In this study,the microstructures and mechanical properties of 9%Cr reduced activation ferritic/martensitic（RAFM） steel friction stir welded joints were investigated.When a W-Re tool is used,the recommended welding ...In this study,the microstructures and mechanical properties of 9%Cr reduced activation ferritic/martensitic（RAFM） steel friction stir welded joints were investigated.When a W-Re tool is used,the recommended welding parameters are 300 rpm rotational speed,60 mm/min welding speed and10 kn axial force.In stir zone（SZ）,austenite dynamic recrystallization induced by plastic deformation and the high cooling rates lead to an obvious refinement of prior austenite grains and martensite laths.The microstructure in SZ contains lath martensite with high dislocation density,a lot of nano-sized MX and M3C phase particles,but almost no M23C6 precipitates.In thermal mechanically affect zone（TMAZ）and heat affect zone（HAZ）,refinement of prior austenite and martensitic laths and partial dissolution of M（23）C6 precipitates are obtained at relatively low rotational speed.However,with the increase of heat input,coarsening of martensitic laths,prior austenite grains,and complete dissolution of M23C6 precipitates are achieved.Impact toughness of SZ at-20℃ is slightly lower than that of base material（BM）,and exhibits a decreasing trend with the increase of rotational speed.展开更多
针对核聚变反应堆试验包层模块(TBM)中使用的CLF-1低活化铁素体/马氏体钢进行焊接试验,采用15 k W光纤激光,实现了17.5 mm厚CLF-1钢的穿透焊接,得到了正反表面成形良好、无明显缺陷的焊接接头,并对接头显微组织及力学性能进行了分析研究...针对核聚变反应堆试验包层模块(TBM)中使用的CLF-1低活化铁素体/马氏体钢进行焊接试验,采用15 k W光纤激光,实现了17.5 mm厚CLF-1钢的穿透焊接,得到了正反表面成形良好、无明显缺陷的焊接接头,并对接头显微组织及力学性能进行了分析研究.结果表明,焊缝区主要为粗大的板条马氏体;熔合线附近热影响区为细小的板条马氏体和少量贝氏体;不完全淬火区为经焊接热循环作用下二次回火的回火索氏体及马氏体双相组织;接头室温及550℃高温抗拉强度较高,均断裂于母材;焊缝显微硬度高于母材,且热影响区无明显软化;接头冲击韧性良好.接头综合力学性能良好.展开更多
Reduced activation ferritic/martensitic steel （RAFM） is recognized as the primary candidate structural material for ITER＇s test blanket module （TBM）. To provide a material and property database for the design and...Reduced activation ferritic/martensitic steel （RAFM） is recognized as the primary candidate structural material for ITER＇s test blanket module （TBM）. To provide a material and property database for the design and fabrication of the Chinese helium cooled ceramic breeding TBM （CN HCCB TBM）, a type of RAFM steel named CLF-1 was developed and chaxacter^zed at the Southwestern Institute of Physics （SWIP）, China. In this paper, the R＆D status of CLF-1 steel and the technical issues in using CLF-1 steel to manufacture CN HCCB TBM were reviewed, including the steel manufacture and different welding technologies. Several kinds of property data have been obtained for its application to the design of the ITER TBM.展开更多
The hot deformation behavior and workability of a new reduced activation ferritic/martensitic steel named SIMP steel for accelerator-driven system were studied. The flow curve and its microstructure were studied at 90...The hot deformation behavior and workability of a new reduced activation ferritic/martensitic steel named SIMP steel for accelerator-driven system were studied. The flow curve and its microstructure were studied at 900-1200 ℃ and strain rate range of 0.001-10 s^-1. The results showed that the deformation behavior of the SIMP steel during hot compression could be manifested by the Zener-Hollomon parameter in an exponent-type equation. Based on the obtained constitutive equation, the calculated flow stresses were in agreement with the experimentally measured ones, and the average activity energies Qdrv and QHw for the initiation of dynamic recrystallization and the peak strain were calculated to be 476.1 kJ/mol and 462.7 kJ/mol, respectively. Furthermore, based on the processing maps and microstructure evolution, the optimum processing condition for the SIMP steel was determined to be 1050-1200 ℃/0.001-0.1s^-1.展开更多
