A Si-Al-lr oxidation resistant coating was prepared for SiC coated carbon/carbon composites by slurry dipping. The phase composition, microstructure and oxidation resistance of the as-prepared Si-Al-lr coating were st...A Si-Al-lr oxidation resistant coating was prepared for SiC coated carbon/carbon composites by slurry dipping. The phase composition, microstructure and oxidation resistance of the as-prepared Si-Al-lr coating were studied by XRD （X-ray diffraction）, SEM （scanning electron microscopy）, and isothermal oxidation test at 1773 K in air, respectively. The surface of the as-prepared Si-Al-lr coating was dense and the thickness was approximately 100 um. Its anti-oxidation property was superior to that of the inner SiC coating. The weight loss of SiC/Si- Al-lr coated carbon/carbon composites was less than 5 wt. pct after oxidation at 1773 K in air for 79 h. The local oxidation defects in the coating may result in the failure of the SiC/Si-Al-Ir coating.展开更多
基金supported by the National "973"Project under grant No. 2006CB600908
文摘A Si-Al-lr oxidation resistant coating was prepared for SiC coated carbon/carbon composites by slurry dipping. The phase composition, microstructure and oxidation resistance of the as-prepared Si-Al-lr coating were studied by XRD （X-ray diffraction）, SEM （scanning electron microscopy）, and isothermal oxidation test at 1773 K in air, respectively. The surface of the as-prepared Si-Al-lr coating was dense and the thickness was approximately 100 um. Its anti-oxidation property was superior to that of the inner SiC coating. The weight loss of SiC/Si- Al-lr coated carbon/carbon composites was less than 5 wt. pct after oxidation at 1773 K in air for 79 h. The local oxidation defects in the coating may result in the failure of the SiC/Si-Al-Ir coating.