TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The ...TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The results show that the TA2 part of exhibiting near-equiaxed grains was Widmanst？tten α-laths microstructure. The TA15 part containing large columnar grains was fine basket-weave microstructure. The graded zone was divided into four deposited layers with 3000 μm in thickness. As the distance from the TA2 part increases, the alloy element contents and the β phase volume fraction increase, the α phase volume fraction decreases and the microstructure shows the evolution from Widmanst？tten α-laths to basket-weave α-laths gradually. The micro-hardness increases from the TA2 part to the TA15 part due to the solid solution strengthening and grain boundary strengthening.展开更多
The dynamic globularization kinetics of TA15（Ti-6Al-2Zr-1Mo-1V） titanium alloy with a colony α microstructure during deformation at temperature range of 860-940 ℃ and strain rate range of 0.01-10 s-1 was quantitat...The dynamic globularization kinetics of TA15（Ti-6Al-2Zr-1Mo-1V） titanium alloy with a colony α microstructure during deformation at temperature range of 860-940 ℃ and strain rate range of 0.01-10 s-1 was quantitatively studied through isothermal compression tests.It is found that the dynamic globularization kinetics and the kinetics rate of TA15 are sensitive to deformation parameters.The dynamic globularized fraction increases with increasing strain,temperature but decreasing strain rate.The variation of globularized fraction with strain approximately follows an Avrami type equation.Using the Avrami type equation,the initiation and completion strains for dynamic globularization of TA15 were predicted to be 0.34-0.59 and 3.40-6.80.The kinetics rate of dynamic globularization increases with strain at first,then decreases.The peak value of kinetics rate,which corresponds to 20%-33% globularization fraction,increases with increasing temperature and decreasing strain rate.展开更多
The effects of cooling rate on the mechanical properties and the fatigue crack growth behavior of TA15 ELI alloy plates with different microstructures were investigated at room temperature. The results indicate that t...The effects of cooling rate on the mechanical properties and the fatigue crack growth behavior of TA15 ELI alloy plates with different microstructures were investigated at room temperature. The results indicate that the cooling rate （water quench, air cooling, and furnace cooling） has a pronounced influence on the mechanical properties and on the fatigue crack growth, especially for air cooling and furnace cooling. Optical microstructure observation and scanning electron microscopy of tensile fracture surfaces were performed to gain an insight into the mechanism of properties. The dependence of mechanical properties and fatigue crack growth behavior on the cooling rate can be attributed to the oc lamellae width and the colony size, which induce the change in slip length. The microstmcture produced by air cooling shows the best damage tolerance behavior when compared with water quench and furnace cooling.展开更多
The microstructure, phase composition and cold shut defect of thick titanium alloy electron beam welded joint were studied. The results showed that the microstructure of weld zone was composed of α′ phase; the heat ...The microstructure, phase composition and cold shut defect of thick titanium alloy electron beam welded joint were studied. The results showed that the microstructure of weld zone was composed of α′ phase; the heat affected zone was divided into fine-grained zone and coarse-grained zone, the microstructure of fine-grained zone was primary α phase ＋ β phase ＋ equiaxed α phase, and the microstructure of coarse-grained zone was primary α phase ＋ acicular α′ phase; the microstructure of base metal zone basically consisted of primary α phase, and a small amount of residual β phase sprinkled. The forming. reason of cold shut was analyzed, and the precaution of cold shut was proposed.展开更多
Nanoindentation and high resolution electron backscatter diffraction（EBSD） were combined to examine the elastic modulus and hardness of α and β phases,anisotropy in residual elastic stress strain fields and distri...Nanoindentation and high resolution electron backscatter diffraction（EBSD） were combined to examine the elastic modulus and hardness of α and β phases,anisotropy in residual elastic stress strain fields and distributions of geometrically necessary dislocation（GND） density around the indentations within TA15 titanium alloy.The nano-indention tests were conducted on α and β phases,respectively.The residual stress strain fields surrounding the indentation were calculated through crosscorrelation method from recorded patterns.The GND density distribution around the indentation was calculated based on the strain gradient theories to reveal the micro-mechanism of plastic deformation.The results indicate that the elastic modulus and hardness for α p hase are 129.05 GPas and 6.44 GPa,while for β phase,their values are 109.80 GPa and 4.29 GPa,respectively.The residual Mises stress distribution around the indentation is relatively heterogeneous and significantly influenced by neighboring soft β phase.The region with low residual stress around the indentation is accompanied with markedly high a type and prismatic-GND density.展开更多
基金Project(2010CB731705)supported by the National Basic Research Program of China
文摘TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The results show that the TA2 part of exhibiting near-equiaxed grains was Widmanst？tten α-laths microstructure. The TA15 part containing large columnar grains was fine basket-weave microstructure. The graded zone was divided into four deposited layers with 3000 μm in thickness. As the distance from the TA2 part increases, the alloy element contents and the β phase volume fraction increase, the α phase volume fraction decreases and the microstructure shows the evolution from Widmanst？tten α-laths to basket-weave α-laths gradually. The micro-hardness increases from the TA2 part to the TA15 part due to the solid solution strengthening and grain boundary strengthening.
