Siliconated polyurethane （Si-PU） was synthesized using isophorone diisocyanate （IPDI）, hydroxybutyl-terminated polydimethylsiloxane （PDMS）, polytetramethylene ether glycol （PTMG）, polypropylene glycol （PPG）,...Siliconated polyurethane （Si-PU） was synthesized using isophorone diisocyanate （IPDI）, hydroxybutyl-terminated polydimethylsiloxane （PDMS）, polytetramethylene ether glycol （PTMG）, polypropylene glycol （PPG）, 1,6-hexanediol （HDO）, dimethylol propionic acid （DMPA） and triethylamine （TEA）. Based on butyl acrylate （BA）, 2, 2, 2-trifluoroethylmethacrylate （TFEMA） and Si-PU as a seed emulsion, a novel core-shell type acrylic-polyurethane hybrid emulsion, containing siloxane and fluorine （F-Si-PU）, was prepared by seeded emulsion polymerization. The contents of siloxane and fluorine were determined according to the feed ratio. Fourier transform infrared spectroscopy （FTIR） was used to identify the chain structures of Si-PU and F-Si-PU. Investigation of transmission electron microscopy （TEM） confirmed the core-shell structure of F-Si-PU emulsion. Measurement results of water contact angle and the swelling ratio in water and n-octane for cured film showed that the water and the oil resistances for F-Si-PU had been significantly improved at a suitable content of fluorine and siloxane.展开更多
In order to prepare hydrophobic waterborne polyurethane coatings with better performances, the silicon-containing waterborne polyurethane（SiWPU） with functional chain extender hydroxyethyl acrylate（HEA） was prepar...In order to prepare hydrophobic waterborne polyurethane coatings with better performances, the silicon-containing waterborne polyurethane（SiWPU） with functional chain extender hydroxyethyl acrylate（HEA） was prepared first, and then a series of silicon＆fluorine-containing polyurethane/acrylate（FSiPUA） emulsions were obtained with flourine containing acrylic monomer by seed emulsion polymerization, introducing micro-nano SiO2 into FSiPUA emulsion to make the final hybrid emulsion. The properties of Si WPU, FSiPUA and SiO2/FSiPUA were investigated by fourier transform infrared spectra（FTIR）, transmission electron microscope（TEM）, Scanning Electron Microscope（SEM） and some other analytical methods. The results revealed that FSiPUA emulsion particles possessed composite core-shell structure and FSiPUA films with suitable ratio performed better than Si WPU films in hardness, water resistance and solvent resistance. The SiO2/FSiPUA films with micro-nano dual roughness structure showed a water contact angle of 136° with good resistance to acid and alkali.展开更多
基金Financial supports from the National Natural Science Foundation of China(No.50273035)Hangzhou Zhijiang Silicone Chemical Industry Co.,Ltd.are acknowledged.
文摘Siliconated polyurethane （Si-PU） was synthesized using isophorone diisocyanate （IPDI）, hydroxybutyl-terminated polydimethylsiloxane （PDMS）, polytetramethylene ether glycol （PTMG）, polypropylene glycol （PPG）, 1,6-hexanediol （HDO）, dimethylol propionic acid （DMPA） and triethylamine （TEA）. Based on butyl acrylate （BA）, 2, 2, 2-trifluoroethylmethacrylate （TFEMA） and Si-PU as a seed emulsion, a novel core-shell type acrylic-polyurethane hybrid emulsion, containing siloxane and fluorine （F-Si-PU）, was prepared by seeded emulsion polymerization. The contents of siloxane and fluorine were determined according to the feed ratio. Fourier transform infrared spectroscopy （FTIR） was used to identify the chain structures of Si-PU and F-Si-PU. Investigation of transmission electron microscopy （TEM） confirmed the core-shell structure of F-Si-PU emulsion. Measurement results of water contact angle and the swelling ratio in water and n-octane for cured film showed that the water and the oil resistances for F-Si-PU had been significantly improved at a suitable content of fluorine and siloxane.
基金Funded by the National High Technology Research and Development Program("863"Program)(No.2003AA305071)
文摘In order to prepare hydrophobic waterborne polyurethane coatings with better performances, the silicon-containing waterborne polyurethane（SiWPU） with functional chain extender hydroxyethyl acrylate（HEA） was prepared first, and then a series of silicon＆fluorine-containing polyurethane/acrylate（FSiPUA） emulsions were obtained with flourine containing acrylic monomer by seed emulsion polymerization, introducing micro-nano SiO2 into FSiPUA emulsion to make the final hybrid emulsion. The properties of Si WPU, FSiPUA and SiO2/FSiPUA were investigated by fourier transform infrared spectra（FTIR）, transmission electron microscope（TEM）, Scanning Electron Microscope（SEM） and some other analytical methods. The results revealed that FSiPUA emulsion particles possessed composite core-shell structure and FSiPUA films with suitable ratio performed better than Si WPU films in hardness, water resistance and solvent resistance. The SiO2/FSiPUA films with micro-nano dual roughness structure showed a water contact angle of 136° with good resistance to acid and alkali.