The pozzolanic activity of coal gangue burned at different burning temperatures was investigated. The burned coal gangue was mixed with portland cement in different proportions （ 20% - 60% ）. The pozzolanic activity...The pozzolanic activity of coal gangue burned at different burning temperatures was investigated. The burned coal gangue was mixed with portland cement in different proportions （ 20% - 60% ）. The pozzolanic activity of coal gangue burned and the hydration products were examined, the compressive strengths of the pastes of the mixtures were tested, and the mechanism of the reaction was discussed. The experimental results slum, that the coal gangue burned at 750 ℃ has the optimum pozzolanic activity, and the burned coal ganguc with SiO2 and Al2 O3 is in an active form. When the coal gangue burned at 750℃ is mixed into portland cement, the content of calcium hydroxide in paste is significantly reduced, while the contents of hydrated calcium silk.ate and hydrated calcium aluminate are increased accordingly, hence resulting in the improvement of the microstructure of mortar. The compressive strength of cement paste decreases with increasing the content of burncd coal gangue. The decease in strength is small in the range of 20% - 30% coal gangue substitution and significant in 30%- 60% substitution.展开更多
The compressive strength developing process and the microstructure of cement-asphalt mortar （CA mortar） were investigated.The fluidity of CA mortar has a great influence on its strength.The optimum value of spread d...The compressive strength developing process and the microstructure of cement-asphalt mortar （CA mortar） were investigated.The fluidity of CA mortar has a great influence on its strength.The optimum value of spread diameter of slump flow test is in the range of 300 to 400 mm.The compressive strength of CA mortar keeps a relatively high growth rate in 56 days and grows slowly afterwards.The residual water of hydration in CA mortar freezes under minus environmental temperature which can lead to a significant reduction of the strength of CA mortar.Increasing A/C retards asphalt emulsion splitting and thus prolongs the setting process of CA mortar.The hydration products of cement form the major structural framework of hardened CA mortar and asphalt is a weak phase in the framework but improves the viscoelastic behavior of CA mortar.Therefore,asphalt emulsion should be used as much as possible on the condition that essential performance criterions of CA mortar are satisfied.展开更多
The mining process involves drilling and excavation, resulting in the production of waste rock and tailings. The waste materials are then removed and stored in designated areas. This study aims to evaluate the mechani...The mining process involves drilling and excavation, resulting in the production of waste rock and tailings. The waste materials are then removed and stored in designated areas. This study aims to evaluate the mechanical strength and the environmental and economic impact of using Coltan Mining Waste (CMW) as a substitute for aggregates in concrete and mortar production. To achieve this, the CMW needs to be characterised. The Dreux Gorisse method was primarily used to produce concrete with a strength of 20 MPa at 28 days. The mortars, on the other hand, were formulated according to the NF P 18-452 standard. The environmental impact of using CMW as substitutes for natural aggregates in the production of concrete and mortar was analysed using SimaPro software. The results showed that mortars and concrete made with CMW have comparable compressive strengths to the reference mortar and concrete;reduce the negative impact on ecosystem quality, human health, resources, and climate change. It has also been shown that the substitution of aggregates by CMW reduces the cost of concrete and mortar as a function of the distance from the aggregate footprint.展开更多
The constant need for high-strength materials in the construction industry promotes the research of additives that improve the properties of masonry materials. The use of allophane as an additive in concrete and morta...The constant need for high-strength materials in the construction industry promotes the research of additives that improve the properties of masonry materials. The use of allophane as an additive in concrete and mortar mixtures was implemented to improve their strength and waterproofing, respectively, using compression and water absorption tests according to their corresponding standards (ASTM C1231, ASTM D2938, and ASTM C1585). The samples were evaluated at different concentrations and curing ages. In addition, different sand/cement ratios were considered for the mortar. The results revealed that there was a 9.4% increase in compressive strength in concrete and a 23.7% reduction in water absorption in mortar for the 5:1 ratio. These changes would be the result of the interaction of the nanoporous additive in the atomic crystal structure of the material demonstrating the nanotechnological nature of allophane.展开更多
This work is part of an experimental contribution approach to the study of the incorporation of glass sand from the grinding of recycled glass waste in cement mortars and its influence on the physical and mechanical b...This work is part of an experimental contribution approach to the study of the incorporation of glass sand from the grinding of recycled glass waste in cement mortars and its influence on the physical and mechanical behavior of semi-rich mortars without adjuvants. For this purpose, after a physical characterization of the sands, eight (08) formulations of mortars based on cement CEM II B/L 32.5R and fine sands (0/2) of glass at mass contents of 0%, 10%, 20%, 30%, 40%, 50%, 75% and 100% of the silty sand (0/2) were made respectively to three (03) types of fine glass sand (white, brown, green) with water dosages on cement (W/C) of 0.50, 0.45, 0.40. The results obtained show that the fine sands of recycled glass have a higher water absorption than the silty sand and the physical properties of the mortars prepared are affected by the increase in the glass content. The mechanical performances are obtained for the ratio W/C = 0.50 and the formulation of glass mortars for an optimal compressive strength superior to glass-free mortar requires a substitution of 10% for fine white glass sand, 20% for sand fine green glass and 75% for fine brown glass sand. The comparative study between these different compositions of fine glass sand mortars shows that the mechanical performances of fine brown glass sand are better than other glass sands but generally remain inferior to the control mortar based on natural silty sand.展开更多
基金Funded by Social Development Plan in Science and Technologyof Jiangsu Province (No.BS2006033)
文摘The pozzolanic activity of coal gangue burned at different burning temperatures was investigated. The burned coal gangue was mixed with portland cement in different proportions （ 20% - 60% ）. The pozzolanic activity of coal gangue burned and the hydration products were examined, the compressive strengths of the pastes of the mixtures were tested, and the mechanism of the reaction was discussed. The experimental results slum, that the coal gangue burned at 750 ℃ has the optimum pozzolanic activity, and the burned coal ganguc with SiO2 and Al2 O3 is in an active form. When the coal gangue burned at 750℃ is mixed into portland cement, the content of calcium hydroxide in paste is significantly reduced, while the contents of hydrated calcium silk.ate and hydrated calcium aluminate are increased accordingly, hence resulting in the improvement of the microstructure of mortar. The compressive strength of cement paste decreases with increasing the content of burncd coal gangue. The decease in strength is small in the range of 20% - 30% coal gangue substitution and significant in 30%- 60% substitution.
