Poly（vinyl pyrrolidone）（PVP）/Fe 3O 4 composite nanofibers were successfully prepared by using electrospinning technique.The composite nanofibers were characterized by means of TEM（transmission electron microscopy...Poly（vinyl pyrrolidone）（PVP）/Fe 3O 4 composite nanofibers were successfully prepared by using electrospinning technique.The composite nanofibers were characterized by means of TEM（transmission electron microscopy）,XRD（X-ray diffraction）and TGA（thermogravimetric analysis）.Transmission electron microscope images of the PVP/Fe3O4 nanofibers show that the Fe3O4 nanoparticles with a diameter about 10.5 nm were dispersed in PVP fiber matrices.The XRD results show that the particles in PVP fibers were indeed Fe3O4 nanoparticles.And the TGA of PVP/Fe3O4 nanofibers show that the content of Fe3O4 nanoparticles in the composite was about 36.8%（mass fraction）.The PVP/Fe3O4 nanofibers were found to be superparamagnetic.The hysteresis loop at room temperature showed a high saturated magnetization（M s=15.1 emu/g）and a low coercive force（μ c=0）.展开更多
文摘Poly（vinyl pyrrolidone）（PVP）/Fe 3O 4 composite nanofibers were successfully prepared by using electrospinning technique.The composite nanofibers were characterized by means of TEM（transmission electron microscopy）,XRD（X-ray diffraction）and TGA（thermogravimetric analysis）.Transmission electron microscope images of the PVP/Fe3O4 nanofibers show that the Fe3O4 nanoparticles with a diameter about 10.5 nm were dispersed in PVP fiber matrices.The XRD results show that the particles in PVP fibers were indeed Fe3O4 nanoparticles.And the TGA of PVP/Fe3O4 nanofibers show that the content of Fe3O4 nanoparticles in the composite was about 36.8%（mass fraction）.The PVP/Fe3O4 nanofibers were found to be superparamagnetic.The hysteresis loop at room temperature showed a high saturated magnetization（M s=15.1 emu/g）and a low coercive force（μ c=0）.