Cored wires and high velocity arc spraying (HVAS) technique were applied to produce high Al content Zn-Al alloy coatings on low carbon steel substrates. The electrochemical corrosion behaviors of Zn, Al and Zn-Al coat...Cored wires and high velocity arc spraying (HVAS) technique were applied to produce high Al content Zn-Al alloy coatings on low carbon steel substrates. The electrochemical corrosion behaviors of Zn, Al and Zn-Al coatings were studied with potentiodynamic measurement in 5 % NaCl solution. Compared with pure Zn, pure Al and Zn-15Al coatings, Zn-26Al coatings show a higher corrosion resistance in salt solution. The potentiodynamic polarization tests show that the corrosion resistance of Zn-Al coatings increases as Al content is raised. Pure Al coating exhibits different electrochemical behaviors with other coatings. The corrosion initiated at the micro-pores of the coating and the underlying corrosion mechanism is very similar to that of the pitting corrosion.展开更多
Potentiodynamic polarization measurement was used to investigate the effects of temperature, dissolved ox- ygen concentration and pH on the electrochemical behavior of X70 pipeline steel in simulated solution accordin...Potentiodynamic polarization measurement was used to investigate the effects of temperature, dissolved ox- ygen concentration and pH on the electrochemical behavior of X70 pipeline steel in simulated solution according to the orthogonal testing method. The results showed that temperature, dissolved oxygen concentration and pH had great influence on corrosion current density （icorr） of X70 steel. Corrosion current density of X70 steel was most influenced by dissolved oxygen concentration in simulated solution. The corrosion degree of X70 steel was the least under the environment of low temperature, deficient oxygen and weak acid.展开更多
This paper reports the comparative evaluation of the corrosion behaviour of AZ31B magnesium alloy under immersion and potentiodynamic polarization test in NaCl solution at different chloride ion concentrations,pH valu...This paper reports the comparative evaluation of the corrosion behaviour of AZ31B magnesium alloy under immersion and potentiodynamic polarization test in NaCl solution at different chloride ion concentrations,pH value and exposure time.The specimens were exposed to immersion and polarization environments in order to evaluate their corrosion rates.Empirical relationship was established to predict the corrosion rate of AZ31B magnesium alloy.Three factors,five level,central composite rotatable design matrix was used to minimize the number of experimental conditions.Response surface methodology was used to develop the relationship.The developed relationship can be effectively used to predict the corrosion rate of AZ31B magnesium alloy at 95%confidence level for both the testing.This research work proves a better corrosion resistance of AZ31B magnesium alloy at the alkaline solution than the acidic and the neutral solutions,moreover,low corrosion rate was found at low concentrated solution and higher exposure time respectively.展开更多
In this work, a comparison study on corrosion behavior of extruded near eutectic Al-12.3%Si-0.26%Mg and 6063 alloys has been carried out by mass loss test in 4% H2SO4 aqueous solution in the open air and potentiodynam...In this work, a comparison study on corrosion behavior of extruded near eutectic Al-12.3%Si-0.26%Mg and 6063 alloys has been carried out by mass loss test in 4% H2SO4 aqueous solution in the open air and potentiodynamic polarization test in 3.5 wt.% NaCI aqueous solution. Results indicate that the corrosion resistance of the near eutectic AI-Si-Mg alloy is less than that of 6063 alloy. Macro/microscopy and scanning electron microscopy results clearly show the difference of the corrosion progress of these two alloys in 4% H2SO4 aqueous solution. The corrosion type of 6063 alloy is pitting corrosion. The Mg2Si and AIFeSi particles and surface defects act as nucleation sites for pitting, and the amount and distribution of them have a significant effect on the pitting behavior. For the near eutectic alloy, there are two types of corrosion cells. One is between the extruded primary α-AI and the eutectic, the other is between the eutectic AI and eutectic Si particles. Combination of these two types of corrosion cells leads to a lower corrosion resistance, a higher mass loss of the near eutectic alloy compared with 6063 alloy, and the formation of the paralleling corroded grooves.展开更多
The passivation process of X80 pipeline steel in bicarbonate solutions was investigated using potentiodynamic, dynamic electro-chemical impedance spectroscopy （DEIS）, and Mott-Schottky measurements. The results show...The passivation process of X80 pipeline steel in bicarbonate solutions was investigated using potentiodynamic, dynamic electro-chemical impedance spectroscopy （DEIS）, and Mott-Schottky measurements. The results show that the shape of polarization curves changes with concentration. The critical ＇passive＇ concentration is 0.009 mol/L for X80 pipeline steel in bicarbonate solutions. No anodic current peak exists in solutions when the concentration is lower than 0.009 mol/L, whereas there are one and two anodic current peaks when the concentration ranges from 0.009 to 0.05 mol/L and is higher than 0.1 mol/L, respectively. DEIS measurements show that there exist active dissolution range, transition range, pre-passive range, passive layer formation range, passive range, and trans-passive range for X80 pipeline steel in the 0.1 mol/L solutions. The results of DEIS measurements are in complete agreement with the potentiodynamic diagram. An equivalent circuit containing three sub-layers is used to explain the Nyquist plots in the passive range. Analyses are well made for explaining the corresponding fitted capacitance and impedance. The Mott-Schottky plots show that the passive film of X80 pipeline steel is an n-type semiconductor, and capacitance measurements are in good accordance with the results of DEIS experiment.展开更多
