This paper presents a new method of modifying sodium silicate binder with ultra-fine powders. The sodium silicate binder modified by ultra-fine powder A and the organic B can reduce the addition amount of the binder. ...This paper presents a new method of modifying sodium silicate binder with ultra-fine powders. The sodium silicate binder modified by ultra-fine powder A and the organic B can reduce the addition amount of the binder. The results indicate that the 24 h strength has increased by 39.9% at room temperature and the residual strength has decreased by 30.7% at 800℃, compared to the conventional sodium silicate. An available material to improve the moisture resistance was also found by adding about 2% more inorganic C, and it can increase the moist strength by 20%. In the end, the microanalyses are given to explain the modifying machanism, i. e., the ultra-fine powder A can refine the sodium silicate binder to avoid holes in the binder bond, which can increase the 24 h strength at room temperture, and can lead to more cracks in the bond after the molding sand is heated to 800℃. This is because of the stress caused by the new eutectic complex of modified sodium silicate binder.展开更多
Tricalcium silicate cement(TSC)has been widely used in dental materials because of its self-setting behavior,good bioactivity,biocompatibility,osteoinductivity,and antibacterial effect.Tricalcium silicate(C3S)powder w...Tricalcium silicate cement(TSC)has been widely used in dental materials because of its self-setting behavior,good bioactivity,biocompatibility,osteoinductivity,and antibacterial effect.Tricalcium silicate(C3S)powder was prepared by Pechini technique with a calcining temperature of 1300℃ for 3 h.The influence of liquid/powder(L/P)rate on the setting time and the mechanical property of TSC was studied.Characterization methods including XRD,FTIR,SEM-EDS,TEM,and ICP-AES were utilized to study the properties of C3S powder and its hydrated cement.The bioactivity and biocompatibility of the cement were investigated by soaking test and cell culture,respectively.The results show that the L/P rate plays an important role in the setting time and the compressive strength of TSC.The surface of TSC was covered by hydroxyapatite deposition during the immersion experiment and the cells attachment on the surface of TSC was well,which indicated that TSC has good bioactivity and biocompatibility.In addition,TSC has excellent antibacterial properties against Staphylococcus aureus.In conclusion,TSC is a promising candidate for root canal filling materials.展开更多
The reactivity of the recycled glass powder (GP) in a cementitious medium has been studied over time by means of X-ray diffraction and thermal gravimetric analysis. Two different mixtures based on cement/glass powder ...The reactivity of the recycled glass powder (GP) in a cementitious medium has been studied over time by means of X-ray diffraction and thermal gravimetric analysis. Two different mixtures based on cement/glass powder (0 or 20 wt% GP) and lime/glass powder (70 wt% GP) were considered. Analysis revealed the coexistence of both hydration and pozzolanic reaction during the hardening of the mortars. At young age, the cement hydration would prevail over the pozzolanic one resulting in a decrease of physico-chemical </span></span><a name="_GoBack"></a><span><span><span style="font-family:"">and mechanical properties of the material due to the dilution effect. The pozzolanic reaction that predominates from 91 days, would induce the formation of supplementary C-S-H leading to improve the material properties.展开更多
Recoverable TiO2 photocatalysis material supported by silicon powder was prepared with sol-gel method, afterwards the silica gol and sodium silicate were used as molding binder respectively to investigate their effec...Recoverable TiO2 photocatalysis material supported by silicon powder was prepared with sol-gel method, afterwards the silica gol and sodium silicate were used as molding binder respectively to investigate their effects （including binder type and binder addition quantity） on the crystal structure and catalysis properties of photocatalyst. In this work, the catalysis activity was defined as the degradation rate of methyl orange solution upon ultraviolet lamp irradiation, and the specific areas were determined with nitrogen desorption method. TiO2 crystal form was measured with X-ray powder diffraction and their micro-morphology was observed with SEM. Experimental results indicate that these two binders do not affect the crystal form transformation of TiO2, but silica gol can increase the specific surface area of TiO2 photocatalyst obviously and the addition of sodium silicate can decrease it. In all, silica gol is a better candidate than sodium silicate for higher catalysis property. In conclusion, 6% silica gol is the optimal addition concentration. Under this condition, the ratio of anatase to rutile TiO2 is 64：36, the specific area is 29.67 m^2/g, and as expected, the degradation rate of methyl orange could be as high as 90% after irradiation for 5 days.展开更多
基金The subject is supported by National Natural Science Fundof China: 50575085.
