PVA(1-x)PSx (x = 0.0, 0.25, 0.50, 0.75 and 1.0) polymer blend films were prepared by simple solution cast method using mixer of dimethyl sulphoxide (DMSO) and double distilled water (DDW) as a common solvent. Gamma ir...PVA(1-x)PSx (x = 0.0, 0.25, 0.50, 0.75 and 1.0) polymer blend films were prepared by simple solution cast method using mixer of dimethyl sulphoxide (DMSO) and double distilled water (DDW) as a common solvent. Gamma irradiation studies have been carried out to investigate the potential for improvements in the electrical properties of pure and blend polymer film. The induced changes in the dielectric constant (εr), dielectric loss (tanδ) and AC conductivity (σac) properties for the unirradiated and irradiated films were studied, in the frequency range 50 Hz - 5 MHz at room temperature (27°C). Further, it was seen that the frequency dependent dielectric constant, dielectric loss and AC conductivity were found to increase with increasing γ irradiation dose for all the PVA(1-x)PSx (x = 0.0, 0.25, 0.50, 0.75 and 1.0) polymer blends. The maximum σac at 1 kHz frequency was observed to be 2.4421 × 10-6 s/m (at room temperature) for PVA film irradiated at 1.5 kGy.展开更多
Stable thin films made from polyionic complex 2C12N+PVS- with incorporated Hb on PG electrodes were characterized by electrochemistry. The electron transfer between Hb and PG electrodes was greatly facilitated in micr...Stable thin films made from polyionic complex 2C12N+PVS- with incorporated Hb on PG electrodes were characterized by electrochemistry. The electron transfer between Hb and PG electrodes was greatly facilitated in microenvironment of 2C12N+PVS- films. The Hb-2C12N+PVS-films could be used to catalytically reduce trichloroacetic acid.展开更多
文摘PVA(1-x)PSx (x = 0.0, 0.25, 0.50, 0.75 and 1.0) polymer blend films were prepared by simple solution cast method using mixer of dimethyl sulphoxide (DMSO) and double distilled water (DDW) as a common solvent. Gamma irradiation studies have been carried out to investigate the potential for improvements in the electrical properties of pure and blend polymer film. The induced changes in the dielectric constant (εr), dielectric loss (tanδ) and AC conductivity (σac) properties for the unirradiated and irradiated films were studied, in the frequency range 50 Hz - 5 MHz at room temperature (27°C). Further, it was seen that the frequency dependent dielectric constant, dielectric loss and AC conductivity were found to increase with increasing γ irradiation dose for all the PVA(1-x)PSx (x = 0.0, 0.25, 0.50, 0.75 and 1.0) polymer blends. The maximum σac at 1 kHz frequency was observed to be 2.4421 × 10-6 s/m (at room temperature) for PVA film irradiated at 1.5 kGy.
文摘Stable thin films made from polyionic complex 2C12N+PVS- with incorporated Hb on PG electrodes were characterized by electrochemistry. The electron transfer between Hb and PG electrodes was greatly facilitated in microenvironment of 2C12N+PVS- films. The Hb-2C12N+PVS-films could be used to catalytically reduce trichloroacetic acid.