Novel red-emitting phosphors Sr2MgSi2O7：Eu3＋ were prepared by gel-combustion method assisted by microwave. The phase struc-ture and luminescent properties of as-synthesized phosphors were investigated by XRD and flu...Novel red-emitting phosphors Sr2MgSi2O7：Eu3＋ were prepared by gel-combustion method assisted by microwave. The phase struc-ture and luminescent properties of as-synthesized phosphors were investigated by XRD and fluorescence spectrophotometer, respectively. The results showed that the as-synthesized sample was Sr2MgSi2O7 with tetragonal crystal structure. The excitation spectrum of Sr2MgSi2O7：Eu3＋ was composed of two major parts： one was the broad band between 200 and 350 nm, which belonged to the charge transfer of Eu3＋-O2-; the other consisted of a series of sharp lines between 350 and 450 nm, ascribed to the f-f transition of Eu3＋. The emission spec-trum consisted of two emission peaks at 593 and 616 nm, which was attributed to 5D0→7F1 and 5D0→7F2 of Eu3＋, respectively. The concen-tration of Eu3＋ （x） had great effect on the emission intensity of Sr2-xMgSi2O7：Eu3＋x. When x varied in the range of 0.04-0.18, the intensity of emission peaks at 593 and 616 nm increased gradually with the concentration of Eu3＋ increasing. It was interesting that no concentration quenching occurred. Moreover, the luminescent intensity could be greatly enhanced with incorporation of charge compensator Li＋ ions.展开更多
采用溶胶-凝胶法将TiO2-x N x包覆在长余辉光致发光材料(Sr2MgSi2O7∶Eu2+,Dy3+)表面制备得到TiO2-x N x/Sr2MgSi2O7∶Eu2+,Dy3+复合材料。利用X-射线衍射(XRD)、扫描电子显微镜(SEM)对TiO2-x N x/Sr2MgSi2O7∶Eu2+,Dy3+复合光催化材料...采用溶胶-凝胶法将TiO2-x N x包覆在长余辉光致发光材料(Sr2MgSi2O7∶Eu2+,Dy3+)表面制备得到TiO2-x N x/Sr2MgSi2O7∶Eu2+,Dy3+复合材料。利用X-射线衍射(XRD)、扫描电子显微镜(SEM)对TiO2-x N x/Sr2MgSi2O7∶Eu2+,Dy3+复合光催化材料的结构及表面形貌进行表征,并研究了TiO2-x N x/Sr2MgSi2O7∶Eu2+,Dy3+复合光催化材料对甲基橙溶液的降解性能。展开更多
A novel method for synthesizing long afterglow silicate phosphor Sr3MgSi2O8：Eu^2＋,Dy^3＋using TEOS and inorganic powders as reactants was reported. Acetic acid as a catalyzer controlled the hydrolysis of TEOS by adj...A novel method for synthesizing long afterglow silicate phosphor Sr3MgSi2O8：Eu^2＋,Dy^3＋using TEOS and inorganic powders as reactants was reported. Acetic acid as a catalyzer controlled the hydrolysis of TEOS by adjusting pH value of the system. The morphologies of precursor were characterized by transmission electron microscope （TEM）. The structure and optical properties of the phosphor powders were systematically investigated by means of X-ray diffraction and spectrofluorometry. TEM images have reflected the core-shell structure and quasi-spherical morphology of the precursor particles. It was found that the single-phase Sr3MgSi2O8 crystalline structures were obtained at 1050 and 1250 ℃ for the samples prepared with the nano-coating method and the solid state reaction, respectively. The emission intensities of the phosphors prepared by the present method were higher than those by the conventional process. Also, the afterglow characteristic was better than that prepared by solid-state reaction in the comparable condition.展开更多
To discuss the function of Eu and Dy and their interaction in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ long afterglow material,the Eu and Dy single doped and their co-doped Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ were prepared.The samples wer...To discuss the function of Eu and Dy and their interaction in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ long afterglow material,the Eu and Dy single doped and their co-doped Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ were prepared.The samples were characterized by X-ray diffraction（XRD）,decay curves,photoluminescence（PL）,and thermoluminescence（TL）.The results indicate that Sr2 Mg Si2O7：Eu has afterglow properties,and the doping of Eu ion in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ can lower the depth of traps.Eu ion can not only serve as luminescence center,but also produce traps in the matrix,meanwhile,it also exerts certain influences on the traps produced by Dy in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋.The Dy ion can not act as luminescence center but relates to the change of the traps in the Sr2 Mg Si2O7 matrix.展开更多