The hot deformation characteristics and the corrosion behavior of a high-strength low-alloy(HSLA) steel were investigated at deformation temperatures ranging from 800 to 1100 ℃ and strain rates ranging from 0.1 to 10...The hot deformation characteristics and the corrosion behavior of a high-strength low-alloy(HSLA) steel were investigated at deformation temperatures ranging from 800 to 1100 ℃ and strain rates ranging from 0.1 to 10 s-1 using an MMS-200 thermal simulation testing machine. Based on the flow curves from the experiment, the effects of temperature and strain rate on the dynamic recrystallization behavior were analyzed. The flow stress decreased with increasing deformation temperature and decreasing strain rate. With the assistance of the process parameters, constitutive equations were used to obtain the activation energy and hot working equation. The hot deformation activation energy of HSLA steel in this work was 351.87 kJ/mol. The work hardening rate was used to determine the critical stress(strain) or the peak stress(strain). The dependence of these characteristic values on the Zener-Hollomon parameter was found. A dynamic recrystallization kinetics model of the tested HSLA steel was constructed, and the validity of the model was confirmed by the experimental results. Observation of the microstructures indicated that the grain size increased with increasing deformation temperature,which led to a lowered corrosion resistance of the specimens.展开更多
The inhibiting effect of ciprofloxacin,norfloxacin and ofloxacin on the corrosion of mild steel in 1 mol·L-1 HCl and the mechanism were studied at different temperatures using mass loss measurement,electrochemica...The inhibiting effect of ciprofloxacin,norfloxacin and ofloxacin on the corrosion of mild steel in 1 mol·L-1 HCl and the mechanism were studied at different temperatures using mass loss measurement,electrochemical method,and X-ray photoelectron spectroscopy(XPS) .Effective inhibition was shown by mass loss,potentiodynamic polarization and impedance spectroscopy measurement.The corrosion rate of the metal in the mass loss measurement,and the corrosion reaction on cathode and anode in the electrochemical measurement were accelerated when temperature was increased.XPS results showed that the inhibitors adsorbed effectively on the metal surface.展开更多
The electrochemical corrosion behaviour of three Zr-Ag alloys (Zr-1Ag, Zr-3Ag and Zr-5Ag) was investigated. Open circuit potential, linear potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) ...The electrochemical corrosion behaviour of three Zr-Ag alloys (Zr-1Ag, Zr-3Ag and Zr-5Ag) was investigated. Open circuit potential, linear potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) techniques were employed in aerated artificial saliva (pH = 4.0) at 37°C. Silver alloying additions are found to be effective in enhancing the corrosion resistance of zirconium in artificial saliva environment. In fact, Zr-Ag alloys exhibit higher open circuit potentials, larger breakdown potentials and higher impedance values as compared to cp Zr. This behaviour can be ascribed to the formation of a thicker and more stable passive film with increasing compactness, able to provide better protection against the corrosion attack.展开更多
This article studies the effects of the CeCl3 concentrations in conversion solutions with and without addition of NaCl, pH-values of conversion solution, drying temperature, time and temperature of immersion on the Ce...This article studies the effects of the CeCl3 concentrations in conversion solutions with and without addition of NaCl, pH-values of conversion solution, drying temperature, time and temperature of immersion on the Ce-conversion coatings for corrosion protection of the SiCp/5A06 Al-MMC and 5A06 Al-alloy in the 3.5% NaCl aqueous solution at room temperature. Potentiodynamic polarization tests reveal that the Ce-conversion treatment could markedly improve the pitting corrosion resistance of the composite and the matrix alloy in chloride containing environment. The best corrosion resistance effects are obtained for the samples treatment in 1% CeCl3.7H2O/3.5% NaCl solution at 45℃ for 60 min, followed by drying at 100 ℃ for 30 min. Examinations by means of scanning electron microscopy （SEM）, energy dispersion spectroscopy （EDS） and X-ray photoelectron spectroscopy （XPS） indicate that this behavior is due to the precipitation of Ce-oxides/hydroxides on the cathodic intermetallics and the Al-oxide film on the rest of the metal matrix.展开更多
The electrochemical corrosion behaviors of the welded joints of 2205 duplex stainless steel with the laser continuous heat treatment were investigated. The secondary austenite formation is the outcome of thermodynamic...The electrochemical corrosion behaviors of the welded joints of 2205 duplex stainless steel with the laser continuous heat treatment were investigated. The secondary austenite formation is the outcome of thermodynamic equilibrium breach of the alloy during heat treatment and the result of the continuous heat treatment which has the most important effect on the weld material. The partitioning behaviors of chromium and molybdenum as well as the volume fraction of ferrite and austenite have a remarkable influence on the composition of the individual phase. Mechanical examination of the laser trated weld demonstrates that the tensile strength and yield strength increase with increasing the amount of the secondary austenite. It is shown that the ultimate tensile strength of the 6 kW laser-treated weld is higher about 20 MPa than no heat treatment weld and the ductility can be further improved without compromising strength. The results indicate that the welding alters the corrosion behavior because of different post heat treatment power and the broad active peak is not identified which is attributed to the dissolution of the secondary austenitic in the ferrite phase. It is indicated that pitting resistance equivalent （PRE） values of base metal and 6 kW weld are higher than that of other welds; base metal is 33.7, 6 kW weld 33.3, no treatment 32.4, 4 kW weld 32.8, 8 kW weld 32.5. The extent of corrosion resistance improvement after reheating treatment is mainly caused by the removal of nitrogen from ferritic regions, which occurred as a consequence of secondary austenite growth.展开更多
