The anisotropic plastic deformation behavior of as-extruded ZK60 magnesium alloy at room tempera-ture (RT) was investigated by compressive and tensile testing in different directions, i.e. the loading axis oriented at...The anisotropic plastic deformation behavior of as-extruded ZK60 magnesium alloy at room tempera-ture (RT) was investigated by compressive and tensile testing in different directions, i.e. the loading axis oriented at 0°, 45° and 90° to the extrusion direction. The relationship between texture and plastic deformation behavior were examined. The results show that the extruded ZK60 alloy exhibits a strong ring fiber texture. The mechanical properties are strongly orientation dependent. In tension testing, the 0° specimen exhibited higher yield strength and lower elongation. In compression testing, however, ZK60 alloy exhibited almost the same yield strength in three directions. The anisotropic plastic defor-mation behavior is due to strong fiber texture and the lower symmetry of the hexagonal close packed (hcp) structure of ZK60 alloy. The correlation between texture and mechanical behaviour offers the possibility to improve the mechanical properties of magnesium alloy by optimization of the material production process.展开更多
In this study, compounded surface modification technology-high current pulsed electron beam （HCPEB） ＋ micro-plasma oxidation （MPO） was applied to treat ZK60 Mg alloys. The characteristics of the microstructure of...In this study, compounded surface modification technology-high current pulsed electron beam （HCPEB） ＋ micro-plasma oxidation （MPO） was applied to treat ZK60 Mg alloys. The characteristics of the microstructure of ZK60 Mg alloy after single MPO and HCPEB＋MPO compounded treatment were investigated by SEM. The results showed that the density of the ceramic layer of HCPEB＋MPO-treated ZK60 Mg alloy was improved and defects were reduced compared to that under MPO treatment alone. Surface modified layer of ZK60 Mg alloys treated by HCPEB＋MPO was divided into three zones, namely the top loose ceramic zone, middle compact zone and inside HCPEB-induced melted zone. Corrosion resistance of ZK60 Mg alloy before and after the compounded surface modification was measured in a solution of 3.5% NaCl by potentiodynamic polarization curves. It was found that the corrosion current density of ZK60 Mg alloys could be reduced by about three orders of magnitude, from 311μA/cm^2 of the original sample to 0.2μA/cm^2 of the HCPEB＋MPO-treated sample. This indicates the great application potential of the HCPEB＋MPO compounded surface modification technology in improving the corrosion resistance of ZK60 Mg alloys in the future.展开更多
基金Supported by the Natural Science Foundation of China (Grant No. 50674067)the National Basic Research Program of China ("973" project) (Grant No. 2007CB613701)the Program of Shanghai Subject Chief Scientist (Grant No. 08XD14020)
文摘The anisotropic plastic deformation behavior of as-extruded ZK60 magnesium alloy at room tempera-ture (RT) was investigated by compressive and tensile testing in different directions, i.e. the loading axis oriented at 0°, 45° and 90° to the extrusion direction. The relationship between texture and plastic deformation behavior were examined. The results show that the extruded ZK60 alloy exhibits a strong ring fiber texture. The mechanical properties are strongly orientation dependent. In tension testing, the 0° specimen exhibited higher yield strength and lower elongation. In compression testing, however, ZK60 alloy exhibited almost the same yield strength in three directions. The anisotropic plastic defor-mation behavior is due to strong fiber texture and the lower symmetry of the hexagonal close packed (hcp) structure of ZK60 alloy. The correlation between texture and mechanical behaviour offers the possibility to improve the mechanical properties of magnesium alloy by optimization of the material production process.
基金supported by Liaoning BaiQianWan Talents Program of China (No. 2008921028)Doctoral Fund of Ministry of Education of China (No. 200801451082)
文摘In this study, compounded surface modification technology-high current pulsed electron beam （HCPEB） ＋ micro-plasma oxidation （MPO） was applied to treat ZK60 Mg alloys. The characteristics of the microstructure of ZK60 Mg alloy after single MPO and HCPEB＋MPO compounded treatment were investigated by SEM. The results showed that the density of the ceramic layer of HCPEB＋MPO-treated ZK60 Mg alloy was improved and defects were reduced compared to that under MPO treatment alone. Surface modified layer of ZK60 Mg alloys treated by HCPEB＋MPO was divided into three zones, namely the top loose ceramic zone, middle compact zone and inside HCPEB-induced melted zone. Corrosion resistance of ZK60 Mg alloy before and after the compounded surface modification was measured in a solution of 3.5% NaCl by potentiodynamic polarization curves. It was found that the corrosion current density of ZK60 Mg alloys could be reduced by about three orders of magnitude, from 311μA/cm^2 of the original sample to 0.2μA/cm^2 of the HCPEB＋MPO-treated sample. This indicates the great application potential of the HCPEB＋MPO compounded surface modification technology in improving the corrosion resistance of ZK60 Mg alloys in the future.
基金Project(51175018) supported by the National Natural Science Foundation of ChinaProject(HIT.NSRIF2010118) supported by the Fundamental Research Funds for the Central Universities, China