This study researches the effect of V-Nb on the growth of austenite grains in 17CrNiMo6 carburized gear steel. Results show that the carbonitride in V and Nb acts as second-phase particles in the steel, which can be u...This study researches the effect of V-Nb on the growth of austenite grains in 17CrNiMo6 carburized gear steel. Results show that the carbonitride in V and Nb acts as second-phase particles in the steel, which can be used to block the migration of grain boundaries and the thinning of the austenite grains. This causes the crystals in the V-Nb microalloy 17CrNiMo6 steel to coarsen and the temperature to rise, thus reducing the cost of the carbonization that follows processing on the gears.展开更多
对9Cr 1Mo V Nb N钢厚壁无缝管研制品与进口住友P91钢管在供货状态下进行了比较研究,测试了两者的静力拉伸强塑性,分析了其间存在的差异.结果表明,研制品的强塑性与进口管相差尚少,但钢中杂质元素的控制与住友钢管有一定差距,质量均... 对9Cr 1Mo V Nb N钢厚壁无缝管研制品与进口住友P91钢管在供货状态下进行了比较研究,测试了两者的静力拉伸强塑性,分析了其间存在的差异.结果表明,研制品的强塑性与进口管相差尚少,但钢中杂质元素的控制与住友钢管有一定差距,质量均匀性有待提高.展开更多
对经1 055 ℃正火和765 ℃回火优化工艺生产的9Cr 1Mo V Nb N厚壁无缝钢管,进行室温和 566 ℃的静力强塑性的检测和评估,就取样位置和取样方向对强塑性的影响进行了 t统计检验评估及强塑性的标准偏差评估。结果表明,按优化工艺生产的9Cr...对经1 055 ℃正火和765 ℃回火优化工艺生产的9Cr 1Mo V Nb N厚壁无缝钢管,进行室温和 566 ℃的静力强塑性的检测和评估,就取样位置和取样方向对强塑性的影响进行了 t统计检验评估及强塑性的标准偏差评估。结果表明,按优化工艺生产的9Cr 1Mo V Nb N厚壁无缝钢管显著优于1 050 ℃正火和790 ℃回火原工艺生产的厚壁无缝钢管,强塑性指标及其标准偏差已达到进口P91厚壁无缝钢管的水平,表明我国9Cr 1Mo V Nb N厚壁无缝钢管的制造技术已日趋成熟。展开更多
The effect of W on mechanical properties of 12% Cr-W-V-Nb heat resistant steel at high temperatures and room temperature is reported.The experimental results indicated that if the W content was about 2.2—3.0 wt-%,the...The effect of W on mechanical properties of 12% Cr-W-V-Nb heat resistant steel at high temperatures and room temperature is reported.The experimental results indicated that if the W content was about 2.2—3.0 wt-%,there was no obviously change of R.T.tensile strength, but impact toughness decreased with the rise of W content.On the other hand,the increase of W content enhanced the short time stress rupture strength,but did not for the long time one. The increase of W have two effects on the precipitation behavior,promoting Laves formation of type Fe_2W,increasing the precipitated phase amount and speeding up the coarsening pro- cess of precipitated phase at high temperatures.The effect of W on the mechanical properties is closely associated with precipitation behaviors.When the rupture life is short,there has no enough time to coarsen the precipitated phases,so the increase of precipitated phases results in strengthening effect,i.e.the W increases the high temperature strength.After prolonged expo- sure,the evident coarsening took plaee,that decreased the effect of precipitation.展开更多
文摘This study researches the effect of V-Nb on the growth of austenite grains in 17CrNiMo6 carburized gear steel. Results show that the carbonitride in V and Nb acts as second-phase particles in the steel, which can be used to block the migration of grain boundaries and the thinning of the austenite grains. This causes the crystals in the V-Nb microalloy 17CrNiMo6 steel to coarsen and the temperature to rise, thus reducing the cost of the carbonization that follows processing on the gears.
文摘对经1 055 ℃正火和765 ℃回火优化工艺生产的9Cr 1Mo V Nb N厚壁无缝钢管,进行室温和 566 ℃的静力强塑性的检测和评估,就取样位置和取样方向对强塑性的影响进行了 t统计检验评估及强塑性的标准偏差评估。结果表明,按优化工艺生产的9Cr 1Mo V Nb N厚壁无缝钢管显著优于1 050 ℃正火和790 ℃回火原工艺生产的厚壁无缝钢管,强塑性指标及其标准偏差已达到进口P91厚壁无缝钢管的水平,表明我国9Cr 1Mo V Nb N厚壁无缝钢管的制造技术已日趋成熟。
文摘The effect of W on mechanical properties of 12% Cr-W-V-Nb heat resistant steel at high temperatures and room temperature is reported.The experimental results indicated that if the W content was about 2.2—3.0 wt-%,there was no obviously change of R.T.tensile strength, but impact toughness decreased with the rise of W content.On the other hand,the increase of W content enhanced the short time stress rupture strength,but did not for the long time one. The increase of W have two effects on the precipitation behavior,promoting Laves formation of type Fe_2W,increasing the precipitated phase amount and speeding up the coarsening pro- cess of precipitated phase at high temperatures.The effect of W on the mechanical properties is closely associated with precipitation behaviors.When the rupture life is short,there has no enough time to coarsen the precipitated phases,so the increase of precipitated phases results in strengthening effect,i.e.the W increases the high temperature strength.After prolonged expo- sure,the evident coarsening took plaee,that decreased the effect of precipitation.