A number of studies have been reported on the use of nanocrystalline plasma electrolytic nitrocarburising technology for surface hardening of stainless steels for higher corrosion resistance resulted from this techniq...A number of studies have been reported on the use of nanocrystalline plasma electrolytic nitrocarburising technology for surface hardening of stainless steels for higher corrosion resistance resulted from this technique. However, very few studies have focused on the optimization of the nanocrystalline plasma electrolytic nitrocarburising process parameters. In this study, a design of experiment （DOE） technique, the Taguchi method, has been used to optimize the nanocrystalline plasma electrolytic nitrocarburising not only for surface hardening but also for the corrosion protection of 316L austenitic stainless steel by controlling the coating processes factors. The experimental design consisted of four factors （Urea concentration, electrical conductivity of electrolyte, voltage and duration of process）, each containing three levels. Potentiodynamic polarization measurements were carried out to determine the corrosion resistance of the coated samples. The results were analyzed with related software. An analysis of the mean of signal-to-noise （S/N） ratio indicated that the corrosion resistance of nanocrystalline plasma electrolytic nitrocarburised 316L stainless steel was influenced significantly by the levels in the Taguchi orthogonal array. The optimized coating parameters for corrosion resistance are 1150 g/L for urea concentration, 360 mS/cm for electrical conductivity of electrolyte, 260 V for applied voltage, 6 min for treatment time. The percentage of contribution for each factor was determined by the analysis of variance （ANOVA）. The results showed that the applied voltage is the most significant factor affecting the corrosion resistance of the coatings.展开更多
In this study,ceramic coatings were deposited on 6061 Al alloy using a plasma electrolytic oxidation（PEO）technique,and the effect of concentrations of KOH and Na_2SiO_3 as electrolytes for PEO process was studied on...In this study,ceramic coatings were deposited on 6061 Al alloy using a plasma electrolytic oxidation（PEO）technique,and the effect of concentrations of KOH and Na_2SiO_3 as electrolytes for PEO process was studied on microstructure,chemical composition,and electrochemical behavior of PEO coatings formed on the 6061 Al alloy.The results indicated that the increase in concentration of KOH led to rise in electrical conductivity of electrolyte.Consequently,the breakdown voltage reduced,which in turn improved the surface quality and the corrosion behavior.Moreover,the increase in concentration of Na_2SiO_3 resulted in the increase in incorporation of Si in the coating,which led to a higher corrosion potential in the concentration of 4 g L^（-1）.According to this investigation,the best protection behavior of coatings can be obtained when the KOH and Na_2SiO_3 concentrations in PEO electrolyte are equal to 4 g L^（-1）.展开更多
Micro arc oxidation(MAO)coatings were formed on magnesium alloy AZ31B to improve the corrosion resistance using environmental friendly electrolyte solution under single-polar pulse power supply.The effect of electrica...Micro arc oxidation(MAO)coatings were formed on magnesium alloy AZ31B to improve the corrosion resistance using environmental friendly electrolyte solution under single-polar pulse power supply.The effect of electrical parameters of pulse frequency on the coating performance was studied at frequencies of 2.5 Hz,25 Hz and 250 Hz.The coating performance at different frequencies was characterized by scanning electron microscopy(SEM),energy-dispersive X-ray spectroscopy(EDS)and potentiodynamic polarization testing method.It was found that the corrosion resistance of the MAO coatings was improved when increasing the pulse frequencies from 2.5 Hz to 250 Hz.The corrosion current in 250 Hz case decreased by three orders of magnitude as compared with bare Mg alloy and the corrosion impedance also increased remarkably,means significantly enhanced corrosion resistance than bare Mg alloy.The results give us more insight in the optimization of electrical parameters to improve the MAO coating performance.The MAO technology is attractive for application on magnesium and other light alloys for surface protection in automotive and space industries.展开更多
