尖晶石相Li_(1+x)Mn_2O_4及LiAl_(0.1)Mn_(1.9)O_(4-y)F_y的循环性能 被引量:2
1
作者 李艳 胡杨 +1 位作者 钟盛文 刘庆国 《电池》 CAS CSCD 北大核心 2005年第5期342-344,共3页
用高温固相法制备了尖晶石相Li1+xMn2O4及LiAl0.1Mn1.9O4-yFy锂离子电池正极材料。电性能测试表明,Al、F共掺杂能提高LiMn2O4的容量。LiAl0.1Mn1.9O4-yFy(y=0.05、0.10)常温下的初始容量分别为104.4 mAh/g和105.3mAh/g,高于Li1+xMn2O4;... 用高温固相法制备了尖晶石相Li1+xMn2O4及LiAl0.1Mn1.9O4-yFy锂离子电池正极材料。电性能测试表明,Al、F共掺杂能提高LiMn2O4的容量。LiAl0.1Mn1.9O4-yFy(y=0.05、0.10)常温下的初始容量分别为104.4 mAh/g和105.3mAh/g,高于Li1+xMn2O4;100次循环后,容量仍高于Li1+xMn2O4。Li1+xMn2O4(x=0.05、0.06和0.07)的高温(55℃)循环性能较好,100次循环后,容量衰减率分别为24.02%、21.78%和22.23%,除Li1.04Mn2O4(x=0.04)外,均低于LiAl0.1Mn1.9O4-yFy。阴离子的掺杂提高了材料的容量,阳离子掺杂抑制了Jahn-Teller效应,增强了尖晶石结构的稳定性,提高了材料的循环性能。 展开更多
关键词 尖晶石limn2O4 循环性能 锂离子电池
下载PDF
溶胶凝胶法制备尖晶石LiMn_2O_4合成条件的研究 被引量:2
2
作者 胡忠玉 《安徽化工》 CAS 2006年第5期9-13,共5页
采用溶胶凝胶合成法制备尖晶石LiMn2O4锂离子电池正极材料,详细研究了合成条件对产物结构和电化学性能的影响。结果表明,在以LiBr为Li源,乙酸锰为锰源,溶胶凝胶法制备尖晶石锂锰氧的最佳工艺条件是:Li/Mn=1.05/2;合成时溶液pH=7.5;采用... 采用溶胶凝胶合成法制备尖晶石LiMn2O4锂离子电池正极材料,详细研究了合成条件对产物结构和电化学性能的影响。结果表明,在以LiBr为Li源,乙酸锰为锰源,溶胶凝胶法制备尖晶石锂锰氧的最佳工艺条件是:Li/Mn=1.05/2;合成时溶液pH=7.5;采用分段式升温,以8℃/min从室温升温到450℃,保温5小时;再5℃/min的升温速率升温到650℃,再恒温12小时,然后自然冷却到室温,可得到结晶度较高,晶体结构完整,电化学性能较好的尖晶石型LiMn2O4。 展开更多
关键词 尖晶石limn2O4 溶胶凝胶合成法 锂离子二次电池 正极材料
下载PDF
胶晶模板法制备尖晶石型正极材料LiMn_2O_4
3
作者 王英平 王先友 +3 位作者 杨顺毅 吴强 白艳松 舒洪波 《中南大学学报(自然科学版)》 EI CAS CSCD 北大核心 2012年第3期848-854,共7页
通过聚甲基丙烯酸甲酯(PMMA)胶晶模板法制备尖晶石型LiMn2O4材料,并探讨焙烧温度对材料性能的影响。运用热重分析(TG)、X线衍射(XRD)、扫描电镜(SEM)、充放电测试和循环伏安测试等方法对LiMn2O4样品的结构、形貌以及电化学性能进行表征... 通过聚甲基丙烯酸甲酯(PMMA)胶晶模板法制备尖晶石型LiMn2O4材料,并探讨焙烧温度对材料性能的影响。运用热重分析(TG)、X线衍射(XRD)、扫描电镜(SEM)、充放电测试和循环伏安测试等方法对LiMn2O4样品的结构、形貌以及电化学性能进行表征和测试。研究结果表明:在不同温度下制备的LiMn2O4样品均具有较好的尖晶石型结构,且粒径分布均匀;在700℃时制备的LiMn2O4样品(S-700)具有最佳的电化学性能,在3.0~4.4V时,0.2C倍率首次放电比容量为130.9mA.h/g;0.5C倍率首次放电比容量为126.4mA.h/g,50次循环之后容量仍有102.7mA.h/g,具有良好的循环稳定性。 展开更多
关键词 锂离子电池 正极材料 尖晶石limn2O4 胶晶模板法 聚甲基丙烯酸甲酯微球
下载PDF
Effect of sintering time on the electrochemical properties of spinel LiMn_2O_4 synthesized by solid-state reaction 被引量:1
4
作者 Tao Li Weihua Qiu +3 位作者 Renhua Zhao Hui Xia Hailei Zhao Jingjing Liu 《Journal of University of Science and Technology Beijing》 CSCD 2008年第1期74-78,共5页
LiMn2O4 powder as a cathode materials for rechargeable lithium-ion batteries was prepared by solid-state reaction from LitCO3 and electrolytic MnOz at different sintering periods (2, 6, 18, and 32 h). X-ray diffract... LiMn2O4 powder as a cathode materials for rechargeable lithium-ion batteries was prepared by solid-state reaction from LitCO3 and electrolytic MnOz at different sintering periods (2, 6, 18, and 32 h). X-ray diffraction (XRD) patterns of the prepared samples are identified as the spinel structure with a space group of Fd3 m. The lattice parameters almost remain the same as the sintering periods increase. The sample with a sintering period of 32 h shows good cycling performance at both low and nigh current densities, and also elevated temperature. It is believed that the excellent electrochemical behavior of this sample results from its good crystallinity and large grain size compared with other samples. Different electrochemical measurements were conducted to investigate the electrochemical properties of spinel LiMn204. 2008 University of Science and Technology Beijing. All rights reserved. 展开更多
关键词 cathode material spinel limn204 sintering period microstructure electrochemical properties
下载PDF
低温电解法制备球形尖晶石LiMn_2O_4及性能研究
5
作者 周园 岳鸿飞 冉广芬 《稀有金属材料与工程》 SCIE EI CAS CSCD 北大核心 2007年第8期1477-1479,共3页
采用MnSO4-H2SO4混合溶液作电解液,高纯铅板作电极,控制电解池温度为0~10℃,低温电解制取球形MnO2微粒;将其用一定浓度硝酸锂溶液浸渍,经过520℃低温合成、760℃高温结晶获得球径较为均一的球形尖晶石锰酸锂锂离子电池正极材料。通过XR... 采用MnSO4-H2SO4混合溶液作电解液,高纯铅板作电极,控制电解池温度为0~10℃,低温电解制取球形MnO2微粒;将其用一定浓度硝酸锂溶液浸渍,经过520℃低温合成、760℃高温结晶获得球径较为均一的球形尖晶石锰酸锂锂离子电池正极材料。通过XRD和SEM对其进行了相结构表征和表面形貌观察。组装试验电池,测得材料初始容量约为105mAh.g-1,6次循环放电后循环过程趋于稳定,第30次循环充电容量保持在98.1mAh.g-1,放电容量保持在95.0mAh.g-1,表现出良好的充放电循环性能。 展开更多
关键词 低温电解 球形尖晶石limn2O4 正极材料 锂离子电池
下载PDF