In order to investigate the ratcheting behavior of T225NG alloy, a series of ratcheting tests under uniaxial long-cyclic stressing were performed. The results show that the ratcheting strain of this alloy can get into...In order to investigate the ratcheting behavior of T225NG alloy, a series of ratcheting tests under uniaxial long-cyclic stressing were performed. The results show that the ratcheting strain of this alloy can get into shakedown after tens （or hundreds） of thousand cycles. After the ratcheting strain is saturated under the condition that stress amplitude is half of peak stress, it will bring about subsequent fatigue failure, and relationship between fatigue life and one of peak stress and saturated ratcheting （SR） strain meets power law. As the alloy is under stress jiggling with stress amplitude that is 1%-2.5% of peak stress, the ratcheting strain still become remarkable and goes into shakedown after several hundreds of thousand cycles but there exists little accessional strain caused by creep effect. It is notable that, when the peak stress is 85%-100% of yield stress, the long-cyclic stressing will lead SR strain to be from 1.4% to 2.5% even if the initial ratio of ratcheting strain is zero. Based on ratcheting threshold property of peak stress and monotonicity of relationship between the peak stress and SR strain, a saturated ratcheting model （SRM） is developed to predict SR strain and to estimate saturated creep strain also. In addition, the classes of ratcheting evolutions of metals are discussed.展开更多
文摘In order to investigate the ratcheting behavior of T225NG alloy, a series of ratcheting tests under uniaxial long-cyclic stressing were performed. The results show that the ratcheting strain of this alloy can get into shakedown after tens （or hundreds） of thousand cycles. After the ratcheting strain is saturated under the condition that stress amplitude is half of peak stress, it will bring about subsequent fatigue failure, and relationship between fatigue life and one of peak stress and saturated ratcheting （SR） strain meets power law. As the alloy is under stress jiggling with stress amplitude that is 1%-2.5% of peak stress, the ratcheting strain still become remarkable and goes into shakedown after several hundreds of thousand cycles but there exists little accessional strain caused by creep effect. It is notable that, when the peak stress is 85%-100% of yield stress, the long-cyclic stressing will lead SR strain to be from 1.4% to 2.5% even if the initial ratio of ratcheting strain is zero. Based on ratcheting threshold property of peak stress and monotonicity of relationship between the peak stress and SR strain, a saturated ratcheting model （SRM） is developed to predict SR strain and to estimate saturated creep strain also. In addition, the classes of ratcheting evolutions of metals are discussed.