SnO2 nano particles with various Pd-doping concentrations were prepared using a template-free hydrothermal method.The effects of Pd doping on the crystal structure,morphology,microstructure,thermal stability and surfa...SnO2 nano particles with various Pd-doping concentrations were prepared using a template-free hydrothermal method.The effects of Pd doping on the crystal structure,morphology,microstructure,thermal stability and surface chemistry of these nano particles were characterized by transmission electron microscope,X-ray diffractometer and X-ray photoelectron spectroscope respectively.It was observed that Pd-doping had little effect on the grain sizes of the obtained SnO2 nano particles during the hydrothermal route.During thermal annealing,Pd-doping could restrain the growth of grain sizes below 500℃ while the grain growth was promoted when the temperature increased to above 700℃.XPS results revealed that Pd existed in three chemical states in the as-synthesized sample as Pd^0,Pd^2＋ and Pd^4＋,respectively.Pd^4＋ was the main state which was responsible for improving the gas-sensing property.The optimal Pd-doping concentration for better gas-sensing property and thermal stability was 2.0%-2.5% （mole fraction）.展开更多
以Sn(OEt)2为起始原料,采用水热晶化法合成了分散性良好的金红石结构的SnO2纳米颗粒.采用X射线衍射对其进行了表征,表明SnO2纳米颗粒的结晶性良好,颗粒尺寸小于10nm.将合成的SnO2纳米颗粒均匀分散到Sb:SnO2镀膜液中,经陈化后制成镀膜溶...以Sn(OEt)2为起始原料,采用水热晶化法合成了分散性良好的金红石结构的SnO2纳米颗粒.采用X射线衍射对其进行了表征,表明SnO2纳米颗粒的结晶性良好,颗粒尺寸小于10nm.将合成的SnO2纳米颗粒均匀分散到Sb:SnO2镀膜液中,经陈化后制成镀膜溶胶,以溶胶-凝胶浸渍镀膜工艺制备纳米颗粒掺杂Sb:SnO2薄膜.分别采用范德堡(Van Der Pauw)法、UV/VIS分光光度计和FTIR中红外分析仪测量并分析膜层的导电性能、光学性能及结构特征,研究了导电纳米颗粒添加对Sb:SnO2薄膜电性能、光学性能和结构的影响.展开更多
基金Projects(60806032,20975107) supported by the National Natural Science Foundation of ChinaProject(2009R10064) supported by the Scientific Research Foundation for the Returned Overseas Chinese Scholars of Education Ministry,China+2 种基金 Project(2009R10064) supported by "Qianjiang Talent Program"Projects(2009A610058,2009A610030) supported by the Ningbo Natural Science Foundation,ChinaProject supported by K.C.WONG Magna Fund in Ningbo University,China
文摘SnO2 nano particles with various Pd-doping concentrations were prepared using a template-free hydrothermal method.The effects of Pd doping on the crystal structure,morphology,microstructure,thermal stability and surface chemistry of these nano particles were characterized by transmission electron microscope,X-ray diffractometer and X-ray photoelectron spectroscope respectively.It was observed that Pd-doping had little effect on the grain sizes of the obtained SnO2 nano particles during the hydrothermal route.During thermal annealing,Pd-doping could restrain the growth of grain sizes below 500℃ while the grain growth was promoted when the temperature increased to above 700℃.XPS results revealed that Pd existed in three chemical states in the as-synthesized sample as Pd^0,Pd^2＋ and Pd^4＋,respectively.Pd^4＋ was the main state which was responsible for improving the gas-sensing property.The optimal Pd-doping concentration for better gas-sensing property and thermal stability was 2.0%-2.5% （mole fraction）.
文摘以Sn(OEt)2为起始原料,采用水热晶化法合成了分散性良好的金红石结构的SnO2纳米颗粒.采用X射线衍射对其进行了表征,表明SnO2纳米颗粒的结晶性良好,颗粒尺寸小于10nm.将合成的SnO2纳米颗粒均匀分散到Sb:SnO2镀膜液中,经陈化后制成镀膜溶胶,以溶胶-凝胶浸渍镀膜工艺制备纳米颗粒掺杂Sb:SnO2薄膜.分别采用范德堡(Van Der Pauw)法、UV/VIS分光光度计和FTIR中红外分析仪测量并分析膜层的导电性能、光学性能及结构特征,研究了导电纳米颗粒添加对Sb:SnO2薄膜电性能、光学性能和结构的影响.
基金National Science Foundation of China(11364005,11174132)Foundation of the National Key Project for Basic Research(2010CB923402,2011CB922102)+1 种基金International Cooperation Project of Guizhou Province(2012-7002)National Science Foundation of Guizhou Province(2014-2059)
