Cubic and monoclinic Gd2O3:Eu3+ phosphors in the range of nano-scale and submicron-scale were prepared by a modified solution combustion method.Coexistence of cubic and monoclinic phases was found in the highest lumin...Cubic and monoclinic Gd2O3:Eu3+ phosphors in the range of nano-scale and submicron-scale were prepared by a modified solution combustion method.Coexistence of cubic and monoclinic phases was found in the highest luminescent sample synthesized at 600 oC.In relation to commercial sample,the relative luminescence intensity was 49.8%.The shape of emission spectrum of the sample thus changed and the charge-transfer-state band of excitation spectrum slightly shift toward higher energies.With increasing the anneal...展开更多
A 20 wt% Ni/bentonite catalyst was prepared by a solution combustion synthesis (SCS), which exhibited higher activity for the CO_2methanation than that of an impregnation method (IPM), and the catalyst prepared by SCS...A 20 wt% Ni/bentonite catalyst was prepared by a solution combustion synthesis (SCS), which exhibited higher activity for the CO_2methanation than that of an impregnation method (IPM), and the catalyst prepared by SCS showed a CO_2 conversion of 85% and a CH4selectivity of 100% at 300 °C, atmospheric pressure, and 3600 ml·(g cat)-1·h-1, and the catalyst exhibited stable within a 110-h reaction. The results showed higher me- tallic Ni dispersion, smaller Ni particle size, larger specific surface area and lower reduction temperature in the Ni/ bentonite prepared by SCS than that of IPM. And the Ni/bentonite prepared by the SCS moderated the interaction between NiO and bentonite.展开更多
Ultrafine Y0.95–xGdxEu0.05Al3(BO3)4 phosphors with different Gd3+ concentrations were prepared by a solution combustion method, and characterized with X-ray diffraction (XRD), scanning electron microscopy (SEM). Resu...Ultrafine Y0.95–xGdxEu0.05Al3(BO3)4 phosphors with different Gd3+ concentrations were prepared by a solution combustion method, and characterized with X-ray diffraction (XRD), scanning electron microscopy (SEM). Results showed that the pure phase of YAl3(BO3)4 was obtained at 1000 oC and the prepared particle size varied with calcining temperatures. Photoluminescence spectra indicated that the dominant emission peak was observed at 612 nm due to the 5D0→7F2 transition of Eu3+. The luminescence intensity of ...展开更多
Nanoscale Lu2O3：Eu3＋ phosphor was prepared by a modified solution combustion method using urea and acrylamide monomer.The particle sizes and photoluminescent properties of nano-phosphor were closely related to the m...Nanoscale Lu2O3：Eu3＋ phosphor was prepared by a modified solution combustion method using urea and acrylamide monomer.The particle sizes and photoluminescent properties of nano-phosphor were closely related to the molar ratio of urea-to-RE nitrates and acrylamide monomer-to-RE nitrates.The as-prepared samples with the sizes of 9.6-11.6 nm were characterized by X-ray diffraction,scanning electron microscopy,transmission electron microscopy and energy dispersive spectrometer.Lu2O3：Eu3＋ nano-phosphor that depicted high photoluminescence in the size around 10 nm was reported.Compared with the sample prepared by solid state reaction,the photoluminescence of sample was increased sufficiently to be 45.1%.The emission spectra of the samples presented the typical emission from 5D0 level to 7FJ（J=0,1,2,3,4） level of the Eu3＋ ion.展开更多
基金supported by the Ministry of Science and Technology of China (2006CB601104)the Foundation of International Joint Research of Beijing (2007N08)+1 种基金Natural Science Foundation of Jiangxi Province (2009GQC0042)Foundation of Jiangxi Educational Committee (GJJ10153)
文摘Cubic and monoclinic Gd2O3:Eu3+ phosphors in the range of nano-scale and submicron-scale were prepared by a modified solution combustion method.Coexistence of cubic and monoclinic phases was found in the highest luminescent sample synthesized at 600 oC.In relation to commercial sample,the relative luminescence intensity was 49.8%.The shape of emission spectrum of the sample thus changed and the charge-transfer-state band of excitation spectrum slightly shift toward higher energies.With increasing the anneal...
基金Supported by the National Natural Science Foundation of China(21566005)the Natural Science Foundation of Guangxi Province(2016GXNSFFA380015)
文摘A 20 wt% Ni/bentonite catalyst was prepared by a solution combustion synthesis (SCS), which exhibited higher activity for the CO_2methanation than that of an impregnation method (IPM), and the catalyst prepared by SCS showed a CO_2 conversion of 85% and a CH4selectivity of 100% at 300 °C, atmospheric pressure, and 3600 ml·(g cat)-1·h-1, and the catalyst exhibited stable within a 110-h reaction. The results showed higher me- tallic Ni dispersion, smaller Ni particle size, larger specific surface area and lower reduction temperature in the Ni/ bentonite prepared by SCS than that of IPM. And the Ni/bentonite prepared by the SCS moderated the interaction between NiO and bentonite.
基金Project supported by the Fundamental Research Funds for the Central Universities and Natural Science Basic Research Plan in Shaanxi Province of China (2009JQ6009)
文摘Ultrafine Y0.95–xGdxEu0.05Al3(BO3)4 phosphors with different Gd3+ concentrations were prepared by a solution combustion method, and characterized with X-ray diffraction (XRD), scanning electron microscopy (SEM). Results showed that the pure phase of YAl3(BO3)4 was obtained at 1000 oC and the prepared particle size varied with calcining temperatures. Photoluminescence spectra indicated that the dominant emission peak was observed at 612 nm due to the 5D0→7F2 transition of Eu3+. The luminescence intensity of ...
基金Project supported by the Special Foundation for Technique Development Research of Institute of Ministry of Science and Technology of China (2009EG115070,2010EG115072)Natural Science Foundation of Jiangxi Province (2009GQC0042)+1 种基金Foundation of Jiangxi Educational Committee (GJJ10153)Foundation of Jiangxi University of Science and Technology (Jxxjzd10007)
文摘Nanoscale Lu2O3：Eu3＋ phosphor was prepared by a modified solution combustion method using urea and acrylamide monomer.The particle sizes and photoluminescent properties of nano-phosphor were closely related to the molar ratio of urea-to-RE nitrates and acrylamide monomer-to-RE nitrates.The as-prepared samples with the sizes of 9.6-11.6 nm were characterized by X-ray diffraction,scanning electron microscopy,transmission electron microscopy and energy dispersive spectrometer.Lu2O3：Eu3＋ nano-phosphor that depicted high photoluminescence in the size around 10 nm was reported.Compared with the sample prepared by solid state reaction,the photoluminescence of sample was increased sufficiently to be 45.1%.The emission spectra of the samples presented the typical emission from 5D0 level to 7FJ（J=0,1,2,3,4） level of the Eu3＋ ion.