TiO2/SiO2 aerogels with different molar ratio of SiO2/TiO2 were prepared via non-supercritical method using tetrabutyl titanate and silica sols as raw materials. The samples were characterized by TEM, SEM, BET, IR, XR...TiO2/SiO2 aerogels with different molar ratio of SiO2/TiO2 were prepared via non-supercritical method using tetrabutyl titanate and silica sols as raw materials. The samples were characterized by TEM, SEM, BET, IR, XRD and so on. The results indicate that the BET surface area of TiO2/SiO2 aerogels calcined at 550℃ which consisted of anatase structure of TiO2 with narrow distribution pores of 5-25 nm is as high as 357.89 m2·g-1. For the photocatalytic degradation of pyridine, the catalytic activities of TiO2/SiO2 aerogels are much higher than that of TiO2 powder. The photocatalytic activity of TiO2/SiO2 aerogels calcined at 800℃ is the optimum. The higher the content of SiO2, the higher the photocatalytic activity of TiO2/SiO2 aerogels. The cost for preparation of the aerogels is greatly reduced by using non-supercritical drying method, and the aerogels are hopefully applied in the treatment of industrial waste water such as coking effluent treatment.展开更多
采用溶胶–凝胶法在常压下经不同温度热处理制备了TiO2/SiO2复合气凝胶光催化剂,利用XRD、TGA和BET等手段对其微观结构进行表征,以甲基橙溶液光催化降解实验评价其光催化性能,研究了热处理温度对TiO2/SiO2复合气凝胶的微观结构及光催化...采用溶胶–凝胶法在常压下经不同温度热处理制备了TiO2/SiO2复合气凝胶光催化剂,利用XRD、TGA和BET等手段对其微观结构进行表征,以甲基橙溶液光催化降解实验评价其光催化性能,研究了热处理温度对TiO2/SiO2复合气凝胶的微观结构及光催化性能影响规律.结果表明:随着热处理温度升高,TiO2/SiO2复合气凝胶中锐钛矿结晶度升高,晶粒尺寸增大,比表面积减小,使TiO2/SiO2复合气凝胶对甲基橙溶液的光催化降解活性呈现先升后降的变化趋势.当热处理温度为700℃左右,紫外光照20 min TiO2/SiO2复合气凝胶对甲基橙溶液的降解率达到95.4%.展开更多
基金Supported by the National Natural Science Foundation of China (No. 20473057)Development Foundation of Science and Technology of Shanghai (No. 0352nm094).
文摘TiO2/SiO2 aerogels with different molar ratio of SiO2/TiO2 were prepared via non-supercritical method using tetrabutyl titanate and silica sols as raw materials. The samples were characterized by TEM, SEM, BET, IR, XRD and so on. The results indicate that the BET surface area of TiO2/SiO2 aerogels calcined at 550℃ which consisted of anatase structure of TiO2 with narrow distribution pores of 5-25 nm is as high as 357.89 m2·g-1. For the photocatalytic degradation of pyridine, the catalytic activities of TiO2/SiO2 aerogels are much higher than that of TiO2 powder. The photocatalytic activity of TiO2/SiO2 aerogels calcined at 800℃ is the optimum. The higher the content of SiO2, the higher the photocatalytic activity of TiO2/SiO2 aerogels. The cost for preparation of the aerogels is greatly reduced by using non-supercritical drying method, and the aerogels are hopefully applied in the treatment of industrial waste water such as coking effluent treatment.
文摘采用溶胶–凝胶法在常压下经不同温度热处理制备了TiO2/SiO2复合气凝胶光催化剂,利用XRD、TGA和BET等手段对其微观结构进行表征,以甲基橙溶液光催化降解实验评价其光催化性能,研究了热处理温度对TiO2/SiO2复合气凝胶的微观结构及光催化性能影响规律.结果表明:随着热处理温度升高,TiO2/SiO2复合气凝胶中锐钛矿结晶度升高,晶粒尺寸增大,比表面积减小,使TiO2/SiO2复合气凝胶对甲基橙溶液的光催化降解活性呈现先升后降的变化趋势.当热处理温度为700℃左右,紫外光照20 min TiO2/SiO2复合气凝胶对甲基橙溶液的降解率达到95.4%.