基金Project supported by the National Natural Science Foundation of China (20675023)
文摘Novel red-emitting phosphors Sr2MgSi2O7：Eu3＋ were prepared by gel-combustion method assisted by microwave. The phase struc-ture and luminescent properties of as-synthesized phosphors were investigated by XRD and fluorescence spectrophotometer, respectively. The results showed that the as-synthesized sample was Sr2MgSi2O7 with tetragonal crystal structure. The excitation spectrum of Sr2MgSi2O7：Eu3＋ was composed of two major parts： one was the broad band between 200 and 350 nm, which belonged to the charge transfer of Eu3＋-O2-; the other consisted of a series of sharp lines between 350 and 450 nm, ascribed to the f-f transition of Eu3＋. The emission spec-trum consisted of two emission peaks at 593 and 616 nm, which was attributed to 5D0→7F1 and 5D0→7F2 of Eu3＋, respectively. The concen-tration of Eu3＋ （x） had great effect on the emission intensity of Sr2-xMgSi2O7：Eu3＋x. When x varied in the range of 0.04-0.18, the intensity of emission peaks at 593 and 616 nm increased gradually with the concentration of Eu3＋ increasing. It was interesting that no concentration quenching occurred. Moreover, the luminescent intensity could be greatly enhanced with incorporation of charge compensator Li＋ ions.
文摘采用溶胶-凝胶法将TiO2-x N x包覆在长余辉光致发光材料(Sr2MgSi2O7∶Eu2+,Dy3+)表面制备得到TiO2-x N x/Sr2MgSi2O7∶Eu2+,Dy3+复合材料。利用X-射线衍射(XRD)、扫描电子显微镜(SEM)对TiO2-x N x/Sr2MgSi2O7∶Eu2+,Dy3+复合光催化材料的结构及表面形貌进行表征,并研究了TiO2-x N x/Sr2MgSi2O7∶Eu2+,Dy3+复合光催化材料对甲基橙溶液的降解性能。
基金Project supported by the National Natural Science Foundation （No. 20376009） and the Liaoning Natural Science Foundation （No. 20032129） of China.
文摘A novel method for synthesizing long afterglow silicate phosphor Sr3MgSi2O8：Eu^2＋,Dy^3＋using TEOS and inorganic powders as reactants was reported. Acetic acid as a catalyzer controlled the hydrolysis of TEOS by adjusting pH value of the system. The morphologies of precursor were characterized by transmission electron microscope （TEM）. The structure and optical properties of the phosphor powders were systematically investigated by means of X-ray diffraction and spectrofluorometry. TEM images have reflected the core-shell structure and quasi-spherical morphology of the precursor particles. It was found that the single-phase Sr3MgSi2O8 crystalline structures were obtained at 1050 and 1250 ℃ for the samples prepared with the nano-coating method and the solid state reaction, respectively. The emission intensities of the phosphors prepared by the present method were higher than those by the conventional process. Also, the afterglow characteristic was better than that prepared by solid-state reaction in the comparable condition.
文摘To discuss the function of Eu and Dy and their interaction in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ long afterglow material,the Eu and Dy single doped and their co-doped Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ were prepared.The samples were characterized by X-ray diffraction（XRD）,decay curves,photoluminescence（PL）,and thermoluminescence（TL）.The results indicate that Sr2 Mg Si2O7：Eu has afterglow properties,and the doping of Eu ion in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋ can lower the depth of traps.Eu ion can not only serve as luminescence center,but also produce traps in the matrix,meanwhile,it also exerts certain influences on the traps produced by Dy in Sr2 Mg Si2O7：Eu^2＋,Dy^3＋.The Dy ion can not act as luminescence center but relates to the change of the traps in the Sr2 Mg Si2O7 matrix.