer of Fe Co W Mo with low carbon content was formed on the surface of the high carbon steel, thus an a...Steel T8 treated by plasma surface decarburizing was alloyed by the Xu Tec process with Co,W and Mo. An alloyed layer of Fe Co W Mo with low carbon content was formed on the surface of the high carbon steel, thus an advanced gradient composite was produced. The specimens then were treated by the solution and aging treatments. The characteristics of age hardening of the alloying layer were studied. The hardness of the surface layer increases from HV200 to HV1 200 after the solution treatment at 1 190 ℃ and aging at 400 ℃ for 30 min. The results show that the surface aged high speed steel possesses not only high surface hardness, but also enough bulk strength. [展开更多
文摘Steel T8 treated by plasma surface decarburizing was alloyed by the Xu Tec process with Co,W and Mo. An alloyed layer of Fe Co W Mo with low carbon content was formed on the surface of the high carbon steel, thus an advanced gradient composite was produced. The specimens then were treated by the solution and aging treatments. The characteristics of age hardening of the alloying layer were studied. The hardness of the surface layer increases from HV200 to HV1 200 after the solution treatment at 1 190 ℃ and aging at 400 ℃ for 30 min. The results show that the surface aged high speed steel possesses not only high surface hardness, but also enough bulk strength. [