Yttria stabilized zirconia (YSZ) has widely been used as electrolyte in solid oxide fuel cell (SOFC). The microstructure of YSZ related to the fabrication process was discussed in the paper. With YSZ nano-powders abou...Yttria stabilized zirconia (YSZ) has widely been used as electrolyte in solid oxide fuel cell (SOFC). The microstructure of YSZ related to the fabrication process was discussed in the paper. With YSZ nano-powders about 40-100 nm as raw material, the YSZ adobe was manufactured by tape calendering process. The named three-step sintering process was performed at 1000 ℃ for 2 h, then raised the temperature with normal rate and as soon as up to 1400 ℃, the furnace was controlled at 1250-1300 ℃ for 10-20 h. The high dense YSZs with the relative density of 96%-99% were obtained; the grain size of YSZ could be reduced to 0.5-3 μm. The above result is benefited to co-fired in the electrode-supported SOFCs.展开更多
The properties of yttria stabilized zirconia（YSZ） related to the sintering process were discussed.YSZ nano-powders about 40-100 nm as raw material,the sub-micrometer grain sizes such as 0.4-3 μm in YSZ were gotten ...The properties of yttria stabilized zirconia（YSZ） related to the sintering process were discussed.YSZ nano-powders about 40-100 nm as raw material,the sub-micrometer grain sizes such as 0.4-3 μm in YSZ were gotten by sintering process at 1300 ℃,which was performed at 1000 ℃ for 2 h,then raised the temperature at the rate of 50 ℃ / h to 1400 ℃,then decreased directly to 1300 ℃ in 30 minutes,finally at 1300 ℃ for 5-20 hours.The ratio of bigger grain size becomes larger as the holding time increasing at 1300 ℃.The grains less than 1 μm are about 50%,eg,43.2%,52.2% and 51.1% related to 1300 ℃ holding 5 hours,8 hours and 10 hours,respectively.As YSZ grain size became small,the electrical conductivities did not decrease,even increased,about 0.20 s/cm at 1000 ℃.The reduced sintering temperature and time were benefited to co-fire with the electrodes in electrode-supported SOFCs.展开更多
Yttria-stabilized zirconia(YSZ) is the most common electrolyte material for solid oxide fuel cells. Herein, we conducted a comparative study on the densification behavior of three different kinds of commercial 8 mol% ...Yttria-stabilized zirconia(YSZ) is the most common electrolyte material for solid oxide fuel cells. Herein, we conducted a comparative study on the densification behavior of three different kinds of commercial 8 mol% YSZ powders:(i) TZ-8Y(Tosoh, Japan),(ii) MELox 8Y(MEL Chemicals, UK), and(iii) YSZ-HT(Huatsing Power, China). The comparison was made on both the selfsupporting pellets and thin-film electrolytes coated onto a NiO–YSZ anode support. For the pellets, MELox 8Y showed the highest densification at lower sintering temperatures with 93% and 96% of the theoretical density at 1250 and 1300 ℃, respectively. Although YSZ-HT showed a higher sintering rate than TZ-8Y, a sintering temperature of 1350 ℃ was required for both the powders to reach 95% of the theoretical density. For the thin-film electrolytes, on the other hand, YSZ-HT showed the highest sintering rate with a dense microstructure at a co-sintering temperature of 1250 ℃. Our results indicate that besides the average particle size, other factors such as particle size distribution and post-processing play a significant role in determining the sintering rate and densification behavior of the YSZ powders. Additionally, a close match in the sintering shrinkage of the electrolyte and anode support is important for facilitating the densification of the thin-film electrolytes.展开更多
基金The project was financiallysupportedby Ministry of Education,China(No.106087)and 863 Program of National High Technology Research Development Project,China(2005AA501050).
文摘Yttria stabilized zirconia (YSZ) has widely been used as electrolyte in solid oxide fuel cell (SOFC). The microstructure of YSZ related to the fabrication process was discussed in the paper. With YSZ nano-powders about 40-100 nm as raw material, the YSZ adobe was manufactured by tape calendering process. The named three-step sintering process was performed at 1000 ℃ for 2 h, then raised the temperature with normal rate and as soon as up to 1400 ℃, the furnace was controlled at 1250-1300 ℃ for 10-20 h. The high dense YSZs with the relative density of 96%-99% were obtained; the grain size of YSZ could be reduced to 0.5-3 μm. The above result is benefited to co-fired in the electrode-supported SOFCs.
基金Funded by the National Natural Science Foundation of China (NSFC)(No. 50730004)the New Century Elitist Project (No. NCET-06-0203)
文摘The properties of yttria stabilized zirconia（YSZ） related to the sintering process were discussed.YSZ nano-powders about 40-100 nm as raw material,the sub-micrometer grain sizes such as 0.4-3 μm in YSZ were gotten by sintering process at 1300 ℃,which was performed at 1000 ℃ for 2 h,then raised the temperature at the rate of 50 ℃ / h to 1400 ℃,then decreased directly to 1300 ℃ in 30 minutes,finally at 1300 ℃ for 5-20 hours.The ratio of bigger grain size becomes larger as the holding time increasing at 1300 ℃.The grains less than 1 μm are about 50%,eg,43.2%,52.2% and 51.1% related to 1300 ℃ holding 5 hours,8 hours and 10 hours,respectively.As YSZ grain size became small,the electrical conductivities did not decrease,even increased,about 0.20 s/cm at 1000 ℃.The reduced sintering temperature and time were benefited to co-fire with the electrodes in electrode-supported SOFCs.
基金supported by National Aeronautics and Space Administration (NASA) through Contract No.NNX15CC12C
文摘Yttria-stabilized zirconia(YSZ) is the most common electrolyte material for solid oxide fuel cells. Herein, we conducted a comparative study on the densification behavior of three different kinds of commercial 8 mol% YSZ powders:(i) TZ-8Y(Tosoh, Japan),(ii) MELox 8Y(MEL Chemicals, UK), and(iii) YSZ-HT(Huatsing Power, China). The comparison was made on both the selfsupporting pellets and thin-film electrolytes coated onto a NiO–YSZ anode support. For the pellets, MELox 8Y showed the highest densification at lower sintering temperatures with 93% and 96% of the theoretical density at 1250 and 1300 ℃, respectively. Although YSZ-HT showed a higher sintering rate than TZ-8Y, a sintering temperature of 1350 ℃ was required for both the powders to reach 95% of the theoretical density. For the thin-film electrolytes, on the other hand, YSZ-HT showed the highest sintering rate with a dense microstructure at a co-sintering temperature of 1250 ℃. Our results indicate that besides the average particle size, other factors such as particle size distribution and post-processing play a significant role in determining the sintering rate and densification behavior of the YSZ powders. Additionally, a close match in the sintering shrinkage of the electrolyte and anode support is important for facilitating the densification of the thin-film electrolytes.