Double-layered microcapsule corrosion inhibitors were developed by sodium monofluorophosphate as the core material,polymethyl methacrylate as the inner wall material,and polyvinyl alcohol as the outer wall material co...Double-layered microcapsule corrosion inhibitors were developed by sodium monofluorophosphate as the core material,polymethyl methacrylate as the inner wall material,and polyvinyl alcohol as the outer wall material combining the solvent evaporation method and spray drying method.The protection by the outer capsule wall was used to prolong the service life of the corrosion inhibitor.The dispersion,encapsulation,thermal stability of microcapsules,and the degradation rate of capsule wall in concrete pore solution were analyzed by ultra-deep field microscopy,scanning electron microscopy,thermal analyzer,and sodium ion release rate analysis.The microcapsules were incorporated into mortar samples containing steel reinforcement,and the effects of double-layered microcapsule corrosion inhibitors on the performance of the cement matrix and the actual corrosion-inhibiting effect were analyzed.The experimental results show that the double-layered microcapsules have a moderate particle size and uniform distribution,and the capsules were completely wrapped.The microcapsules as a whole have good thermal stability below 230 ℃.The monolayer membrane structure microcapsules completely broke within 1 day in the simulated concrete pore solution,and the double-layer membrane structure prolonged the service life of the microcapsules to 80 days in the simulated concrete pore solution before the core material was completely released.The mortar samples containing steel reinforcement incorporated with the double-layered microcapsule corrosion inhibitors still maintained a higher corrosion potential than the monolayer microcapsule corrosion inhibitors control group at 60 days.The incorporation of double-layered microcapsules into the cement matrix has no significant adverse effect on the setting time and early strength.展开更多
In this study,the microstructures,mechanical properties,corrosion behaviors,and biocompatibility of extruded magnesium-zirconiumstrontium-holmium(Mg-Zr-Sr-Ho)alloys were comprehensively investigated.The effect of diff...In this study,the microstructures,mechanical properties,corrosion behaviors,and biocompatibility of extruded magnesium-zirconiumstrontium-holmium(Mg-Zr-Sr-Ho)alloys were comprehensively investigated.The effect of different concentrations of Ho on the microstructural characteristics,tensile and compressive properties,corrosion resistance,and biocompatibility were investigated.The microstructures of the extruded Mg-1Zr-0.5Sr-xHo(x=0.5,1.5,and 4 wt.%)alloys consisted ofα-Mg matrix,fineα-Zr particles,and intermetallic phase particles of Mg_(17)Sr_(2) and Ho_(2)Mg mainly distributed at the grain boundaries.Extensive{1012}tensile twins were observed in the partially recrystallized samples of Mg-1Zr-0.5Sr-0.5Ho and Mg-1Zr-0.5Sr-1.5Ho.Further addition of Ho to 4 wt.%resulted in a complete recrystallization due to activation of the particle stimulated nucleation around the Mg_(17)Sr_(2) particles.The evolution of a rare earth(RE)texture was observed with the Ho addition,which resulted in the weakened basal and prismatic textures.Furthermore,a drastic increase of 200%in tensile elongation and 89%in compressive strain was observed with Ho addition increased from 0.5 to 4 wt%,respectively.The tension-compression yield asymmetry was significantly decreased from 0.62 for Mg-1Zr-0.5Sr-0.5Ho to 0.98 for Mg-1Zr-0.5Sr-4Ho due to the weakening of textures.Corrosion analysis of the extruded Mg-Zr-Sr-Ho alloys revealed the presence of pitting corrosion.A minimum corrosion rate of 4.98 mm y^(−1) was observed in Mg-1Zr-0.5Sr-0.5Ho alloy.The enhanced corrosion resistance is observed due to the presence of Ho_(2)O_(3) in the surface film which reduced galvanic effect.The formation of a stabilized surface film due to the Ho_(2)O_(3) was confirmed through the electrical impedance spectroscopy and XPS analysis.An in vitro cytotoxicity assessment revealed good biocompatibility and cell adhesion in relation to SaOS2 cells.展开更多
Spontaneous electrochemical noise (EN) can be a rich source of information concerning the processes simultaneously occurring at a corroding interface. Potential noise fluctuations during the free corrosion of pure alu...Spontaneous electrochemical noise (EN) can be a rich source of information concerning the processes simultaneously occurring at a corroding interface. Potential noise fluctuations during the free corrosion of pure aluminum in different concentration of neutral sodium chloride solution are investigated, and the breakdown and restoration of passive metal's film are studied using potentiodynamic scanning (PDS) measurements and electrochemical impedance spectroscopy (EIS) technique. Two capacitance loops are observed in the Nyquist plots in two kinds of concentration, and the corrosion process is under activation control at first, then become diffusion control within the oxide film and corrosion products of (Al(OH)p-mCl-m) accumulated on the surface of the corroding electrode. It is suggested that the pitting corrosion is much easier to occur for pure aluminum in 7.0wt% than in 2.0wt% NaCl solution, and the high concentration of chloride ion in solution inhibits the repassivation of a metastable pit. The corrosion rate deterministic step does not involve Cl-.展开更多
Alloys containing chromium （Cr） and molybdenum （Mo）, as the major alloying elements, are widely used in various industries where the material experiences corrosive environments. Chromium （Cr）, when added in an o...Alloys containing chromium （Cr） and molybdenum （Mo）, as the major alloying elements, are widely used in various industries where the material experiences corrosive environments. Chromium （Cr）, when added in an optimum amount, forms a Cr203 passive film which protects the underlying metal in aggressive solutions. Molybdenum （Mo） forms its oxides in the low pH solutions, thus, enhances the uniform corrosion resistance of an alloy in reducing acids and assists in inhibition to localized corrosion. Minor alloying elements, like tungsten （W） and copper （Cu）, also improve the overall corrosion resistance of an alloy in specific solutions. In the present study, corrosion resistance behavior of commercial iron- based alloys （316L SS, 254 SMO and 20Cb3） and nickel-based alloys （Mone1400, Alloy 625 and C-276） was studied in the acidic solutions. While the corrosion behavior of wrought alloys has been widely studied, there is little to no information on the corrosion performance of their welds, typically being the weak regions for corrosion initiation and propagation. Therefore, an attempt was undertaken to investigate the uniform and localized corrosion performance of base metal, simulated heat-affected zone and all-weld-metal samples of a Ni-Cr-Mo-W alloy, C-276. The study was conducted in aggressive acidic solutions. Various corrosion and surface analytical techniques were utilized to analyze the results.展开更多
