The effects of pulsed magnetic field on the solidified microstructure of an AZ91D magnesium alloy were investigated. The experimental results show that the remarkable microstructural refinement is achieved when the pu...The effects of pulsed magnetic field on the solidified microstructure of an AZ91D magnesium alloy were investigated. The experimental results show that the remarkable microstructural refinement is achieved when the pulsed magnetic field is applied in the solidification of AZ91D alloy. The average grain size of the as-cast microstructure of AZ91D alloy is refined to 104 μm. Besides the grain refinement, the morphology of the primary α-Mg is changed from dendritic to rosette, then to globular shape with changing the parameters of the pulsed magnetic field. The pulsed magnetic field causes melt convection during solidification, which makes the temperature of the whole melt homogenized, and produces an undercooling zone in front of the liquid/solid interface by the magnetic pressure, which makes the nucleation rate increased and big dendrites prohibited. In addition, primary α-Mg dendrites break into fine crystals, resulting in a refined solidification structure of the AZ91D alloy. The Joule heat effect induced in the melt also strengthens the grain refinement effect and spheroidization of dendrite arms.展开更多
The structures and macro-segregation of 2124 Al-alloy were studied when a pulsed magnetic field (PMF) was applied during solidification. It is found through experi-ments that a remarkable change occurs in the solidifi...The structures and macro-segregation of 2124 Al-alloy were studied when a pulsed magnetic field (PMF) was applied during solidification. It is found through experi-ments that a remarkable change occurs in the solidification structures of 2124 Al-alloy under pulsed magnetic field. The eutectic phase at grain boundaries change from thick continuous eutectic network to thin discontinuous one, and the distribution of solute elements was also homogenized. The typical negative segregation phenomenon of Cu in common solidification condition was restrained, and the segregation of Mg decreased.展开更多
The effects of a pulsed magnetic field （PMF） on the microsegregation of solute elements during directional solidification of a Ni-based single crystal superalloy were experimentally investigated, and the results sho...The effects of a pulsed magnetic field （PMF） on the microsegregation of solute elements during directional solidification of a Ni-based single crystal superalloy were experimentally investigated, and the results show that the PMF significantly affects the microsegregation of Al, Ti, Co, Mo and W elements in the alloy. However, the distribution behavior differs for both positive and negative segregation elements. With the PMF, the microsegregation of negative segregation elements, Co and W, was restrained effectively, while that of positive segregation elements, A1, Ti and Mo, was aggravated. A segregation model was estab- lished to reveal the distribution mechanism of the elements with PME It is considered that, under the action of PME the jumping of solute atoms from the liquid phase to solid phase is hindered, but the jumping of solute atoms from the solid phase into liquid phase is promoted during solidification. As a result, the effective distribution coefficient of the solute atoms is reduced, which leads to the reduction of microsegregation of negative segregation elements and aggravation of microsegregation of positive segregation elements.展开更多
基金Project(50774075) supported by the National Natural Science Foundation of ChinaProject(2006BAE04B01-4) supported by the Key Technologies R&D Program of Ministry of Science and Technology of China
文摘The effects of pulsed magnetic field on the solidified microstructure of an AZ91D magnesium alloy were investigated. The experimental results show that the remarkable microstructural refinement is achieved when the pulsed magnetic field is applied in the solidification of AZ91D alloy. The average grain size of the as-cast microstructure of AZ91D alloy is refined to 104 μm. Besides the grain refinement, the morphology of the primary α-Mg is changed from dendritic to rosette, then to globular shape with changing the parameters of the pulsed magnetic field. The pulsed magnetic field causes melt convection during solidification, which makes the temperature of the whole melt homogenized, and produces an undercooling zone in front of the liquid/solid interface by the magnetic pressure, which makes the nucleation rate increased and big dendrites prohibited. In addition, primary α-Mg dendrites break into fine crystals, resulting in a refined solidification structure of the AZ91D alloy. The Joule heat effect induced in the melt also strengthens the grain refinement effect and spheroidization of dendrite arms.
基金This research was supported by National Key Basic Research and Development Programme of China "973" (No. G19990649051).
文摘The structures and macro-segregation of 2124 Al-alloy were studied when a pulsed magnetic field (PMF) was applied during solidification. It is found through experi-ments that a remarkable change occurs in the solidification structures of 2124 Al-alloy under pulsed magnetic field. The eutectic phase at grain boundaries change from thick continuous eutectic network to thin discontinuous one, and the distribution of solute elements was also homogenized. The typical negative segregation phenomenon of Cu in common solidification condition was restrained, and the segregation of Mg decreased.
基金the financial support from the National Natural Science Foundation of China(No.51034012)the National Basic Research Program of China(No.2010CB631205)
文摘The effects of a pulsed magnetic field （PMF） on the microsegregation of solute elements during directional solidification of a Ni-based single crystal superalloy were experimentally investigated, and the results show that the PMF significantly affects the microsegregation of Al, Ti, Co, Mo and W elements in the alloy. However, the distribution behavior differs for both positive and negative segregation elements. With the PMF, the microsegregation of negative segregation elements, Co and W, was restrained effectively, while that of positive segregation elements, A1, Ti and Mo, was aggravated. A segregation model was estab- lished to reveal the distribution mechanism of the elements with PME It is considered that, under the action of PME the jumping of solute atoms from the liquid phase to solid phase is hindered, but the jumping of solute atoms from the solid phase into liquid phase is promoted during solidification. As a result, the effective distribution coefficient of the solute atoms is reduced, which leads to the reduction of microsegregation of negative segregation elements and aggravation of microsegregation of positive segregation elements.