应用循环伏安法研究Pb Sm Sn和Pb Ca Sn合金电极在4.5mol·dm-3硫酸溶液中和0.6～1.6V(vs.Hg/Hg2SO4)电位范围内的电化学特性,并采用线性电位扫描法和交流伏安法研究了上述合金在相同溶液中分别于0.9和1.28V(vs.Hg/Hg2SO4)生长的阳...应用循环伏安法研究Pb Sm Sn和Pb Ca Sn合金电极在4.5mol·dm-3硫酸溶液中和0.6～1.6V(vs.Hg/Hg2SO4)电位范围内的电化学特性,并采用线性电位扫描法和交流伏安法研究了上述合金在相同溶液中分别于0.9和1.28V(vs.Hg/Hg2SO4)生长的阳极膜的性质.结果表明,Sm代替Pb Ca Sn合金中的Ca在0.9和1.28V电位下均可抑制铅合金阳极膜的生长和降低阳极膜的阻抗,并可减少在高阳极电位(1.6V)时氧气的析出.展开更多
利用线性电位扫描、恒电位阶跃、交流阻抗等方法分别研究了Pb Ca Bi合金被阳极或阴极极化后,表面上析氧、析氢以及合金腐蚀行为。结果表明:与Pb Ca合金相比,Pb Ca Bi合金可增加氧的析出,但抑制氢的析出,同时铋的加入,使Pb Ca耐蚀性提高...利用线性电位扫描、恒电位阶跃、交流阻抗等方法分别研究了Pb Ca Bi合金被阳极或阴极极化后,表面上析氧、析氢以及合金腐蚀行为。结果表明:与Pb Ca合金相比,Pb Ca Bi合金可增加氧的析出,但抑制氢的析出,同时铋的加入,使Pb Ca耐蚀性提高,且不同含量的铋对合金腐蚀有不同的影响。展开更多
The density,nature of the dislocations and distribution of the domain sizes in cold-deformed Pb-Ca-Sn solid solution were determined by X-ray diffraction profile analysis.The dislocation densities are of the order of ...The density,nature of the dislocations and distribution of the domain sizes in cold-deformed Pb-Ca-Sn solid solution were determined by X-ray diffraction profile analysis.The dislocation densities are of the order of 1010 cm-2.The strain broadening of diffraction profiles was accounted for by dislocation contrast factor.The coherent domain size was determined by the recently developed PM2K software package.Assuming that the domain size distribution is log-normal,the distribution function（median μ and variance σ） was calculated from the size parameters determined from X-ray diffraction profile analysis.展开更多
文摘应用循环伏安法研究Pb Sm Sn和Pb Ca Sn合金电极在4.5mol·dm-3硫酸溶液中和0.6～1.6V(vs.Hg/Hg2SO4)电位范围内的电化学特性,并采用线性电位扫描法和交流伏安法研究了上述合金在相同溶液中分别于0.9和1.28V(vs.Hg/Hg2SO4)生长的阳极膜的性质.结果表明,Sm代替Pb Ca Sn合金中的Ca在0.9和1.28V电位下均可抑制铅合金阳极膜的生长和降低阳极膜的阻抗,并可减少在高阳极电位(1.6V)时氧气的析出.
文摘The density,nature of the dislocations and distribution of the domain sizes in cold-deformed Pb-Ca-Sn solid solution were determined by X-ray diffraction profile analysis.The dislocation densities are of the order of 1010 cm-2.The strain broadening of diffraction profiles was accounted for by dislocation contrast factor.The coherent domain size was determined by the recently developed PM2K software package.Assuming that the domain size distribution is log-normal,the distribution function（median μ and variance σ） was calculated from the size parameters determined from X-ray diffraction profile analysis.