Pd-MnO2/TiO2 nanotube arrays（NTAs） photo-electrodes were successfully fabricated via anodization and electro deposition subsequently; the obtained Pd-MnO2/TiO2 NTAs photo electrodes were analyzed by scanning electro...Pd-MnO2/TiO2 nanotube arrays（NTAs） photo-electrodes were successfully fabricated via anodization and electro deposition subsequently; the obtained Pd-MnO2/TiO2 NTAs photo electrodes were analyzed by scanning electron microscopy（SEM）, X-ray diffraction（XRD） and characterized accordingly. Moreover, the light harvesting and absorption properties were investigated via ultraviolet–visible diffuse reflectance spectrum（DRS）; photo degradation efficiency was investigated via analyzing the photo catalytic degradation of Rhodamine B under visible illumination（xenon light）. The performed analyses illustrated that Pd-MnO2 codoped particles were successfully deposited onto the surface of the TiO2 nanotube arrays;DRS results showed significant improvement in visible light absorption which was between400 and 700 nm. Finally, the photo catalytic degradation efficiency results of the designated organic pollutant（Rhodamine B） illustrated a superior photocatalytic（PC） efficiency of approximately 95% compared to the bare TiO2 NTAs, which only exhibited a photo catalytic degradation efficiency of approximately 61%, thus it indicated the significant enhancement of the light absorption properties of fabricated photo electrodes and their yield of UOH radicals.展开更多
基金the support from the National Natural Science Foundation of China (2220102005,22071246,and 22033008)Shandong Provincial Natural Science Foundation (ZR2023QB173)+1 种基金the Technology Support Program for Youth Innovation Team of Shandong Higher Education Institutions (2023KJ225)the Postdoctoral Application Project of Qingdao (QHBSH20230102024)。
基金supported by the National Natural Science Foundation of China (No. 51178138)the National Creative Research Groups of China (No. 51121062)the State Key Laboratory of Urban Water Resources and Environment (No. 2010DX03)
文摘Pd-MnO2/TiO2 nanotube arrays（NTAs） photo-electrodes were successfully fabricated via anodization and electro deposition subsequently; the obtained Pd-MnO2/TiO2 NTAs photo electrodes were analyzed by scanning electron microscopy（SEM）, X-ray diffraction（XRD） and characterized accordingly. Moreover, the light harvesting and absorption properties were investigated via ultraviolet–visible diffuse reflectance spectrum（DRS）; photo degradation efficiency was investigated via analyzing the photo catalytic degradation of Rhodamine B under visible illumination（xenon light）. The performed analyses illustrated that Pd-MnO2 codoped particles were successfully deposited onto the surface of the TiO2 nanotube arrays;DRS results showed significant improvement in visible light absorption which was between400 and 700 nm. Finally, the photo catalytic degradation efficiency results of the designated organic pollutant（Rhodamine B） illustrated a superior photocatalytic（PC） efficiency of approximately 95% compared to the bare TiO2 NTAs, which only exhibited a photo catalytic degradation efficiency of approximately 61%, thus it indicated the significant enhancement of the light absorption properties of fabricated photo electrodes and their yield of UOH radicals.