以Bi(NO3)3·5H2O、Na2WO4·2H2O、AgNO3为原料,利用液相沉淀法制备Bi2WO6及Ag掺杂Bi2WO6光催化剂,以亚甲基蓝溶液为目标降解物,对其降解效率进行研究。研究结果表明,当亚甲基蓝溶液的浓度为15 mg/L,体积为50 m L,降解时间3.5 h...以Bi(NO3)3·5H2O、Na2WO4·2H2O、AgNO3为原料,利用液相沉淀法制备Bi2WO6及Ag掺杂Bi2WO6光催化剂,以亚甲基蓝溶液为目标降解物,对其降解效率进行研究。研究结果表明,当亚甲基蓝溶液的浓度为15 mg/L,体积为50 m L,降解时间3.5 h,Bi2WO6降解率仅为55%;当Ag/Bi摩尔比为0.4%时,Ag/Bi2WO6表现出较好的催化性能,相同时间降解率达到97%。展开更多
Ag3PO4has good potential for use in photocatalytic degradation of organic contaminants.However,the activity and stability of Ag3PO4is hard to sustain because of photocorrosion and the positive potential of the conduct...Ag3PO4has good potential for use in photocatalytic degradation of organic contaminants.However,the activity and stability of Ag3PO4is hard to sustain because of photocorrosion and the positive potential of the conduction band of Ag3PO4.In this study,A composite consisting of Bi2WO6nanosheets and Ag3PO4was developed to curb recombination of charge carriers and enhance the activity and stability of the catalyst.Formation of a Ag3PO4/Bi2WO6composite was confirmed using X‐ray diffraction,energy‐dispersive X‐ray spectroscopy,and X‐ray photoelectron spectroscopy.Photoluminescence spectroscopy provided convincing evidence that compositing Bi2WO6with Ag3PO4effectively reduced photocorrosion of Ag3PO4.The Ag3PO4/Bi2WO6composite gave a high photocatalytic performance in photodegradation of methylene blue.A degradation rate of0.61min?1was achieved;this is1.3and6.0times higher than those achieved using Ag3PO4(0.47min?1)and Bi2WO6(0.10min?1),respectively.Reactive species trapping experiments using the Ag3PO4/Bi2WO6composite showed that holes,?OH,and?O2?all played specific roles in the photodegradation process.The photocatalytic mechanism was investigated and a Z‐scheme was proposed as a plausible mechanism.展开更多
文摘以Bi(NO3)3·5H2O、Na2WO4·2H2O、AgNO3为原料,利用液相沉淀法制备Bi2WO6及Ag掺杂Bi2WO6光催化剂,以亚甲基蓝溶液为目标降解物,对其降解效率进行研究。研究结果表明,当亚甲基蓝溶液的浓度为15 mg/L,体积为50 m L,降解时间3.5 h,Bi2WO6降解率仅为55%;当Ag/Bi摩尔比为0.4%时,Ag/Bi2WO6表现出较好的催化性能,相同时间降解率达到97%。
基金supported by the National Natural Science Foundation of China(20771010,20801052)National Key Basic Research Program of China(973)(2011CB932601)+1 种基金National High Technology Research and Development Program of China(863)(2007AA03Z311)"100 Talents Program of Chinese Academy of Sciences"(A1010)~~
基金supported by the National Natural Science Foundation of China(51572103,51502106)the Foundation for Young Talents in College of Anhui Province(gxyqZD201751)~~
文摘Ag3PO4has good potential for use in photocatalytic degradation of organic contaminants.However,the activity and stability of Ag3PO4is hard to sustain because of photocorrosion and the positive potential of the conduction band of Ag3PO4.In this study,A composite consisting of Bi2WO6nanosheets and Ag3PO4was developed to curb recombination of charge carriers and enhance the activity and stability of the catalyst.Formation of a Ag3PO4/Bi2WO6composite was confirmed using X‐ray diffraction,energy‐dispersive X‐ray spectroscopy,and X‐ray photoelectron spectroscopy.Photoluminescence spectroscopy provided convincing evidence that compositing Bi2WO6with Ag3PO4effectively reduced photocorrosion of Ag3PO4.The Ag3PO4/Bi2WO6composite gave a high photocatalytic performance in photodegradation of methylene blue.A degradation rate of0.61min?1was achieved;this is1.3and6.0times higher than those achieved using Ag3PO4(0.47min?1)and Bi2WO6(0.10min?1),respectively.Reactive species trapping experiments using the Ag3PO4/Bi2WO6composite showed that holes,?OH,and?O2?all played specific roles in the photodegradation process.The photocatalytic mechanism was investigated and a Z‐scheme was proposed as a plausible mechanism.