A spiral photoreactor system （SPS） was developed for the degradation of 4-tert-octylphenol （4-t-OP） in aqueous phase. 4-t-OP was previously considered as a endocrine disrupting compound frequently present in water...A spiral photoreactor system （SPS） was developed for the degradation of 4-tert-octylphenol （4-t-OP） in aqueous phase. 4-t-OP was previously considered as a endocrine disrupting compound frequently present in water. The direct photodegradation reaction caused by the SPS was found to accord with the characteristic of apparent first-order reaction with reaction rate constant k = 4.8 x 10-2 min-1. However, the direct photodegradation reaction could not make the 4-t-OP mineralized. The photodegradation efficiency increased from 88% to 91.2% in 45 min irradiation period after the internal surface of SPS was sintered with TiO2 thin film as catalyst. Catalyst concentration, number of catalyst coating layers and initial concentration of 4-t-OP were proven to be the factors affecting the photocatalytic degradation performance of the SPS on aqueous 4-t-OP. The degradation mechanism was investigated and the byproducts were analyzed using total organic carbon analyzer （TOC） and LC-MS. The possible chemical structures of the products were suggested. SPS with single layer of TiO2 prepared by sintering 13.6% of TiO2 precursor was proven to be more efficient than most of previous systems for removal of 4-t-OP from aqueous phase. 28.3% of the 4-t-OP was mineralized in 45 min according to the decreased amount of TOC value.展开更多
The initial stage of Ni-TiO2 composite system electrodeposition on glassy carbon electrode from an acidic solution of nickel sulfate was investigated using cyclic voltammetry （CV）, chronoamperometry （CA） and elect...The initial stage of Ni-TiO2 composite system electrodeposition on glassy carbon electrode from an acidic solution of nickel sulfate was investigated using cyclic voltammetry （CV）, chronoamperometry （CA） and electrochemical impedance spectroscopy （EIS）. Analysis of current density-time transients was performed using the nonlinear fitting procedure and electrochemical impedance spectroscopy was simulated by Z-view software. Besides, the surface morphology of Ni-TiO2 co-deposition at the initial stage was observed by scanning electron microscopy （SEM）. The results show that, in the case of low overpotential （-790 mV vs SCE）, the presence of TiO2 particles in the plating bath makes the nucleation relaxation time tm^x decreased clearly. Meanwhile, the electro-crystallization of Ni-TiO2 system follows a Scharifker-Hills （SH） progressive nucleation/growth mechanism. While in the case of higher overpotential, the presence of the TiO2 particles in solution makes the nucleation relaxation time tmax increased. At -850 mV （vs SCE）, the co-deposition of Ni-TiO2 system meets SH instantaneous nucleation/growth mechanism. The results of impedance spectra show that the appearance of the characteristic inductive loops represents the nucleation/growth of nickel and the presence of TiO2 particles reduces the charge transfer resistance of solution. The SEM observation confirms that TiO2 particles can be considered as favorable sites for nickel nucleating.展开更多
INVESTIGAORS recognized the role of finely divided insoluble solid particles in stabilizing oil-water emulsions in the 1920s. The work has been extensively done since the 1980s. Butthe studies only focused on particle...INVESTIGAORS recognized the role of finely divided insoluble solid particles in stabilizing oil-water emulsions in the 1920s. The work has been extensively done since the 1980s. Butthe studies only focused on particles with the parameter up to micrometer size rather than thoseof nanometer size. In this letter, emulsive properties, including the type, ability and mecha-展开更多
基金supported by the National Natural Science Foundation of China(No.20777012,21077027 40503011)the Research Fund for the Doctoral Program of Higher Education of China(No.200802460006)the Innovative Foundation of Fudan University
文摘A spiral photoreactor system （SPS） was developed for the degradation of 4-tert-octylphenol （4-t-OP） in aqueous phase. 4-t-OP was previously considered as a endocrine disrupting compound frequently present in water. The direct photodegradation reaction caused by the SPS was found to accord with the characteristic of apparent first-order reaction with reaction rate constant k = 4.8 x 10-2 min-1. However, the direct photodegradation reaction could not make the 4-t-OP mineralized. The photodegradation efficiency increased from 88% to 91.2% in 45 min irradiation period after the internal surface of SPS was sintered with TiO2 thin film as catalyst. Catalyst concentration, number of catalyst coating layers and initial concentration of 4-t-OP were proven to be the factors affecting the photocatalytic degradation performance of the SPS on aqueous 4-t-OP. The degradation mechanism was investigated and the byproducts were analyzed using total organic carbon analyzer （TOC） and LC-MS. The possible chemical structures of the products were suggested. SPS with single layer of TiO2 prepared by sintering 13.6% of TiO2 precursor was proven to be more efficient than most of previous systems for removal of 4-t-OP from aqueous phase. 28.3% of the 4-t-OP was mineralized in 45 min according to the decreased amount of TOC value.
基金Project(MKPT-04-106) supported by the Project of National Defense of China
文摘The initial stage of Ni-TiO2 composite system electrodeposition on glassy carbon electrode from an acidic solution of nickel sulfate was investigated using cyclic voltammetry （CV）, chronoamperometry （CA） and electrochemical impedance spectroscopy （EIS）. Analysis of current density-time transients was performed using the nonlinear fitting procedure and electrochemical impedance spectroscopy was simulated by Z-view software. Besides, the surface morphology of Ni-TiO2 co-deposition at the initial stage was observed by scanning electron microscopy （SEM）. The results show that, in the case of low overpotential （-790 mV vs SCE）, the presence of TiO2 particles in the plating bath makes the nucleation relaxation time tm^x decreased clearly. Meanwhile, the electro-crystallization of Ni-TiO2 system follows a Scharifker-Hills （SH） progressive nucleation/growth mechanism. While in the case of higher overpotential, the presence of the TiO2 particles in solution makes the nucleation relaxation time tmax increased. At -850 mV （vs SCE）, the co-deposition of Ni-TiO2 system meets SH instantaneous nucleation/growth mechanism. The results of impedance spectra show that the appearance of the characteristic inductive loops represents the nucleation/growth of nickel and the presence of TiO2 particles reduces the charge transfer resistance of solution. The SEM observation confirms that TiO2 particles can be considered as favorable sites for nickel nucleating.
文摘INVESTIGAORS recognized the role of finely divided insoluble solid particles in stabilizing oil-water emulsions in the 1920s. The work has been extensively done since the 1980s. Butthe studies only focused on particles with the parameter up to micrometer size rather than thoseof nanometer size. In this letter, emulsive properties, including the type, ability and mecha-