The magnetic field provided by magnetized SrFe_(12)O_(19)particles in FeSi/SrFe_(12)O_(19)composites is used to replace the applied transverse magnetic field,which successfully reduces the magnetic loss of the composi...The magnetic field provided by magnetized SrFe_(12)O_(19)particles in FeSi/SrFe_(12)O_(19)composites is used to replace the applied transverse magnetic field,which successfully reduces the magnetic loss of the composites with minor reduction of permeability.This magnetic loss reduction mainly comes from the decrease in hysteresis loss,while the eddy current loss is basically unaffected.The hysteresis loss reduction in magnetized composites is believed to be due to the decrease in domain wall displacement caused by the increase in the average magnetic domain size in a DC magnetic field.This is an effective method for reducing the magnetic loss of soft magnetic composites with wide application potential,and there is no problem of increasing the cost and the volume of the magnetic cores.展开更多
Exchange coupling interaction in sintered magnetic materials is generally isotropic.In this study,the anisotropic exchange coupling interaction was found in sintered oblate cylindrical SrFe_(12)O_(19)(SrM)specimens ob...Exchange coupling interaction in sintered magnetic materials is generally isotropic.In this study,the anisotropic exchange coupling interaction was found in sintered oblate cylindrical SrFe_(12)O_(19)(SrM)specimens obtained by the SrM nanopowders synthesized via a hydrothermal method.According to Henkel plots,the exchange coupling interaction between hard-hard magnetic grains was found in both as-pressed and sintered specimens.However,the exchange coupling interaction can only be found in the in-plane direction but not in the out-of-plane direction for thel sintered specimens.By building a model of a grain configuration,this anisotropy of the exchange coupling interaction was ascribed to the vertically arranged plate-like SrM grains with micrometers in width but nanometers in thickness,which was confirmed by morphologies of cross sections in fractured specimens.展开更多
The La-Co substituted Sr1–xLaxFe12–xCoxO19 (x=0–0.5) ferrites with appropriate Bi2O3 additive were prepared by conventional sintering method and microwave sintering method at low sintering temperatures compatible w...The La-Co substituted Sr1–xLaxFe12–xCoxO19 (x=0–0.5) ferrites with appropriate Bi2O3 additive were prepared by conventional sintering method and microwave sintering method at low sintering temperatures compatible with LTCC (low temperature co-fired ceramics) systems, and their sintering behavior was chiefly investigated, including the crystal structure, saturation magnetizationMs, magnetic anisotropy fieldHa, intrinsic coercivityHci, and Curie temperatureTC. Experiment results clearly showed that the pure M-type crystal phase was successfully obtained when the La-Co substitution amountx did not exceed 0.3. However, the single M-type phase structure transformed to multiphase structure with further increased x, where the M-type phase coexisted with the non-magnetic phase such asα-Fe2O3 phase, La2O3 phase, and LaCoO3 phase. Appropriate La-Co substitution improved theMs (>62 emu/g),Ha (>1400 kA/m), andHci (>320 kA/m) for the ferrites withx varying from 0.1 to 0.3, but theTC decreased with increasing substitution amount. More-over, the microwave sintered ferrites could provide largerHci and similarMs compared with the conventional sintered ferrites.展开更多
The dried gel of SrFe12O19, prepared by citrate approach, was investigated by means of infrared spectroscopy （ IR ）, thermogravimetric analysis （ TG ）, differential scanning calorimetry （ DSC ）, X- ray diffract...The dried gel of SrFe12O19, prepared by citrate approach, was investigated by means of infrared spectroscopy （ IR ）, thermogravimetric analysis （ TG ）, differential scanning calorimetry （ DSC ）, X- ray diffraction（ XRD ） techniques, energy dispersive spectroscopy（ EDS ）, and transmission electron microscopy（ TEM ）. The thermal instability and the thermal decomposition of low-temperature strontium M-type hexaferrite crystallized at about 600℃ were confirmed for the first time by XRD method. The decomposition of the low-temperature strontium M-type hexaferrite took place at about 688.6℃ determined by DSC investigation. The low-temperature