The microstructure and mechanical properties of Mg-6Al-1.2Y-0.9Nd magnesium alloy with Sb, Sm, or Sn addition were investigated through X-ray diffraction （XRD）, optical microscopy （OM）, scanning electron microsco...The microstructure and mechanical properties of Mg-6Al-1.2Y-0.9Nd magnesium alloy with Sb, Sm, or Sn addition were investigated through X-ray diffraction （XRD）, optical microscopy （OM）, scanning electron microscopy （SEM）, and energy dispersive spectroscopy （EDS）. The results show that small amounts of Sb, Sm, and especially Sn can refine the grains of the alloy. High melting point Sb3Y5, Al2Sm, and Nd5Sn3 intermetallic compounds can be formed respectively when Sb, Sm, and Sn are added to the alloy. Sb and Sm can improve the tensile strength of the alloy at ambient and elevated temperatures. The tensile strength of the alloy with Sm addition is the highest at 293 and 423 K. However, the tensile strength of the alloy with Sn addition is the highest at 448 K.展开更多
Ti/Sb-SnO2 anodes were prepared by thermal decomposition to examine the influence of the amount of Sb dopant on the structure and electrocatalytic capability of the electrodes in the oxidation of 4-chlorophenol. The p...Ti/Sb-SnO2 anodes were prepared by thermal decomposition to examine the influence of the amount of Sb dopant on the structure and electrocatalytic capability of the electrodes in the oxidation of 4-chlorophenol. The physicochemical properties of the Sb-SnO2 coating were markedly influenced by different amounts of Sb dopant. The electrodes, which contained 5% Sb dopant in the coating, presented a much more homogenous surface and much smaller mud-cracks, compared with Ti/Sb-SnO2 electrodes containing 10% or 15% Sb dopant, which exibited larger mud cracks and pores on the surface. However, the main microstructure remained unchanged with the addition of the Sb dopant. No new crystal phase was observed by X-ray diffraction （XRD）. The electrochemical oxidation of 4-chlorophenol on the Ti/SnO2 electrode with 5% Sb dopant was inclined to electrochemical combustion; while for those containing more Sb dopant, intermediate species were accumulated. The electrodes with 5% Sb dopant showed the highest efficiency in the bulk electrolysis of 4-chlorophenol at a current density of 20 mA/cm^2 for 180 min; and the removal rates of 4-chlorophenol and COD were 51.0% and 48.9%, respectively.展开更多
文摘The microstructure and mechanical properties of Mg-6Al-1.2Y-0.9Nd magnesium alloy with Sb, Sm, or Sn addition were investigated through X-ray diffraction （XRD）, optical microscopy （OM）, scanning electron microscopy （SEM）, and energy dispersive spectroscopy （EDS）. The results show that small amounts of Sb, Sm, and especially Sn can refine the grains of the alloy. High melting point Sb3Y5, Al2Sm, and Nd5Sn3 intermetallic compounds can be formed respectively when Sb, Sm, and Sn are added to the alloy. Sb and Sm can improve the tensile strength of the alloy at ambient and elevated temperatures. The tensile strength of the alloy with Sm addition is the highest at 293 and 423 K. However, the tensile strength of the alloy with Sn addition is the highest at 448 K.
基金Project supported by the Institute of Environmental Engineering,Peking University and China Postdoctoral Science Foundation(No.2005037032)
文摘Ti/Sb-SnO2 anodes were prepared by thermal decomposition to examine the influence of the amount of Sb dopant on the structure and electrocatalytic capability of the electrodes in the oxidation of 4-chlorophenol. The physicochemical properties of the Sb-SnO2 coating were markedly influenced by different amounts of Sb dopant. The electrodes, which contained 5% Sb dopant in the coating, presented a much more homogenous surface and much smaller mud-cracks, compared with Ti/Sb-SnO2 electrodes containing 10% or 15% Sb dopant, which exibited larger mud cracks and pores on the surface. However, the main microstructure remained unchanged with the addition of the Sb dopant. No new crystal phase was observed by X-ray diffraction （XRD）. The electrochemical oxidation of 4-chlorophenol on the Ti/SnO2 electrode with 5% Sb dopant was inclined to electrochemical combustion; while for those containing more Sb dopant, intermediate species were accumulated. The electrodes with 5% Sb dopant showed the highest efficiency in the bulk electrolysis of 4-chlorophenol at a current density of 20 mA/cm^2 for 180 min; and the removal rates of 4-chlorophenol and COD were 51.0% and 48.9%, respectively.