The requirement of energy-storage equipment needs to develop the lithium ion battery(LIB) with high electrochemical performance. The surface modification of commercial LiFePO_4(LFP) by utilizing zeolitic imidazolate f...The requirement of energy-storage equipment needs to develop the lithium ion battery(LIB) with high electrochemical performance. The surface modification of commercial LiFePO_4(LFP) by utilizing zeolitic imidazolate frameworks-8(ZIF-8) offers new possibilities for commercial LFP with high electrochemical performances.In this work, the carbonized ZIF-8(C_(ZIF-8)) was coated on the surface of LFP particles by the in situ growth and carbonization of ZIF-8. Transmission electron microscopy indicates that there is an approximate 10 nm coating layer with metal zinc and graphite-like carbon on the surface of LFP/C_(ZIF-8) sample. The N_2 adsorption and desorptionisotherm suggests that the coating layer has uniform and simple connecting mesopores. As cathode material, LFP/C_(ZIF-8) cathode-active material delivers a discharge specific capacity of 159.3 m Ah g^(-1) at 0.1 C and a discharge specific energy of 141.7 m Wh g^(-1) after 200 cycles at 5.0 C(the retention rate is approximate 99%). These results are attributed to the synergy improvement of the conductivity,the lithium ion diffusion coefficient, and the degree of freedom for volume change of LFP/C_(ZIF-8) cathode. This work will contribute to the improvement of the cathode materials of commercial LIB.展开更多
基金supported by the Scientific and Technological Development Project of the Beijing Education Committee(No.KZ201710005009)
文摘The requirement of energy-storage equipment needs to develop the lithium ion battery(LIB) with high electrochemical performance. The surface modification of commercial LiFePO_4(LFP) by utilizing zeolitic imidazolate frameworks-8(ZIF-8) offers new possibilities for commercial LFP with high electrochemical performances.In this work, the carbonized ZIF-8(C_(ZIF-8)) was coated on the surface of LFP particles by the in situ growth and carbonization of ZIF-8. Transmission electron microscopy indicates that there is an approximate 10 nm coating layer with metal zinc and graphite-like carbon on the surface of LFP/C_(ZIF-8) sample. The N_2 adsorption and desorptionisotherm suggests that the coating layer has uniform and simple connecting mesopores. As cathode material, LFP/C_(ZIF-8) cathode-active material delivers a discharge specific capacity of 159.3 m Ah g^(-1) at 0.1 C and a discharge specific energy of 141.7 m Wh g^(-1) after 200 cycles at 5.0 C(the retention rate is approximate 99%). These results are attributed to the synergy improvement of the conductivity,the lithium ion diffusion coefficient, and the degree of freedom for volume change of LFP/C_(ZIF-8) cathode. This work will contribute to the improvement of the cathode materials of commercial LIB.