基金Project(50235030)supported by the National Natural Science Foundation of China
文摘Cored wires and high velocity arc spraying (HVAS) technique were applied to produce high Al content Zn-Al alloy coatings on low carbon steel substrates. The electrochemical corrosion behaviors of Zn, Al and Zn-Al coatings were studied with potentiodynamic measurement in 5 % NaCl solution. Compared with pure Zn, pure Al and Zn-15Al coatings, Zn-26Al coatings show a higher corrosion resistance in salt solution. The potentiodynamic polarization tests show that the corrosion resistance of Zn-Al coatings increases as Al content is raised. Pure Al coating exhibits different electrochemical behaviors with other coatings. The corrosion initiated at the micro-pores of the coating and the underlying corrosion mechanism is very similar to that of the pitting corrosion.
基金Item Sponsored by National Science and Technology Infrastructure Platforms Construction Projects of China (2005DKA10400)National Science and Technology Support 11th Five-Year Plan of China(2006BAK02B01)
文摘Potentiodynamic polarization measurement was used to investigate the effects of temperature, dissolved ox- ygen concentration and pH on the electrochemical behavior of X70 pipeline steel in simulated solution according to the orthogonal testing method. The results showed that temperature, dissolved oxygen concentration and pH had great influence on corrosion current density （icorr） of X70 steel. Corrosion current density of X70 steel was most influenced by dissolved oxygen concentration in simulated solution. The corrosion degree of X70 steel was the least under the environment of low temperature, deficient oxygen and weak acid.
文摘This paper reports the comparative evaluation of the corrosion behaviour of AZ31B magnesium alloy under immersion and potentiodynamic polarization test in NaCl solution at different chloride ion concentrations,pH value and exposure time.The specimens were exposed to immersion and polarization environments in order to evaluate their corrosion rates.Empirical relationship was established to predict the corrosion rate of AZ31B magnesium alloy.Three factors,five level,central composite rotatable design matrix was used to minimize the number of experimental conditions.Response surface methodology was used to develop the relationship.The developed relationship can be effectively used to predict the corrosion rate of AZ31B magnesium alloy at 95%confidence level for both the testing.This research work proves a better corrosion resistance of AZ31B magnesium alloy at the alkaline solution than the acidic and the neutral solutions,moreover,low corrosion rate was found at low concentrated solution and higher exposure time respectively.
基金supported by Jiangsu Graduated-student Innovation Program of China(No.CXZZ-0146)the Scientific Research Foundation of Graduate School of Southeast University
文摘In this work, a comparison study on corrosion behavior of extruded near eutectic Al-12.3%Si-0.26%Mg and 6063 alloys has been carried out by mass loss test in 4% H2SO4 aqueous solution in the open air and potentiodynamic polarization test in 3.5 wt.% NaCI aqueous solution. Results indicate that the corrosion resistance of the near eutectic AI-Si-Mg alloy is less than that of 6063 alloy. Macro/microscopy and scanning electron microscopy results clearly show the difference of the corrosion progress of these two alloys in 4% H2SO4 aqueous solution. The corrosion type of 6063 alloy is pitting corrosion. The Mg2Si and AIFeSi particles and surface defects act as nucleation sites for pitting, and the amount and distribution of them have a significant effect on the pitting behavior. For the near eutectic alloy, there are two types of corrosion cells. One is between the extruded primary α-AI and the eutectic, the other is between the eutectic AI and eutectic Si particles. Combination of these two types of corrosion cells leads to a lower corrosion resistance, a higher mass loss of the near eutectic alloy compared with 6063 alloy, and the formation of the paralleling corroded grooves.
基金supported by the National Science and Technology Infrastructure Platforms Construction Projects (No.2005DKA10400)
文摘The passivation process of X80 pipeline steel in bicarbonate solutions was investigated using potentiodynamic, dynamic electro-chemical impedance spectroscopy （DEIS）, and Mott-Schottky measurements. The results show that the shape of polarization curves changes with concentration. The critical ＇passive＇ concentration is 0.009 mol/L for X80 pipeline steel in bicarbonate solutions. No anodic current peak exists in solutions when the concentration is lower than 0.009 mol/L, whereas there are one and two anodic current peaks when the concentration ranges from 0.009 to 0.05 mol/L and is higher than 0.1 mol/L, respectively. DEIS measurements show that there exist active dissolution range, transition range, pre-passive range, passive layer formation range, passive range, and trans-passive range for X80 pipeline steel in the 0.1 mol/L solutions. The results of DEIS measurements are in complete agreement with the potentiodynamic diagram. An equivalent circuit containing three sub-layers is used to explain the Nyquist plots in the passive range. Analyses are well made for explaining the corresponding fitted capacitance and impedance. The Mott-Schottky plots show that the passive film of X80 pipeline steel is an n-type semiconductor, and capacitance measurements are in good accordance with the results of DEIS experiment.