strontium M-type hexaferrite nanopartieles were decomposed into SrFeO2.5 with an orthorthombic cell and Fe2O3 with a tetragonal cell as well as possibl α-Fe2O3 . The agglomerated particles with sizes less than 200 nm obtained at 800℃ were plesiomorphous to strontium M-type hexaferrite. The thermally stable strontium M-type hexaferrite nanopartieles with sizes less than 100um cotdd take place at 900 ℃ . Up to 1000 ℃ , the phose transformotion to form strontium M-type hexaferrite was ended, the calcinations with the sizes more than 1μm were composed of α-Fe2O3 and strontium M-type hexaferrite. The method of distinguishing γ-Fe2O3 with a spinel structure from Fe2O3 with tetragonal cells by using powder XRD method was proposed. Fe2O3 with tetragonal cells to be crystallized before the crystallization of thermally stable strontium M-type hexaferrite was confirmed for the first time. The reason why α- Fe2O3 as an additional phase appears in the calcinations is the cationic vacancy of stroutium M-type hexaferrite , SrFe12-x□O19 （0≤x ≤0.5）.展开更多
The SrFe12O19@carbonyl iron(CI) core–shell composites used in microwave absorption are prepared by the metal–organic chemical vapor deposition(MOCVD). The x-ray diffractometer, scanning electron microscope, energy d...The SrFe12O19@carbonyl iron(CI) core–shell composites used in microwave absorption are prepared by the metal–organic chemical vapor deposition(MOCVD). The x-ray diffractometer, scanning electron microscope, energy dispersive spectrometer, and vector network analyzer are used to characterize the structural, electromagnetic, and absorption properties of the composites. The results show that the SrFe12O19@CI composites with a core–shell structure could be successfully prepared under the condition: deposition temperatures above 180℃, deposition time 30 min, and gas flow rate 30 m L/min.The electromagnetic properties of the composites change significantly, and their absorption capacities are improved. Of the obtained samples, those samples prepared at a deposition temperature of 180℃ exhibit the best absorption performance.The reflection loss of SrFe12O19@CI(180℃) with 1.5 mm–2.5 mm in thickness is less than-10 dB in a frequency range of 8 GHz–18 GHz, which covers the whole X band and Ku band.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.51872004 and 51802002)the Key Program of the Education Department of Anhui Province,China(Grant No.KJ2019ZD03)the Science Foundation of the National Key Laboratory of Science and Technology on Advanced Composites in Specials Environments(Grant No.6142905202112)。
文摘The magnetic field provided by magnetized SrFe_(12)O_(19)particles in FeSi/SrFe_(12)O_(19)composites is used to replace the applied transverse magnetic field,which successfully reduces the magnetic loss of the composites with minor reduction of permeability.This magnetic loss reduction mainly comes from the decrease in hysteresis loss,while the eddy current loss is basically unaffected.The hysteresis loss reduction in magnetized composites is believed to be due to the decrease in domain wall displacement caused by the increase in the average magnetic domain size in a DC magnetic field.This is an effective method for reducing the magnetic loss of soft magnetic composites with wide application potential,and there is no problem of increasing the cost and the volume of the magnetic cores.
基金supported by the National Natural Science Foundation of China(Grant No.51772004).
文摘Exchange coupling interaction in sintered magnetic materials is generally isotropic.In this study,the anisotropic exchange coupling interaction was found in sintered oblate cylindrical SrFe_(12)O_(19)(SrM)specimens obtained by the SrM nanopowders synthesized via a hydrothermal method.According to Henkel plots,the exchange coupling interaction between hard-hard magnetic grains was found in both as-pressed and sintered specimens.However,the exchange coupling interaction can only be found in the in-plane direction but not in the out-of-plane direction for thel sintered specimens.By building a model of a grain configuration,this anisotropy of the exchange coupling interaction was ascribed to the vertically arranged plate-like SrM grains with micrometers in width but nanometers in thickness,which was confirmed by morphologies of cross sections in fractured specimens.