基金financially supported by the National Natural Science Foundation of China (Grant Nos.51325401 and U1660201)the National Magnetic Confinement Fusion Energy Research Project (Grant No.2015GB119001)
文摘In this study,the microstructures and mechanical properties of 9%Cr reduced activation ferritic/martensitic（RAFM） steel friction stir welded joints were investigated.When a W-Re tool is used,the recommended welding parameters are 300 rpm rotational speed,60 mm/min welding speed and10 kn axial force.In stir zone（SZ）,austenite dynamic recrystallization induced by plastic deformation and the high cooling rates lead to an obvious refinement of prior austenite grains and martensite laths.The microstructure in SZ contains lath martensite with high dislocation density,a lot of nano-sized MX and M3C phase particles,but almost no M23C6 precipitates.In thermal mechanically affect zone（TMAZ）and heat affect zone（HAZ）,refinement of prior austenite and martensitic laths and partial dissolution of M（23）C6 precipitates are obtained at relatively low rotational speed.However,with the increase of heat input,coarsening of martensitic laths,prior austenite grains,and complete dissolution of M23C6 precipitates are achieved.Impact toughness of SZ at-20℃ is slightly lower than that of base material（BM）,and exhibits a decreasing trend with the increase of rotational speed.
文摘针对核聚变反应堆试验包层模块(TBM)中使用的CLF-1低活化铁素体/马氏体钢进行焊接试验,采用15 k W光纤激光,实现了17.5 mm厚CLF-1钢的穿透焊接,得到了正反表面成形良好、无明显缺陷的焊接接头,并对接头显微组织及力学性能进行了分析研究.结果表明,焊缝区主要为粗大的板条马氏体;熔合线附近热影响区为细小的板条马氏体和少量贝氏体;不完全淬火区为经焊接热循环作用下二次回火的回火索氏体及马氏体双相组织;接头室温及550℃高温抗拉强度较高,均断裂于母材;焊缝显微硬度高于母材,且热影响区无明显软化;接头冲击韧性良好.接头综合力学性能良好.
基金supported by the China Nuclear Energy Development Program (No. H6603100)
文摘Reduced activation ferritic/martensitic steel （RAFM） is recognized as the primary candidate structural material for ITER＇s test blanket module （TBM）. To provide a material and property database for the design and fabrication of the Chinese helium cooled ceramic breeding TBM （CN HCCB TBM）, a type of RAFM steel named CLF-1 was developed and chaxacter^zed at the Southwestern Institute of Physics （SWIP）, China. In this paper, the R＆D status of CLF-1 steel and the technical issues in using CLF-1 steel to manufacture CN HCCB TBM were reviewed, including the steel manufacture and different welding technologies. Several kinds of property data have been obtained for its application to the design of the ITER TBM.
基金financially supported by the National Natural Science Foundation of China (No. 51874368)the Project of CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences (No. 2018NMSAKF03)
文摘The hot deformation behavior and workability of a new reduced activation ferritic/martensitic steel named SIMP steel for accelerator-driven system were studied. The flow curve and its microstructure were studied at 900-1200 ℃ and strain rate range of 0.001-10 s^-1. The results showed that the deformation behavior of the SIMP steel during hot compression could be manifested by the Zener-Hollomon parameter in an exponent-type equation. Based on the obtained constitutive equation, the calculated flow stresses were in agreement with the experimentally measured ones, and the average activity energies Qdrv and QHw for the initiation of dynamic recrystallization and the peak strain were calculated to be 476.1 kJ/mol and 462.7 kJ/mol, respectively. Furthermore, based on the processing maps and microstructure evolution, the optimum processing condition for the SIMP steel was determined to be 1050-1200 ℃/0.001-0.1s^-1.