基金Project(50935007)supported by the National Natural Science Foundation of ChinaProject(2010CB731701)supported by the National Basic Research Program of China
文摘The dynamic globularization kinetics of TA15（Ti-6Al-2Zr-1Mo-1V） titanium alloy with a colony α microstructure during deformation at temperature range of 860-940 ℃ and strain rate range of 0.01-10 s-1 was quantitatively studied through isothermal compression tests.It is found that the dynamic globularization kinetics and the kinetics rate of TA15 are sensitive to deformation parameters.The dynamic globularized fraction increases with increasing strain,temperature but decreasing strain rate.The variation of globularized fraction with strain approximately follows an Avrami type equation.Using the Avrami type equation,the initiation and completion strains for dynamic globularization of TA15 were predicted to be 0.34-0.59 and 3.40-6.80.The kinetics rate of dynamic globularization increases with strain at first,then decreases.The peak value of kinetics rate,which corresponds to 20%-33% globularization fraction,increases with increasing temperature and decreasing strain rate.
文摘The effects of cooling rate on the mechanical properties and the fatigue crack growth behavior of TA15 ELI alloy plates with different microstructures were investigated at room temperature. The results indicate that the cooling rate （water quench, air cooling, and furnace cooling） has a pronounced influence on the mechanical properties and on the fatigue crack growth, especially for air cooling and furnace cooling. Optical microstructure observation and scanning electron microscopy of tensile fracture surfaces were performed to gain an insight into the mechanism of properties. The dependence of mechanical properties and fatigue crack growth behavior on the cooling rate can be attributed to the oc lamellae width and the colony size, which induce the change in slip length. The microstmcture produced by air cooling shows the best damage tolerance behavior when compared with water quench and furnace cooling.
基金Project (2010CB731704) supported by the National Basic Research Program of China
文摘The microstructure, phase composition and cold shut defect of thick titanium alloy electron beam welded joint were studied. The results showed that the microstructure of weld zone was composed of α′ phase; the heat affected zone was divided into fine-grained zone and coarse-grained zone, the microstructure of fine-grained zone was primary α phase ＋ β phase ＋ equiaxed α phase, and the microstructure of coarse-grained zone was primary α phase ＋ acicular α′ phase; the microstructure of base metal zone basically consisted of primary α phase, and a small amount of residual β phase sprinkled. The forming. reason of cold shut was analyzed, and the precaution of cold shut was proposed.
文摘Nanoindentation and high resolution electron backscatter diffraction（EBSD） were combined to examine the elastic modulus and hardness of α and β phases,anisotropy in residual elastic stress strain fields and distributions of geometrically necessary dislocation（GND） density around the indentations within TA15 titanium alloy.The nano-indention tests were conducted on α and β phases,respectively.The residual stress strain fields surrounding the indentation were calculated through crosscorrelation method from recorded patterns.The GND density distribution around the indentation was calculated based on the strain gradient theories to reveal the micro-mechanism of plastic deformation.The results indicate that the elastic modulus and hardness for α p hase are 129.05 GPas and 6.44 GPa,while for β phase,their values are 109.80 GPa and 4.29 GPa,respectively.The residual Mises stress distribution around the indentation is relatively heterogeneous and significantly influenced by neighboring soft β phase.The region with low residual stress around the indentation is accompanied with markedly high a type and prismatic-GND density.