基金supported financially by the Fundamental Research Funds for the Central Universities (Nos. HEUCFP201719 and HEUCFP201731)
文摘The hot deformation characteristics and the corrosion behavior of a high-strength low-alloy(HSLA) steel were investigated at deformation temperatures ranging from 800 to 1100 ℃ and strain rates ranging from 0.1 to 10 s-1 using an MMS-200 thermal simulation testing machine. Based on the flow curves from the experiment, the effects of temperature and strain rate on the dynamic recrystallization behavior were analyzed. The flow stress decreased with increasing deformation temperature and decreasing strain rate. With the assistance of the process parameters, constitutive equations were used to obtain the activation energy and hot working equation. The hot deformation activation energy of HSLA steel in this work was 351.87 kJ/mol. The work hardening rate was used to determine the critical stress(strain) or the peak stress(strain). The dependence of these characteristic values on the Zener-Hollomon parameter was found. A dynamic recrystallization kinetics model of the tested HSLA steel was constructed, and the validity of the model was confirmed by the experimental results. Observation of the microstructures indicated that the grain size increased with increasing deformation temperature,which led to a lowered corrosion resistance of the specimens.
基金Supported by the National Science ＆ Technology Pillar Program（082603101c） China Postdoctoral Science Foundation （O92623101H）+2 种基金 Shandong Postdoctoral Foundation（200902040） Open Project Program of Marine Corrosion and Protection Research Center of Institute of Oceanology Chinese Academy of Science（200901005） Doctor Foundation of University of Jinan（XBS0899）
文摘The inhibiting effect of ciprofloxacin,norfloxacin and ofloxacin on the corrosion of mild steel in 1 mol·L-1 HCl and the mechanism were studied at different temperatures using mass loss measurement,electrochemical method,and X-ray photoelectron spectroscopy(XPS) .Effective inhibition was shown by mass loss,potentiodynamic polarization and impedance spectroscopy measurement.The corrosion rate of the metal in the mass loss measurement,and the corrosion reaction on cathode and anode in the electrochemical measurement were accelerated when temperature was increased.XPS results showed that the inhibitors adsorbed effectively on the metal surface.
文摘The electrochemical corrosion behaviour of three Zr-Ag alloys (Zr-1Ag, Zr-3Ag and Zr-5Ag) was investigated. Open circuit potential, linear potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) techniques were employed in aerated artificial saliva (pH = 4.0) at 37°C. Silver alloying additions are found to be effective in enhancing the corrosion resistance of zirconium in artificial saliva environment. In fact, Zr-Ag alloys exhibit higher open circuit potentials, larger breakdown potentials and higher impedance values as compared to cp Zr. This behaviour can be ascribed to the formation of a thicker and more stable passive film with increasing compactness, able to provide better protection against the corrosion attack.
文摘This article studies the effects of the CeCl3 concentrations in conversion solutions with and without addition of NaCl, pH-values of conversion solution, drying temperature, time and temperature of immersion on the Ce-conversion coatings for corrosion protection of the SiCp/5A06 Al-MMC and 5A06 Al-alloy in the 3.5% NaCl aqueous solution at room temperature. Potentiodynamic polarization tests reveal that the Ce-conversion treatment could markedly improve the pitting corrosion resistance of the composite and the matrix alloy in chloride containing environment. The best corrosion resistance effects are obtained for the samples treatment in 1% CeCl3.7H2O/3.5% NaCl solution at 45℃ for 60 min, followed by drying at 100 ℃ for 30 min. Examinations by means of scanning electron microscopy （SEM）, energy dispersion spectroscopy （EDS） and X-ray photoelectron spectroscopy （XPS） indicate that this behavior is due to the precipitation of Ce-oxides/hydroxides on the cathodic intermetallics and the Al-oxide film on the rest of the metal matrix.
基金Funded by the Major State Basic Research Development Program of China (973 Program) (No.2011CB706604)the R&D Project from Department of Railway(No. 2010G023)
文摘The electrochemical corrosion behaviors of the welded joints of 2205 duplex stainless steel with the laser continuous heat treatment were investigated. The secondary austenite formation is the outcome of thermodynamic equilibrium breach of the alloy during heat treatment and the result of the continuous heat treatment which has the most important effect on the weld material. The partitioning behaviors of chromium and molybdenum as well as the volume fraction of ferrite and austenite have a remarkable influence on the composition of the individual phase. Mechanical examination of the laser trated weld demonstrates that the tensile strength and yield strength increase with increasing the amount of the secondary austenite. It is shown that the ultimate tensile strength of the 6 kW laser-treated weld is higher about 20 MPa than no heat treatment weld and the ductility can be further improved without compromising strength. The results indicate that the welding alters the corrosion behavior because of different post heat treatment power and the broad active peak is not identified which is attributed to the dissolution of the secondary austenitic in the ferrite phase. It is indicated that pitting resistance equivalent （PRE） values of base metal and 6 kW weld are higher than that of other welds; base metal is 33.7, 6 kW weld 33.3, no treatment 32.4, 4 kW weld 32.8, 8 kW weld 32.5. The extent of corrosion resistance improvement after reheating treatment is mainly caused by the removal of nitrogen from ferritic regions, which occurred as a consequence of secondary austenite growth.
