Pb ( Mn1/3Sb2/3 ) x ( Zn1/3Nb2/3) y ( Zr0.535 Ti0.465 ),1-x-yO3 ( PMZN) piezoelectric ceramics were fabricated, The effects of sintering temperature and heat-treatment time on properties wen discussed, the optimum pre...Pb ( Mn1/3Sb2/3 ) x ( Zn1/3Nb2/3) y ( Zr0.535 Ti0.465 ),1-x-yO3 ( PMZN) piezoelectric ceramics were fabricated, The effects of sintering temperature and heat-treatment time on properties wen discussed, the optimum preparation technology parameters were obtained. In this case, the ceramics have the highest electromechanical coupling coefficients and mechanical quality factor and the least dielectric loss. It is revealed that the PMZN piezo-ceramics material can be utilized for high-power ultrasound transducers.展开更多
A coprecipitation method was used for preparation of 0.95Pb[(Mg0.8,Zn0.2) 1/ 3 Nb2 /3]O3-0.05PbTiO3(PMZN-PT),dielectric ceramic powder. X-ray powder diffraction and electron probe energy dispersive, X-ray analyzer rev...A coprecipitation method was used for preparation of 0.95Pb[(Mg0.8,Zn0.2) 1/ 3 Nb2 /3]O3-0.05PbTiO3(PMZN-PT),dielectric ceramic powder. X-ray powder diffraction and electron probe energy dispersive, X-ray analyzer revealed that the powder calcinated at 800℃ for 2 h is the PMZN-PT with 100% single perovskite phase, and the order of magnitude of atomic proportion of Mg to Zn reaches approximately 10: 1. In addition, the influence of Zn and Ti content on the perovskite phase and pyrochlore phase formation namely : 0.95Pb[(Mg1-x Znx) 1 /3Nb,2/3]O3 -0.05PbTiO3, (1-y)Pb[(Mg0.7Zn0.3) 1 /3Nb2 /3] O3-yPbTiO3 was also analysed.展开更多
文摘Pb ( Mn1/3Sb2/3 ) x ( Zn1/3Nb2/3) y ( Zr0.535 Ti0.465 ),1-x-yO3 ( PMZN) piezoelectric ceramics were fabricated, The effects of sintering temperature and heat-treatment time on properties wen discussed, the optimum preparation technology parameters were obtained. In this case, the ceramics have the highest electromechanical coupling coefficients and mechanical quality factor and the least dielectric loss. It is revealed that the PMZN piezo-ceramics material can be utilized for high-power ultrasound transducers.
文摘A coprecipitation method was used for preparation of 0.95Pb[(Mg0.8,Zn0.2) 1/ 3 Nb2 /3]O3-0.05PbTiO3(PMZN-PT),dielectric ceramic powder. X-ray powder diffraction and electron probe energy dispersive, X-ray analyzer revealed that the powder calcinated at 800℃ for 2 h is the PMZN-PT with 100% single perovskite phase, and the order of magnitude of atomic proportion of Mg to Zn reaches approximately 10: 1. In addition, the influence of Zn and Ti content on the perovskite phase and pyrochlore phase formation namely : 0.95Pb[(Mg1-x Znx) 1 /3Nb,2/3]O3 -0.05PbTiO3, (1-y)Pb[(Mg0.7Zn0.3) 1 /3Nb2 /3] O3-yPbTiO3 was also analysed.