Service life of two different oxide anodes in phenolsulfonic acid (PSA) solution was investigated by accelerated electrolysis. The durability of Ti/IrO_2+Ta_2 O_5 anode increased by the addition of SnO_2 in the mixed...Service life of two different oxide anodes in phenolsulfonic acid (PSA) solution was investigated by accelerated electrolysis. The durability of Ti/IrO_2+Ta_2 O_5 anode increased by the addition of SnO_2 in the mixed oxides. The degradation mechanisms of Ti/IrO_2+ Ta_2 O_5 and Ti/IrO_2 +Ta_2 O_5 +SnO+2 anodes were different. It was shown from the observation of scanning electron microscopy (SEM) and the electrochcmical measurement that, the deactivation of Ti/IrO_2 + Ta_2 O_5 anode was due to the build-up of an organic film on surface. The growth of the covered film on surface was restricted by addition of SnO_2, which resulted in increasing of the service life of anodes. The over-potential for oxygen evolution on Ti/IrO_2 +Ta_2 O_5 electrode increased after doping SnO_2, and the intermediate products of PSA building-up on the surface was much more rapidly oxidized. Meanwhile, a certain part of the surface oxide deposit entered into the solution leading to loss of oxides, which resulted in degradation of Ti/IroO_2 + Ta_2 O_5 anode containing SnO_2 component.展开更多
The hysteresis loop changes of ferroelecric SrBi_2 Ta_2 O_9 (SBT) thin films(330nm) us the temperature of forming gas (5 percent hydrogen+95 percent nitrogen) annealing weremeasured when the annealing time was 1min an...The hysteresis loop changes of ferroelecric SrBi_2 Ta_2 O_9 (SBT) thin films(330nm) us the temperature of forming gas (5 percent hydrogen+95 percent nitrogen) annealing weremeasured when the annealing time was 1min and 10min. The selected annealing temperature was at 100deg C,200 deg C 250 deg C, 300 deg C, 350 deg C,400 deg C and 450 deg C, respectively. Our resultsshowed that the ferroelectric properties were easily destroyed and the leakage current changedabruptly when the SBT thin films were in their ferroelectric phase (<270 deg C). The space chargesat the grain boundary may take an important role' in absorption polarity molecular hydrogen when theSBT thin films were in the ferroelectric phase. The oxygen recovery experiments were also performedand investigated in this work.展开更多
文摘Service life of two different oxide anodes in phenolsulfonic acid (PSA) solution was investigated by accelerated electrolysis. The durability of Ti/IrO_2+Ta_2 O_5 anode increased by the addition of SnO_2 in the mixed oxides. The degradation mechanisms of Ti/IrO_2+ Ta_2 O_5 and Ti/IrO_2 +Ta_2 O_5 +SnO+2 anodes were different. It was shown from the observation of scanning electron microscopy (SEM) and the electrochcmical measurement that, the deactivation of Ti/IrO_2 + Ta_2 O_5 anode was due to the build-up of an organic film on surface. The growth of the covered film on surface was restricted by addition of SnO_2, which resulted in increasing of the service life of anodes. The over-potential for oxygen evolution on Ti/IrO_2 +Ta_2 O_5 electrode increased after doping SnO_2, and the intermediate products of PSA building-up on the surface was much more rapidly oxidized. Meanwhile, a certain part of the surface oxide deposit entered into the solution leading to loss of oxides, which resulted in degradation of Ti/IroO_2 + Ta_2 O_5 anode containing SnO_2 component.
基金This work sponsored by Motorola SPS Digital DNA Laboratories. It is also supported by a grant for State Key Program for Basic Research of China. We would like to thank Dr. Peir Y. Chu of Motorola SPS for his great help, useful advice and discussion.
文摘The hysteresis loop changes of ferroelecric SrBi_2 Ta_2 O_9 (SBT) thin films(330nm) us the temperature of forming gas (5 percent hydrogen+95 percent nitrogen) annealing weremeasured when the annealing time was 1min and 10min. The selected annealing temperature was at 100deg C,200 deg C 250 deg C, 300 deg C, 350 deg C,400 deg C and 450 deg C, respectively. Our resultsshowed that the ferroelectric properties were easily destroyed and the leakage current changedabruptly when the SBT thin films were in their ferroelectric phase (<270 deg C). The space chargesat the grain boundary may take an important role' in absorption polarity molecular hydrogen when theSBT thin films were in the ferroelectric phase. The oxygen recovery experiments were also performedand investigated in this work.