文摘A number of studies have been reported on the use of nanocrystalline plasma electrolytic nitrocarburising technology for surface hardening of stainless steels for higher corrosion resistance resulted from this technique. However, very few studies have focused on the optimization of the nanocrystalline plasma electrolytic nitrocarburising process parameters. In this study, a design of experiment （DOE） technique, the Taguchi method, has been used to optimize the nanocrystalline plasma electrolytic nitrocarburising not only for surface hardening but also for the corrosion protection of 316L austenitic stainless steel by controlling the coating processes factors. The experimental design consisted of four factors （Urea concentration, electrical conductivity of electrolyte, voltage and duration of process）, each containing three levels. Potentiodynamic polarization measurements were carried out to determine the corrosion resistance of the coated samples. The results were analyzed with related software. An analysis of the mean of signal-to-noise （S/N） ratio indicated that the corrosion resistance of nanocrystalline plasma electrolytic nitrocarburised 316L stainless steel was influenced significantly by the levels in the Taguchi orthogonal array. The optimized coating parameters for corrosion resistance are 1150 g/L for urea concentration, 360 mS/cm for electrical conductivity of electrolyte, 260 V for applied voltage, 6 min for treatment time. The percentage of contribution for each factor was determined by the analysis of variance （ANOVA）. The results showed that the applied voltage is the most significant factor affecting the corrosion resistance of the coatings.
文摘In this study,ceramic coatings were deposited on 6061 Al alloy using a plasma electrolytic oxidation（PEO）technique,and the effect of concentrations of KOH and Na_2SiO_3 as electrolytes for PEO process was studied on microstructure,chemical composition,and electrochemical behavior of PEO coatings formed on the 6061 Al alloy.The results indicated that the increase in concentration of KOH led to rise in electrical conductivity of electrolyte.Consequently,the breakdown voltage reduced,which in turn improved the surface quality and the corrosion behavior.Moreover,the increase in concentration of Na_2SiO_3 resulted in the increase in incorporation of Si in the coating,which led to a higher corrosion potential in the concentration of 4 g L^（-1）.According to this investigation,the best protection behavior of coatings can be obtained when the KOH and Na_2SiO_3 concentrations in PEO electrolyte are equal to 4 g L^（-1）.
基金This work performed by the author was financially sup-ported by Singapore Ministry of Education innovation Fund(MOE2010-IF-027).
文摘Micro arc oxidation(MAO)coatings were formed on magnesium alloy AZ31B to improve the corrosion resistance using environmental friendly electrolyte solution under single-polar pulse power supply.The effect of electrical parameters of pulse frequency on the coating performance was studied at frequencies of 2.5 Hz,25 Hz and 250 Hz.The coating performance at different frequencies was characterized by scanning electron microscopy(SEM),energy-dispersive X-ray spectroscopy(EDS)and potentiodynamic polarization testing method.It was found that the corrosion resistance of the MAO coatings was improved when increasing the pulse frequencies from 2.5 Hz to 250 Hz.The corrosion current in 250 Hz case decreased by three orders of magnitude as compared with bare Mg alloy and the corrosion impedance also increased remarkably,means significantly enhanced corrosion resistance than bare Mg alloy.The results give us more insight in the optimization of electrical parameters to improve the MAO coating performance.The MAO technology is attractive for application on magnesium and other light alloys for surface protection in automotive and space industries.
基金Fund by the National Key Technology Research and Development Program of the Ministry of Science and Technology of China (No.2018YFD1101002-03)。
文摘Double-layered microcapsule corrosion inhibitors were developed by sodium monofluorophosphate as the core material,polymethyl methacrylate as the inner wall material,and polyvinyl alcohol as the outer wall material combining the solvent evaporation method and spray drying method.The protection by the outer capsule wall was used to prolong the service life of the corrosion inhibitor.The dispersion,encapsulation,thermal stability of microcapsules,and the degradation rate of capsule wall in concrete pore solution were analyzed by ultra-deep field microscopy,scanning electron microscopy,thermal analyzer,and sodium ion release rate analysis.The microcapsules were incorporated into mortar samples containing steel reinforcement,and the effects of double-layered microcapsule corrosion inhibitors on the performance of the cement matrix and the actual corrosion-inhibiting effect were analyzed.The experimental results show that the double-layered microcapsules have a moderate particle size and uniform distribution,and the capsules were completely wrapped.The microcapsules as a whole have good thermal stability below 230 ℃.The monolayer membrane structure microcapsules completely broke within 1 day in the simulated concrete pore solution,and the double-layer membrane structure prolonged the service life of the microcapsules to 80 days in the simulated concrete pore solution before the core material was completely released.The mortar samples containing steel reinforcement incorporated with the double-layered microcapsule corrosion inhibitors still maintained a higher corrosion potential than the monolayer microcapsule corrosion inhibitors control group at 60 days.The incorporation of double-layered microcapsules into the cement matrix has no significant adverse effect on the setting time and early strength.
