ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that...ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.展开更多
Nanometer ZrO2 - 8% Y2O3 (mole fraction, % ) powders were prepared by the EDTA (ethylenediaminetetraacetic acid) sol-gel process. Effects of the addition of ethylene glycol on agglomerate control was investigated. The...Nanometer ZrO2 - 8% Y2O3 (mole fraction, % ) powders were prepared by the EDTA (ethylenediaminetetraacetic acid) sol-gel process. Effects of the addition of ethylene glycol on agglomerate control was investigated. The results showed that because of the replacement of hydrogen bonds with ethylene glycol in the polymerized gel, gel stabilization and homogeneity were improved and close approach of gel particles was prevented, which led to reduction of hard agglomerates to some extent. Calcined at 4OO t for 2 h and 700 C for 2 h, the powders had a specific surface area of 35 m2/g, average particle size of 28 nm, and median particle size (d50) of 0. 44um with very sharp distribution, mostly being soft agglomerates.展开更多
基金Funded by the National Natural Science Foundation of China(No.51401155)the School Foundation(No.XAGDXJJ1012)The Open Fund of Shaanxi Key Laboratory of Photoelectric Functional Materials and Devices(No.ZSKJ201416)
文摘ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.
文摘Nanometer ZrO2 - 8% Y2O3 (mole fraction, % ) powders were prepared by the EDTA (ethylenediaminetetraacetic acid) sol-gel process. Effects of the addition of ethylene glycol on agglomerate control was investigated. The results showed that because of the replacement of hydrogen bonds with ethylene glycol in the polymerized gel, gel stabilization and homogeneity were improved and close approach of gel particles was prevented, which led to reduction of hard agglomerates to some extent. Calcined at 4OO t for 2 h and 700 C for 2 h, the powders had a specific surface area of 35 m2/g, average particle size of 28 nm, and median particle size (d50) of 0. 44um with very sharp distribution, mostly being soft agglomerates.