The microstructures and mechanical properties of Ti–47 at%Ni–3 at%Fe shape memory alloy wire under the condition of severe cold-drawing at room temperature and different postdeformation annealing processes were inte...The microstructures and mechanical properties of Ti–47 at%Ni–3 at%Fe shape memory alloy wire under the condition of severe cold-drawing at room temperature and different postdeformation annealing processes were intensively investigated using transmission electron microscope(TEM),X-ray diffraction(XRD),Vickers microhardness tester and electron tensile tester.It is indicated that the structure of the alloy evolves into a predominant amorphous structure with a trace of nanocrystalline B2 phase after the cold-drawing of 76%areal reduction.Postdeformation annealing process exerted significant influence on the microstructure and mechanical properties.Crystallization occurs when the cold-drawn wire was annealed at 300℃ for 30 min.The ultimate tensile strength and ductility as well as the superelasticity of the wire are improved significantly by cold-drawing plus postdeformation annealing.展开更多
基金supported by the National Natural Science Foundation of China (No. 50921003)Industry, Education and Research Projects of the China Aviation Industrial (No.cxy2012BH04)
文摘The microstructures and mechanical properties of Ti–47 at%Ni–3 at%Fe shape memory alloy wire under the condition of severe cold-drawing at room temperature and different postdeformation annealing processes were intensively investigated using transmission electron microscope(TEM),X-ray diffraction(XRD),Vickers microhardness tester and electron tensile tester.It is indicated that the structure of the alloy evolves into a predominant amorphous structure with a trace of nanocrystalline B2 phase after the cold-drawing of 76%areal reduction.Postdeformation annealing process exerted significant influence on the microstructure and mechanical properties.Crystallization occurs when the cold-drawn wire was annealed at 300℃ for 30 min.The ultimate tensile strength and ductility as well as the superelasticity of the wire are improved significantly by cold-drawing plus postdeformation annealing.