基金the financial support for this research by the Australian Research Council(ARC)through the Future Fellowship(FT160100252)the Discovery Project(DP170102557)。
文摘In this study,the microstructures,mechanical properties,corrosion behaviors,and biocompatibility of extruded magnesium-zirconiumstrontium-holmium(Mg-Zr-Sr-Ho)alloys were comprehensively investigated.The effect of different concentrations of Ho on the microstructural characteristics,tensile and compressive properties,corrosion resistance,and biocompatibility were investigated.The microstructures of the extruded Mg-1Zr-0.5Sr-xHo(x=0.5,1.5,and 4 wt.%)alloys consisted ofα-Mg matrix,fineα-Zr particles,and intermetallic phase particles of Mg_(17)Sr_(2) and Ho_(2)Mg mainly distributed at the grain boundaries.Extensive{1012}tensile twins were observed in the partially recrystallized samples of Mg-1Zr-0.5Sr-0.5Ho and Mg-1Zr-0.5Sr-1.5Ho.Further addition of Ho to 4 wt.%resulted in a complete recrystallization due to activation of the particle stimulated nucleation around the Mg_(17)Sr_(2) particles.The evolution of a rare earth(RE)texture was observed with the Ho addition,which resulted in the weakened basal and prismatic textures.Furthermore,a drastic increase of 200%in tensile elongation and 89%in compressive strain was observed with Ho addition increased from 0.5 to 4 wt%,respectively.The tension-compression yield asymmetry was significantly decreased from 0.62 for Mg-1Zr-0.5Sr-0.5Ho to 0.98 for Mg-1Zr-0.5Sr-4Ho due to the weakening of textures.Corrosion analysis of the extruded Mg-Zr-Sr-Ho alloys revealed the presence of pitting corrosion.A minimum corrosion rate of 4.98 mm y^(−1) was observed in Mg-1Zr-0.5Sr-0.5Ho alloy.The enhanced corrosion resistance is observed due to the presence of Ho_(2)O_(3) in the surface film which reduced galvanic effect.The formation of a stabilized surface film due to the Ho_(2)O_(3) was confirmed through the electrical impedance spectroscopy and XPS analysis.An in vitro cytotoxicity assessment revealed good biocompatibility and cell adhesion in relation to SaOS2 cells.
基金The authors wish to acknowledge the financial support of the national key basic research foundation of China (Grant No. G19990650), the National Natural Science Foundation of China (Grant No. 50071054) and State key Laboratory for Corrosion and Protecti
文摘Spontaneous electrochemical noise (EN) can be a rich source of information concerning the processes simultaneously occurring at a corroding interface. Potential noise fluctuations during the free corrosion of pure aluminum in different concentration of neutral sodium chloride solution are investigated, and the breakdown and restoration of passive metal's film are studied using potentiodynamic scanning (PDS) measurements and electrochemical impedance spectroscopy (EIS) technique. Two capacitance loops are observed in the Nyquist plots in two kinds of concentration, and the corrosion process is under activation control at first, then become diffusion control within the oxide film and corrosion products of (Al(OH)p-mCl-m) accumulated on the surface of the corroding electrode. It is suggested that the pitting corrosion is much easier to occur for pure aluminum in 7.0wt% than in 2.0wt% NaCl solution, and the high concentration of chloride ion in solution inhibits the repassivation of a metastable pit. The corrosion rate deterministic step does not involve Cl-.
文摘Alloys containing chromium （Cr） and molybdenum （Mo）, as the major alloying elements, are widely used in various industries where the material experiences corrosive environments. Chromium （Cr）, when added in an optimum amount, forms a Cr203 passive film which protects the underlying metal in aggressive solutions. Molybdenum （Mo） forms its oxides in the low pH solutions, thus, enhances the uniform corrosion resistance of an alloy in reducing acids and assists in inhibition to localized corrosion. Minor alloying elements, like tungsten （W） and copper （Cu）, also improve the overall corrosion resistance of an alloy in specific solutions. In the present study, corrosion resistance behavior of commercial iron- based alloys （316L SS, 254 SMO and 20Cb3） and nickel-based alloys （Mone1400, Alloy 625 and C-276） was studied in the acidic solutions. While the corrosion behavior of wrought alloys has been widely studied, there is little to no information on the corrosion performance of their welds, typically being the weak regions for corrosion initiation and propagation. Therefore, an attempt was undertaken to investigate the uniform and localized corrosion performance of base metal, simulated heat-affected zone and all-weld-metal samples of a Ni-Cr-Mo-W alloy, C-276. The study was conducted in aggressive acidic solutions. Various corrosion and surface analytical techniques were utilized to analyze the results.