基金supported by the National Public Welfare Fund Industry Research(201410026)Scientific Research Foundation of Education Office of Sichuan Province(13Z198)the Young and Middle-aged Academic Leaders of Scientific Research Funds of Chengdu University of Information Technology(J201222)
文摘The La-Co substituted Sr1–xLaxFe12–xCoxO19 (x=0–0.5) ferrites with appropriate Bi2O3 additive were prepared by conventional sintering method and microwave sintering method at low sintering temperatures compatible with LTCC (low temperature co-fired ceramics) systems, and their sintering behavior was chiefly investigated, including the crystal structure, saturation magnetizationMs, magnetic anisotropy fieldHa, intrinsic coercivityHci, and Curie temperatureTC. Experiment results clearly showed that the pure M-type crystal phase was successfully obtained when the La-Co substitution amountx did not exceed 0.3. However, the single M-type phase structure transformed to multiphase structure with further increased x, where the M-type phase coexisted with the non-magnetic phase such asα-Fe2O3 phase, La2O3 phase, and LaCoO3 phase. Appropriate La-Co substitution improved theMs (>62 emu/g),Ha (>1400 kA/m), andHci (>320 kA/m) for the ferrites withx varying from 0.1 to 0.3, but theTC decreased with increasing substitution amount. More-over, the microwave sintered ferrites could provide largerHci and similarMs compared with the conventional sintered ferrites.
文摘The dried gel of SrFe12O19, prepared by citrate approach, was investigated by means of infrared spectroscopy （ IR ）, thermogravimetric analysis （ TG ）, differential scanning calorimetry （ DSC ）, X- ray diffraction（ XRD ） techniques, energy dispersive spectroscopy（ EDS ）, and transmission electron microscopy（ TEM ）. The thermal instability and the thermal decomposition of low-temperature strontium M-type hexaferrite crystallized at about 600℃ were confirmed for the first time by XRD method. The decomposition of the low-temperature strontium M-type hexaferrite took place at about 688.6℃ determined by DSC investigation. The low-temperature strontium M-type hexaferrite nanopartieles were decomposed into SrFeO2.5 with an orthorthombic cell and Fe2O3 with a tetragonal cell as well as possibl α-Fe2O3 . The agglomerated particles with sizes less than 200 nm obtained at 800℃ were plesiomorphous to strontium M-type hexaferrite. The thermally stable strontium M-type hexaferrite nanopartieles with sizes less than 100um cotdd take place at 900 ℃ . Up to 1000 ℃ , the phose transformotion to form strontium M-type hexaferrite was ended, the calcinations with the sizes more than 1μm were composed of α-Fe2O3 and strontium M-type hexaferrite. The method of distinguishing γ-Fe2O3 with a spinel structure from Fe2O3 with tetragonal cells by using powder XRD method was proposed. Fe2O3 with tetragonal cells to be crystallized before the crystallization of thermally stable strontium M-type hexaferrite was confirmed for the first time. The reason why α- Fe2O3 as an additional phase appears in the calcinations is the cationic vacancy of stroutium M-type hexaferrite , SrFe12-x□O19 （0≤x ≤0.5）.
文摘The SrFe12O19@carbonyl iron(CI) core–shell composites used in microwave absorption are prepared by the metal–organic chemical vapor deposition(MOCVD). The x-ray diffractometer, scanning electron microscope, energy dispersive spectrometer, and vector network analyzer are used to characterize the structural, electromagnetic, and absorption properties of the composites. The results show that the SrFe12O19@CI composites with a core–shell structure could be successfully prepared under the condition: deposition temperatures above 180℃, deposition time 30 min, and gas flow rate 30 m L/min.The electromagnetic properties of the composites change significantly, and their absorption capacities are improved. Of the obtained samples, those samples prepared at a deposition temperature of 180℃ exhibit the best absorption performance.The reflection loss of SrFe12O19@CI(180℃) with 1.5 mm–2.5 mm in thickness is less than-10 dB in a frequency range of 8 GHz–18 GHz, which covers the whole X band and Ku band.