基金Funded by National Natural Science Foundation of China (No.50802050)the Key Research and Development Program of Chinese Ministry of Railway (No.2008G031-18-6)
文摘The compressive strength developing process and the microstructure of cement-asphalt mortar （CA mortar） were investigated.The fluidity of CA mortar has a great influence on its strength.The optimum value of spread diameter of slump flow test is in the range of 300 to 400 mm.The compressive strength of CA mortar keeps a relatively high growth rate in 56 days and grows slowly afterwards.The residual water of hydration in CA mortar freezes under minus environmental temperature which can lead to a significant reduction of the strength of CA mortar.Increasing A/C retards asphalt emulsion splitting and thus prolongs the setting process of CA mortar.The hydration products of cement form the major structural framework of hardened CA mortar and asphalt is a weak phase in the framework but improves the viscoelastic behavior of CA mortar.Therefore,asphalt emulsion should be used as much as possible on the condition that essential performance criterions of CA mortar are satisfied.
文摘The mining process involves drilling and excavation, resulting in the production of waste rock and tailings. The waste materials are then removed and stored in designated areas. This study aims to evaluate the mechanical strength and the environmental and economic impact of using Coltan Mining Waste (CMW) as a substitute for aggregates in concrete and mortar production. To achieve this, the CMW needs to be characterised. The Dreux Gorisse method was primarily used to produce concrete with a strength of 20 MPa at 28 days. The mortars, on the other hand, were formulated according to the NF P 18-452 standard. The environmental impact of using CMW as substitutes for natural aggregates in the production of concrete and mortar was analysed using SimaPro software. The results showed that mortars and concrete made with CMW have comparable compressive strengths to the reference mortar and concrete;reduce the negative impact on ecosystem quality, human health, resources, and climate change. It has also been shown that the substitution of aggregates by CMW reduces the cost of concrete and mortar as a function of the distance from the aggregate footprint.
文摘The constant need for high-strength materials in the construction industry promotes the research of additives that improve the properties of masonry materials. The use of allophane as an additive in concrete and mortar mixtures was implemented to improve their strength and waterproofing, respectively, using compression and water absorption tests according to their corresponding standards (ASTM C1231, ASTM D2938, and ASTM C1585). The samples were evaluated at different concentrations and curing ages. In addition, different sand/cement ratios were considered for the mortar. The results revealed that there was a 9.4% increase in compressive strength in concrete and a 23.7% reduction in water absorption in mortar for the 5:1 ratio. These changes would be the result of the interaction of the nanoporous additive in the atomic crystal structure of the material demonstrating the nanotechnological nature of allophane.
文摘This work is part of an experimental contribution approach to the study of the incorporation of glass sand from the grinding of recycled glass waste in cement mortars and its influence on the physical and mechanical behavior of semi-rich mortars without adjuvants. For this purpose, after a physical characterization of the sands, eight (08) formulations of mortars based on cement CEM II B/L 32.5R and fine sands (0/2) of glass at mass contents of 0%, 10%, 20%, 30%, 40%, 50%, 75% and 100% of the silty sand (0/2) were made respectively to three (03) types of fine glass sand (white, brown, green) with water dosages on cement (W/C) of 0.50, 0.45, 0.40. The results obtained show that the fine sands of recycled glass have a higher water absorption than the silty sand and the physical properties of the mortars prepared are affected by the increase in the glass content. The mechanical performances are obtained for the ratio W/C = 0.50 and the formulation of glass mortars for an optimal compressive strength superior to glass-free mortar requires a substitution of 10% for fine white glass sand, 20% for sand fine green glass and 75% for fine brown glass sand. The comparative study between these different compositions of fine glass sand mortars shows that the mechanical performances of fine brown glass sand are better than other glass sands but generally remain inferior to the control mortar based on natural silty sand.