It is suggested that the extremely large oxygen isotopic Tc shift recently reported in YBa2Cu3O7 may not be an intrinsic mass effect related to the mechanism but due to the small difference of the oxygen contents.
The melting temperature and critical transition temperature Tc of YBa2Cu3O7-δ with deferent content additives of PbO and BaPbO3 were studied. When PbO was doped in YBa2Cu3O7-δ, the melting temperature of YBa2Cu3O7-...The melting temperature and critical transition temperature Tc of YBa2Cu3O7-δ with deferent content additives of PbO and BaPbO3 were studied. When PbO was doped in YBa2Cu3O7-δ, the melting temperature of YBa2Cu3O7-δ was reduced, however its superconductivity was weakened. From the XRD pattern of the sintered mixture of YBa2Cu3O7-δ and PbO, it was known that there was a reaction between YBa2Cu3O7-δ and PbO, and the product was BaPbO3. Hence different contents of BaPbO3 (10mass%, 20mass% and 30mass%) were added in YBa2Cu3O7-δ. It was proved that there were no reactions between YBa2Cu3O7-δ and BaPbO3. And the superconductivity of the mixtures was much better than that of the samples with PbO additive.展开更多
LaMnO_(3)(LMO) cap layers with different surface roughness were prepared on epi-MgO/ion-beam-assisted deposition (IBAD) MgO/solution deposition planarized (SDP) Y<sub>2</sub>O<sub>3</sub>/Haste...LaMnO_(3)(LMO) cap layers with different surface roughness were prepared on epi-MgO/ion-beam-assisted deposition (IBAD) MgO/solution deposition planarized (SDP) Y<sub>2</sub>O<sub>3</sub>/Hastelloy tape. The effects of the surface roughness of LMO on the crystallization, texture and superconducting properties of Yba<sub>2</sub>Cu<sub>3</sub>O<sub>7?δ </sub> (YBCO) films were systematically investigated. The crystallization and epitaxial texture of resulting YBCO film are significantly improved with the surface roughness of LMO decreasing from 7.0 to 1.3nm. High-performance YBCO-coated conductors could be achieved if surface roughness of LMO cap layer is well controlled.展开更多
基金This work was supported by National Science Fund of China.
文摘It is suggested that the extremely large oxygen isotopic Tc shift recently reported in YBa2Cu3O7 may not be an intrinsic mass effect related to the mechanism but due to the small difference of the oxygen contents.
文摘The melting temperature and critical transition temperature Tc of YBa2Cu3O7-δ with deferent content additives of PbO and BaPbO3 were studied. When PbO was doped in YBa2Cu3O7-δ, the melting temperature of YBa2Cu3O7-δ was reduced, however its superconductivity was weakened. From the XRD pattern of the sintered mixture of YBa2Cu3O7-δ and PbO, it was known that there was a reaction between YBa2Cu3O7-δ and PbO, and the product was BaPbO3. Hence different contents of BaPbO3 (10mass%, 20mass% and 30mass%) were added in YBa2Cu3O7-δ. It was proved that there were no reactions between YBa2Cu3O7-δ and BaPbO3. And the superconductivity of the mixtures was much better than that of the samples with PbO additive.
基金financially supported by the National Science Foundation of China(No.91421110)the National High Technology Research and Development Program of China(No.2014AA032702)+2 种基金the National Basic Research Program of China(No.2015CB358600)Sichuan Youth Science and Technology Innovation Research Team Fund(No.2011JTD0006)Sichuan Provincial Fund for Distinguished Young Academic and Technology Leaders(No.2014JQ0011)
文摘LaMnO_(3)(LMO) cap layers with different surface roughness were prepared on epi-MgO/ion-beam-assisted deposition (IBAD) MgO/solution deposition planarized (SDP) Y<sub>2</sub>O<sub>3</sub>/Hastelloy tape. The effects of the surface roughness of LMO on the crystallization, texture and superconducting properties of Yba<sub>2</sub>Cu<sub>3</sub>O<sub>7?δ </sub> (YBCO) films were systematically investigated. The crystallization and epitaxial texture of resulting YBCO film are significantly improved with the surface roughness of LMO decreasing from 7.0 to 1.3nm. High-performance YBCO-coated conductors could be achieved if surface roughness of LMO cap layer is well controlled.