文摘This paper presents a new method of modifying sodium silicate binder with ultra-fine powders. The sodium silicate binder modified by ultra-fine powder A and the organic B can reduce the addition amount of the binder. The results indicate that the 24 h strength has increased by 39.9% at room temperature and the residual strength has decreased by 30.7% at 800℃, compared to the conventional sodium silicate. An available material to improve the moisture resistance was also found by adding about 2% more inorganic C, and it can increase the moist strength by 20%. In the end, the microanalyses are given to explain the modifying machanism, i. e., the ultra-fine powder A can refine the sodium silicate binder to avoid holes in the binder bond, which can increase the 24 h strength at room temperture, and can lead to more cracks in the bond after the molding sand is heated to 800℃. This is because of the stress caused by the new eutectic complex of modified sodium silicate binder.
基金Project(2019JJ50797)supported by Hunan Provincial Natural Science Foundation of China。
文摘Tricalcium silicate cement(TSC)has been widely used in dental materials because of its self-setting behavior,good bioactivity,biocompatibility,osteoinductivity,and antibacterial effect.Tricalcium silicate(C3S)powder was prepared by Pechini technique with a calcining temperature of 1300℃ for 3 h.The influence of liquid/powder(L/P)rate on the setting time and the mechanical property of TSC was studied.Characterization methods including XRD,FTIR,SEM-EDS,TEM,and ICP-AES were utilized to study the properties of C3S powder and its hydrated cement.The bioactivity and biocompatibility of the cement were investigated by soaking test and cell culture,respectively.The results show that the L/P rate plays an important role in the setting time and the compressive strength of TSC.The surface of TSC was covered by hydroxyapatite deposition during the immersion experiment and the cells attachment on the surface of TSC was well,which indicated that TSC has good bioactivity and biocompatibility.In addition,TSC has excellent antibacterial properties against Staphylococcus aureus.In conclusion,TSC is a promising candidate for root canal filling materials.
文摘The reactivity of the recycled glass powder (GP) in a cementitious medium has been studied over time by means of X-ray diffraction and thermal gravimetric analysis. Two different mixtures based on cement/glass powder (0 or 20 wt% GP) and lime/glass powder (70 wt% GP) were considered. Analysis revealed the coexistence of both hydration and pozzolanic reaction during the hardening of the mortars. At young age, the cement hydration would prevail over the pozzolanic one resulting in a decrease of physico-chemical </span></span><a name="_GoBack"></a><span><span><span style="font-family:"">and mechanical properties of the material due to the dilution effect. The pozzolanic reaction that predominates from 91 days, would induce the formation of supplementary C-S-H leading to improve the material properties.
基金the Natural Science Foundation of Fujian Province(No.T08J0129)the Science and Technology Developing Foundation of Fuzhou University(No. 2008-XQ-001)Research Project of the Education Department of Fujian Province(JA05185)
文摘Recoverable TiO2 photocatalysis material supported by silicon powder was prepared with sol-gel method, afterwards the silica gol and sodium silicate were used as molding binder respectively to investigate their effects （including binder type and binder addition quantity） on the crystal structure and catalysis properties of photocatalyst. In this work, the catalysis activity was defined as the degradation rate of methyl orange solution upon ultraviolet lamp irradiation, and the specific areas were determined with nitrogen desorption method. TiO2 crystal form was measured with X-ray powder diffraction and their micro-morphology was observed with SEM. Experimental results indicate that these two binders do not affect the crystal form transformation of TiO2, but silica gol can increase the specific surface area of TiO2 photocatalyst obviously and the addition of sodium silicate can decrease it. In all, silica gol is a better candidate than sodium silicate for higher catalysis property. In conclusion, 6% silica gol is the optimal addition concentration. Under this condition, the ratio of anatase to rutile TiO2 is 64：36, the specific area is 29.67 m^2/g, and as expected, the degradation rate of methyl orange could be as high as 90% after irradiation for 5 days.